Novel foam glass and preparation method thereof

A foam glass and a new technology, applied in the field of foam glass, can solve the problems of low strength of foam glass, limited source of raw materials and high cost, and achieve the effects of good chemical stability, improved mechanical properties and stability, and low production cost

Inactive Publication Date: 2017-09-22
合肥钢骨玻璃制品有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, foam glass has low strength, and the source of raw materials is limited, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment relates to a new type of foam glass, including the following raw materials in parts by weight: 12 parts of blast furnace slag, 5 parts of siliceous raw material, 20 parts of modified waste glass, 10 parts of ceramic polishing waste, 8 parts of calcite, 9 parts of perlite, 1.3 parts of alumina, 2 parts of sodium carbonate, 3 parts of borax, 0.8 parts of manganese dioxide, 0.7 parts of ferric oxide, 0.05 parts of sodium hexametaphosphate, 1 part of refractory fiber, 0.9 parts of nano medical stone powder, 0.3 parts of nano zinc oxide 1.1 parts, 1.1 parts of distarch sodium acetylated diacid, and 0.8 parts of calcium carbonate.

[0026] Wherein, the titanium dioxide content of the blast furnace slag is 18%-23%, and the silicon raw material is quartzite.

[0027] Wherein, the modified waste glass is obtained by the following method: mix the demagnesia boron mud and waste glass powder at a mass ratio of 1:2, grind, heat to 900°C, keep the temperature for 35 m...

Embodiment 2

[0039] This embodiment relates to a new type of foam glass, including the following raw materials in parts by weight: 27 parts of blast furnace slag, 22 parts of siliceous raw material, 40 parts of modified waste glass, 25 parts of ceramic polishing waste, 13 parts of calcite, 21 parts of perlite, 2.8 parts of alumina, 4 parts of sodium carbonate, 12 parts of borax, 1.4 parts of manganese dioxide, 1.3 parts of ferric oxide, 0.16 parts of sodium hexametaphosphate, 5 parts of refractory fiber, 1.7 parts of nano medical stone powder, 0.7 parts of nano zinc oxide 2.2 parts, 2.2 parts of distarch sodium acetylated diacid, and 2.4 parts of calcium carbonate.

[0040]Wherein, the titanium dioxide content of the blast furnace slag is 18%-23%, and the siliceous raw material is a mixture of quartz sand and vein quartz.

[0041] Wherein, the modified waste glass is obtained by the following method: mix the demagnesia boron mud and waste glass powder at a mass ratio of 1:2, grind, heat to...

Embodiment 3

[0053] This embodiment relates to a new type of foam glass, including the following raw materials in parts by weight: 18 parts of blast furnace slag, 15 parts of siliceous raw material, 30 parts of modified waste glass, 17 parts of ceramic polishing waste, 11 parts of calcite, 14 parts of perlite, 1.9 parts of alumina, 2.5 parts of sodium carbonate, 9 parts of borax, 1.2 parts of manganese dioxide, 1 part of ferric oxide, 0.14 parts of sodium hexametaphosphate, 3 parts of refractory fiber, 1.4 parts of nano medical stone powder, 0.5 parts of nano zinc oxide 1.6 parts, 1.6 parts of distarch sodium acetylated diacid, and 1.7 parts of calcium carbonate.

[0054] Wherein, the titanium dioxide content of the blast furnace slag is 18%-23%, and the siliceous raw material is a mixture of quartz sandstone and quartz sand.

[0055] Wherein, the modified waste glass is obtained by the following method: mix the demagnesia boron mud and waste glass powder at a mass ratio of 1:2, grind, hea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a novel foam glass which is prepared from the following raw materials in parts by weight: 12 to 27 parts of blast furnace slag, 5 to 22 parts of silica raw material, 20 to 40 parts of modified waste glass, 10 to 25 ceramic polishing waste, 8 to 13 parts of calcite, 9 to 21 perlite, 1.3 to 2.8 parts of aluminum oxide, 2 to 4 parts of sodium carbonate, 3 to 12 parts of borax, 0.8 to 1.4 parts of manganese dioxide, 0.7 to 1.3 parts of ferric oxide, 0.05 to 0.16 part of sodium hexametaphosphate, 1 to 5 parts of refractory fiber, 0.9 to 1.7 parts of nano medical stone powder, 0.3 to 0.7 part of nano zinc oxide, 1.1 to 2.2 parts of acetylated di-sodium starch and 0.8 to 2.4 parts of calcium carbonate. According to the novel foam glass, the blast furnace slag, the silica raw material, the modified waste glass and the ceramic polishing waste are utilized as raw materials, waste is turned into wealth, raw material source is wide, and cost is reduced; meanwhile, the refractory fiber and the nano zinc dioxide are added to serve as additives, so that performance of the foam glass is effectively improved, and strength of the foam glass is improved.

Description

technical field [0001] The invention belongs to the technical field of foam glass, and in particular relates to a novel foam glass and a preparation method thereof. Background technique [0002] Foam glass is made of waste flat glass, bottle glass as the main raw material, adding foaming agent, modifier, flux, etc., uniformly mixed by ball milling to form batch materials, and then placed in a specific abrasive tool for foaming, annealing, etc. A porous glass material filled with countless uniform bubbles formed by the process. In addition to the inherent permanence, safety, chemical corrosion resistance and protection from insects, ants and mice, foam glass also has the characteristics of light bulk density, small thermal conductivity, moisture impermeability, small water absorption, non-combustibility, and non-toxicity. Mildew, stable performance, both cold insulation material and thermal insulation material, can adapt to deep cold to higher temperature range and so on. A...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C11/00C03C6/10C03C6/02C03B19/08C03B19/06C03C14/00C03C1/02
CPCC03C11/007C03B19/06C03B19/08C03C1/002C03C1/024C03C14/002C03C2214/02C03C2214/30
Inventor 朱明静
Owner 合肥钢骨玻璃制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap