A kind of anti-aging high-barrier solar battery backplane film and preparation method thereof

A technology for solar cells and back sheet films, applied in chemical instruments and methods, circuits, photovoltaic power generation, etc., can solve the problems of low surface free energy of fluoroplastics, increased UV weather resistance, complicated production processes, etc., and achieve good UV resistance. Aging performance, easy handling, overcoming the effect of low surface energy

Active Publication Date: 2018-08-21
宁波欧达光电有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, the cost of traditional composite materials is high, the production process is complicated, and the surface free energy of fluoroplastics is very low, and the bonding performance with other materials is poor
On the other hand, adhesives are used for bonding between layers, and delamination is prone to occur after aging; the polyester adhesive layer and the insulating layer PET have good affinity, and the adhesion between the substrate and the substrate The adhesion is relatively firm, but the ultraviolet weather resistance of the ester adhesive layer itself becomes yellow and easy to hydrolyze, and the performance decays seriously after aging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-aging high-barrier solar battery backplane film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A backsheet film for a solar cell, comprising a moisture barrier film and a fluorine-containing film arranged on the inside and outside of the moisture barrier film, the moisture barrier film and the fluorine-containing film can be naturally bonded without an adhesive; the The moisture barrier film is a biaxially oriented polyethylene terephthalate film with a thickness of 40 μm; the fluorine-containing film is prepared by radiation polymerization of the following raw materials in parts by weight: 20 parts of perfluoromethyl vinyl ether, 10 parts of vinyl siloxane modified nanometer zinc oxide, 10 parts of methacrylic acid, 15 parts of vinyl benzotriazole, 10 parts of acrylonitrile and 1 part of sodium dodecylbenzenesulfonate.

[0032] Wherein, the preparation method of the vinyl siloxane modified nano zinc oxide is: add 100g vinyl siloxane and 1g polymerization inhibitor to 2000g chloroform suspended with 400g zinc oxide nanoparticles, in N 2 Under atmosphere, reflux a...

Embodiment 2

[0042] A backsheet film for a solar cell, comprising a moisture barrier film and a fluorine-containing film arranged on the inside and outside of the moisture barrier film, the moisture barrier film and the fluorine-containing film can be naturally bonded without an adhesive; the The moisture barrier film is a biaxially oriented polyethylene terephthalate film with a thickness of 100 μm; the fluorine-containing film is prepared by radiation polymerization of the following raw materials in parts by weight: 25 parts perfluoroethyl vinyl ether, ethylene 12 parts of siloxane-modified nano zinc oxide, 12 parts of methacrylic acid, 17 parts of vinyl benzotriazole, 12 parts of acrylonitrile and 1 part of polyoxypropylene polyvinyl glyceryl ether.

[0043] Wherein, the preparation method of the vinyl siloxane modified nano zinc oxide is: 100g vinyl siloxane and 2g polymerization inhibitor methylene blue are added to 3000g chloroform suspended with 500g zinc oxide nanoparticles, under H...

Embodiment 3

[0053] A backsheet film for a solar cell, comprising a moisture barrier film and a fluorine-containing film arranged on the inside and outside of the moisture barrier film, the moisture barrier film and the fluorine-containing film can be naturally bonded without an adhesive; the The moisture barrier film is a biaxially oriented polyethylene terephthalate film with a thickness of 60 μm; the fluorine-containing film is prepared by radiation polymerization of the following raw materials in parts by weight: 27 parts of perfluoromethyl vinyl ether, ethylene 13 parts of siloxane-modified nano zinc oxide, 12 parts of methacrylic acid, 18 parts of vinyl benzotriazole, 13 parts of acrylonitrile and 1.5 parts of nonylphenol polyoxyethylene ether.

[0054] Wherein, the preparation method of the vinylsiloxane-modified nano-zinc oxide is: mix 100g vinylsiloxane and 2g polymerization inhibitor 2,2,6,6-tetramethylpiperidine nitroxide free radical TMP(h ) was added to 3400 g of chloroform in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a backplane film of a solar cell and a preparation method thereof. The backplane film comprises a moisture barrier film and a fluorine-containing film arranged on the inside and outside of the moisture barrier film. There is no need for an adhesive between them, and they can be directly laminated and bonded after corona treatment; the moisture barrier film is biaxially stretched polyethylene terephthalate; the fluorine-containing film is radiated and polymerized by the following raw materials in parts by weight Prepared: 20-30 parts of perfluoroalkyl vinyl ether, 10-15 parts of vinyl siloxane modified nano zinc oxide, 10-15 parts of methacrylic acid, 15-20 parts of vinyl benzotriazole, 10-15 parts of acrylonitrile and 1-2 parts of emulsifier. No solvent and initiator are used in the preparation process of the film layer, which is more environmentally friendly, and the preparation process has the characteristics of simple manufacture and low cost, and the prepared back sheet film has excellent anti-aging performance and barrier performance.

Description

technical field [0001] The invention belongs to the technical field of solar cell manufacturing in the solar photovoltaic industry, and relates to a back sheet film and a preparation method thereof, in particular to an anti-aging high-barrier solar cell back sheet film and a preparation method thereof. Background technique [0002] Solar cell backsheet film is one of the packaging materials for solar cell modules. Its main performance is to encapsulate crystalline silicon. In addition to having excellent electrical insulation properties, anti-oxidation, anti-humidity and long-term prevention of hydrolysis of adhesives, it also needs to have High barrier performance. The barrier performance of the back film includes not only the barrier of water vapor, but also the barrier of gas. Once air and water vapor enter the interior of the solar cell module, it will corrode the corresponding component very quickly, causing damage to the solar cell panel. Therefore, the performance of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L31/049H01L31/18B32B27/08B32B27/36B32B27/30C08F292/00C08F216/14C08F220/06C08F226/06C08F212/32C08F220/44C08J7/12C08F2/46C08F2/24C08L67/02
CPCB32B27/08B32B27/30B32B27/36B32B37/10C08F2/24C08F2/46C08F292/00C08J5/18C08J7/08C08J7/123C08J2367/02H01L31/049H01L31/18C08F216/1408C08F220/06C08F226/06C08F212/32C08F220/44Y02E10/50
Inventor 魏亮
Owner 宁波欧达光电有限公司