Polyethylene composition, expanded beads, production method thereof, and expanded bead molded body

A technology of polyethylene and composition, applied in the field of polyethylene foamed bead moldings, can solve the problems of technical barriers, complexity, limited application fields, etc.

Active Publication Date: 2019-12-20
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the process is intermittent and complex, with high equipment costs and technical barriers, so the price of the obtained polyethylene foam beads is relatively high, which limits its application field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene composition, expanded beads, production method thereof, and expanded bead molded body
  • Polyethylene composition, expanded beads, production method thereof, and expanded bead molded body
  • Polyethylene composition, expanded beads, production method thereof, and expanded bead molded body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0035] According to a preferred embodiment of the present invention, the polyethylene composition is figure 1 Prepared in the shown multi-reactor parallel device, described multi-reactor parallel device comprises first reactor 1, second reactor 2, third reactor 3, solid / liquid (gas) separator 4, homogenizer The silo 5 and the melt granulation system 6, wherein the first reactor 1, the second reactor 2 and the third reactor 3 are connected in parallel, and the number of the solid / liquid (gas) separator 4 is three One, communicated with the first reactor 1, the second reactor 2 and the third reactor 3 respectively, the component A produced by the first reactor 1, the component B produced by the second reactor 2 and the component B produced by the third reactor The component C prepared by the reactor 3 is phase-separated in different solid / liquid (gas) separators 4, and then the phase-separated component A, component B and component C are sent to the homogenizer in proportion si...

Embodiment 1

[0055] This example is used to illustrate the polyethylene composition, expanded beads and expanded bead molded body provided by the present invention and the preparation method thereof.

[0056] (1) Preparation of polyethylene composition:

[0057] The polyethylene composition provided in this embodiment contains component A, component B, component C, cell nucleating agent, lubricant and cell control agent. Among them, component A, component B and component C are linear low-density polyethylene (LLDPE) copolymerized with ethylene / α olefin, and they are all prepared by the same catalyst system (Ziegler-Natta catalyst) and polymerization process , the difference is that the amount of hydrogen added when preparing different components and the type and molar content of α-olefin comonomers are different. Specific steps are as follows:

[0058] Add ethylene, α-olefin, hydrogen and nitrogen (ethylene, α-olefin, hydrogen and nitrogen are of polymerization grade, used after removing...

Embodiment 2

[0076] This example is used to illustrate the polyethylene composition, expanded beads and expanded bead molded body provided by the present invention and the preparation method thereof.

[0077] (1) Preparation of polyethylene composition:

[0078] The polyethylene composition provided in this embodiment contains component A, component B, component C, cell nucleating agent, lubricant and cell control agent. Among them, component A, component B and component C are linear low-density polyethylene (LLDPE) copolymerized with ethylene / α olefin, and they are all prepared by the same catalyst system (Ziegler-Natta catalyst) and polymerization process , the difference is that the amount of hydrogen added when preparing different components and the type and molar content of α-olefin comonomers are different. Specific steps are as follows:

[0079] Add ethylene, alpha olefin, hydrogen and nitrogen into the fluidized bed gas phase reactor, then add the Ziegler-Natta catalyst system, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the field of polymers, and particularly provides a polyethylene composition, a foamed bead and a preparation method thereof, and a foamed bead molding body. The polyethylene composition comprises a component A, a component B, a component C and a cell nucleating agent, wherein the component A is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIA of 0.01-3.5 g / 10 min, and has the density [rho]A of 0.880-0.936 g / cm<3>, the component B is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIB of 3.6-9.9 g / 10 min, and has the density [rho]B of 0.910-0.930 g / cm<3>, and the component C is ethylene / alpha-olefin copolymerized linear low-density polyethylene, has the melt index MIC of 10-80 g / 10 min, and has the density [rho]C of 0.880-0.930 g / cm<3>. The foamed bead prepared from the polyethylene composition has the uniform and compact cells, and the prepared foamed bead molding body has the high compressive strength.

Description

technical field [0001] The invention relates to a polyethylene composition, a polyethylene foam bead, a preparation method of the polyethylene foam bead and a molded polyethylene foam bead. Background technique [0002] Compared with polypropylene foamed beads, polyethylene foamed beads are softer due to their light weight, good mechanical properties including low-temperature impact resistance, higher closed cell ratio, and good resilience. Surface, and can be molded to obtain special shape products and other characteristics. Polyethylene foam beads are a polymer foam material with a wide range of uses. Compared with polystyrene series resin foamed bead molding products, polyethylene foamed bead molded products obtained by molding polyethylene foamed beads have chemical resistance, high toughness, high heat resistance, Good compression resilience and other excellent properties. However, polyethylene resin is a semi-crystalline polymer with a generally linear structure. Wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08J9/18C08J9/228
CPCC08J9/18C08J9/228C08J2323/08C08J2423/08C08L23/0815C08L2203/14C08L2205/025C08L2205/03
Inventor 郭鹏吕明福徐耀辉张师军高达利权慧吕芸张丽英董穆侴白舸
Owner CHINA PETROLEUM & CHEM CORP