Hydrolysis-resistant PC-ABS alloy

A PC-ABS, hydrolysis-resistant technology, used in the field of composite materials, can solve the problems of pulverization, hydrolysis resistance, easy water absorption and decomposition, etc., and achieve good bending strength and mechanical impact strength, not easy to embrittlement and pulverization, not easy to hydrolysis. Effect

Active Publication Date: 2017-09-22
SUZHOU SUNWAY POLYMER
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PC-ABS contains PC components. The carbonate bonds in PC are sensitive to moisture and are easy to absorb and decompose. Even a small amount of moisture will cause degradation at high temperatures, resulting in discoloration of the resin, a sharp drop in molecular weight, and poor product performance.
[0003] At the current level of technology, there are already many PC-ABS alloys, but these materials all have fatal defects, that is, they are not resistant to hydrolysis.
In areas with high environmental humidity, such as Hainan, after 1-2 years of natural storage and use, these materials will become severely embrittled and pulverized due to water absorption, which will affect the use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrolysis-resistant PC-ABS alloy
  • Hydrolysis-resistant PC-ABS alloy
  • Hydrolysis-resistant PC-ABS alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0023] Weigh the raw materials according to the formula amounts of each embodiment in the following table 1, add the weighed samples into the high mixer, rotate at a speed of 1000 rpm, and mix for 20 minutes. After fully mixing, the premix is ​​obtained, and then the premix is The mixture is transferred to a twin-screw extruder, the extrusion temperature of the twin-screw extruder is 200°C, and the extrusion speed of the twin-screw extruder is 600 rpm, extruded and granulated to obtain hydrolysis-resistant PC-ABS alloy composites.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrolysis-resistant PC-ABS alloy which is prepared from the following raw materials in parts by weight: 55-75 parts of PC resin, 10-20 parts of ABS resin, 0.5-2 parts of a random terpolymer, 0.3-1 part of cyclic carbodiimide and 0.05-0.2 part of a coupling agent. The PC-ABS alloy resists high temperature and high humidity, is difficult in hydrolysis, embrittling and pulverization and has better mechanical properties such as bending strength, mechanical shock strength.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a hydrolysis-resistant PC-ABS alloy. Background technique [0002] Plastic parts for automobiles are exposed to a certain humidity and temperature environment for a long time. When selecting materials, it is necessary to check whether the materials can still maintain good performance under high temperature and high humidity. PC-ABS contains PC components. The carbonate bonds in PC are sensitive to moisture and are easy to absorb and decompose. Even a small amount of moisture will cause degradation at high temperatures, resulting in discoloration of the resin, a sharp drop in molecular weight, and poor product performance. [0003] At the current technical level, there are already many PC-ABS alloys, but these materials all have fatal defects, that is, they are not resistant to hydrolysis. In areas with high environmental humidity, such as Hainan, after 1-2 years of n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L23/08C08L83/06C08L75/02C08L75/04C08K5/521
CPCC08L69/00C08L2201/08C08L2205/035C08L55/02C08L23/0892C08L75/04C08K5/521C08L83/06C08L75/02
Inventor 任俊余林华
Owner SUZHOU SUNWAY POLYMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com