Metal ink and preparation method thereof
A metal ink and ink technology, applied in ink, household utensils, applications, etc., can solve the problems of large amount of application, many raw materials, and high transportation costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0053] A metallic ink, calculated in parts by weight, comprising:
[0054] 30 parts of high-purity iron phosphate,
[0055] Hydrogenated ricinoleic acid polymer dispersant 5 parts,
[0056] Fatty acid isopropyl ester 10 parts,
[0057] Fatty acid methyl ester 8 parts,
[0058] 47 parts of white oil.
[0059] A preparation method of metallic ink, wherein the preparation method comprises the following steps:
[0060] A. Calcinate high-purity ferric phosphate at 1100°C for 1 hour, and then grind it to 2000 mesh;
[0061] B. Calculate the total weight of the high-purity ferric phosphate and other components of the metal ink after grinding in step A, and add them to the sand mill in parts by weight, using zirconium beads with a diameter of 0.4-0.5mm Grinding as a grinding medium for 36 hours;
[0062] C. Detect the fineness and viscosity of the product after grinding in the above step B. If the fineness D90 is 700-800nm, and the viscosity is 8-15 mPa·s at 40°C, it is qualifie...
Embodiment 2
[0066] A cermet ink, calculated in parts by weight, comprising:
[0067] 39 parts of high-purity iron phosphate,
[0068] Hydrogenated ricinoleic acid polymer dispersant 5.5 parts,
[0069] 5 parts of diisobutyl succinate,
[0070] 5 parts of diisobutyl glutarate,
[0071] 5 parts of diisobutyl adipate,
[0072] 40.5 parts of white oil.
[0073] A preparation method of metallic ink, wherein the preparation method comprises the following steps:
[0074] A. Calcinate high-purity ferric phosphate at 1100°C for 1 hour, and then grind it to 2000 mesh;
[0075] B. Calculate the total weight of the high-purity ferric phosphate and other components of the metal ink after grinding in step A, and add them to the sand mill in parts by weight, using zirconium beads with a diameter of 0.4-0.5mm Grinding as a grinding medium for 42 hours;
[0076] C. Detect the fineness and viscosity of the product after grinding in the above step B. If the fineness D90 is 700-800nm, and the viscosit...
Embodiment 3
[0080] A cermet ink, calculated in parts by weight, comprising:
[0081] 50 parts of high-purity iron phosphate,
[0082] Hydrogenated ricinoleic acid polymer dispersant 6 parts,
[0083] 14 parts of fatty acid ethylhexyl ester,
[0084] 30 parts of solvent.
[0085] A preparation method of metallic ink, wherein the preparation method comprises the following steps:
[0086] A. Calcinate high-purity ferric phosphate at 1100°C for 1 hour, and then grind it to 2000 mesh;
[0087] B. Calculate the total weight of the high-purity ferric phosphate and other components of the metal ink after grinding in step A, and add them to the sand mill in parts by weight, using zirconium beads with a diameter of 0.4-0.5mm Grinding as a grinding medium for 50 hours;
[0088] C. Detect the fineness and viscosity of the product after grinding in the above step B. If the fineness D90 is 700-800nm, and the viscosity is 8-15 mPa·s at 40°C, it is qualified and enters the next process. Return to s...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Conductivity | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap