A kind of preparation method of graphene modified tungsten carbide self-lubricating wear-resistant additive

A graphene modification and wear-resistant additive technology, which is applied in the direction of graphene, carbide, tungsten/molybdenum carbide, etc., can solve the problem of difficult to ensure the self-lubricating and wear-resistant properties of the coating, the difficulty of uniform mixing of spray powder, Graphene has a large specific surface area, etc., to achieve the effect of reducing the friction coefficient, improving strength and toughness, and large specific surface area

Active Publication Date: 2021-04-20
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, graphene is a carbon material with nano-scale single-layer structure, and its weight is relatively light. Ceramic tungsten carbide spray powder has a large mass. If graphene is directly added to tungsten carbide spray powder, graphene will be sprayed by high-speed flame flow Blowing away and loss, it is difficult to retain the graphene component in the coating
In addition, graphene has a large specific surface area and high activity. It is easy to agglomerate when it is combined with tungsten carbide spray powder. It is difficult to ensure uniform mixing in the spray powder, so it is difficult to ensure that the prepared coating has self-lubricating and wear-resistant properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of graphene modified tungsten carbide self-lubricating wear-resistant additive
  • A kind of preparation method of graphene modified tungsten carbide self-lubricating wear-resistant additive
  • A kind of preparation method of graphene modified tungsten carbide self-lubricating wear-resistant additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The invention provides a graphene-modified tungsten carbide self-lubricating wear-resistant additive. The preparation process is as follows: a certain amount of graphite powder is added to a solution composed of concentrated H2SO4 (12mL), K2S2O8 (2.5g) and P2O5 (2.5g) , reacted at 80°C for 4.5 hours. After cooling to room temperature, 0.5 L of deionized water was added. and dry at room temperature. Add this pre-oxidized graphite powder to 150mL of concentrated H2SO4, keep the environment at 0°C with an ice-water bath, gradually add 15g KMnO4, and keep the temperature not exceeding 20°C, and stir at 35°C for 2 hours after the addition. Then 250 mL of deionized water was added and stirred for 2 hours. Then add 0.7 L of deionized water, then add 30 mL of 30% H2O2, dry at room temperature, and then dialyze in a dialysis bag for 1 week to remove heteroions. Finally, it was vacuum filtered and dried at room temperature to obtain graphene oxide.

[0027] Weigh 1g of graphe...

Embodiment 2

[0038] On the basis of the foregoing embodiments, the present embodiment provides a preparation process of a graphene-modified tungsten carbide self-lubricating wear-resistant additive as follows: a certain amount of graphite powder is added to concentrated H2SO4 (12mL), K2S2O8 (2.5g) and In a solution composed of P2O5 (2.5g), react at 80°C for 4.5 hours. After cooling to room temperature, 0.5 L of deionized water was added. and dry at room temperature. Add this pre-oxidized graphite powder to 150mL of concentrated H2SO4, keep the environment at 0°C with an ice-water bath, gradually add 15g KMnO4, and keep the temperature not exceeding 20°C, and stir at 35°C for 2 hours after the addition. Then 250 mL of deionized water was added and stirred for 2 hours. Then add 0.7 L of deionized water, then add 30 mL of 30% H2O2, dry at room temperature, and then dialyze in a dialysis bag for 1 week to remove heteroions. Finally, it was vacuum filtered and dried at room temperature to ob...

Embodiment 3

[0046] On the basis of the foregoing embodiments, the present embodiment provides a preparation process of a graphene-modified tungsten carbide self-lubricating wear-resistant additive as follows: a certain amount of graphite powder is added to concentrated H2SO4 (12mL), K2S2O8 (2.5g) and In a solution composed of P2O5 (2.5g), react at 80°C for 4.5 hours. After cooling to room temperature, 0.5 L of deionized water was added. and dry at room temperature. Add this pre-oxidized graphite powder to 150mL of concentrated H2SO4, keep the environment at 0°C with an ice-water bath, gradually add 15g KMnO4, and keep the temperature not exceeding 20°C, and stir at 35°C for 2 hours after the addition. Then 250 mL of deionized water was added and stirred for 2 hours. Then add 0.7 L of deionized water, then add 30 mL of 30% H2O2, dry at room temperature, and then dialyze in a dialysis bag for 1 week to remove heteroions. Finally, it was vacuum filtered and dried at room temperature to ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
dispersion coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a graphene-modified tungsten carbide self-lubricating wear-resistant additive, comprising the following steps: 1) weighing a certain amount of graphene and a precursor compound containing tungsten; 2) weighing the weighed graphite Alkenes were modified by wetting with a small amount of absolute ethanol, dispersed in a certain amount of deionized water, and dispersed by ultrasonic. 3) Dissolving the weighed tungsten-containing precursor compound in the graphene aqueous solution prepared in step 2) to obtain a compound powder and place it in an oven to obtain a dry mixed powder. 4) Place the dry powder in an alumina crucible, vacuumize, and 2 Cool naturally to room temperature under atmosphere to obtain graphene-modified tungsten carbide self-lubricating wear-resistant additive. The invention not only retains the layered single-layer carbonaceous structural characteristics of graphene, but also increases the specific gravity of graphene by the grown nano-carbide particles, which is expected to be applied to self-lubricating and wear-resistant additives for thermal spraying tungsten carbide spraying powder, reducing wear rate , play the role of reducing wear and tear.

Description

technical field [0001] The invention belongs to the field of graphene-modified tungsten carbide composite materials, and in particular relates to a preparation method of graphene-modified tungsten carbide self-lubricating and wear-resistant additives. Background technique [0002] After long-term research and analysis, it is found that graphene is a new carbonaceous material in which carbon atoms are tightly packed into a single-layer two-dimensional honeycomb lattice structure. It is the basic unit for building the most commonly used solid lubricant-graphite. Low friction coefficient, is a new type of self-lubricating anti-friction coating additive. However, graphene is a carbon material with a nano-scale single-layer structure, and its weight is relatively light. Ceramic tungsten carbide spray powder has a large mass. If graphene is directly added to tungsten carbide spray powder, graphene will be sprayed by high-speed flame flow It is difficult to retain the graphene com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/949C01B32/182C09D1/00C09D7/62
CPCC01P2002/72C01P2004/03C08K3/04C09D1/00
Inventor 郭孟秋田浩亮汤智慧王长亮崔永静高俊国张欢欢周子民
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS