White ground blue spot glaze and preparation method thereof

A blue-spot glaze and white-ground technology, applied in the field of glazes, can solve the problems of unstable blue-spot color, impure white ground, and high cost

Inactive Publication Date: 2017-12-22
禹州市大龙山钧瓷文化有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The "white glaze" in Jun porcelain is pure in color, uniform in glaze surface, and stable in color. However, as people demand for beauty, red spots, blue spots, and blue spots are usually dotted on the white glaze. There are very few Jun porcelains with blue spots on the white background, and the fired ones are not pure, the color of the blue spots is unstable, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White ground blue spot glaze and preparation method thereof
  • White ground blue spot glaze and preparation method thereof
  • White ground blue spot glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A blue-spotted glaze on a white background, comprising a white-ground glaze and a blue-spotted glaze, the white-ground glaze is prepared from the following raw materials in parts by weight: 47-53 parts by weight of white feldspar, 9-15 parts by quartz, and 15 parts by weight of calcite -21 parts, 5-7 parts of Baiyao, 3.5-4.5 parts of antimonite, 8-12 parts of ashes; the blue spot glaze glaze is prepared from the following raw materials in parts by weight: 9-15 parts of this medicine, 37- 43 parts, 7-13 parts of quartz, 10-16 parts of limestone, 4-6 parts of porphyrin, 7-13 parts of iron ore, 1.5-2.5 parts of tin block, 7-9 parts of ashes.

[0026] The preparation method of above-mentioned white background basket spot glaze specifically comprises the steps:

[0027] (1) Preparation of white bottom glaze glaze slurry and blue spot glaze glaze slurry:

[0028] ①Preparation of the white ground glaze glaze slurry: add the above white ground glaze raw materials into an appro...

Embodiment 2

[0040] A blue-spotted glaze on a white background, comprising a white-ground glaze and a blue-spotted glaze, the white-ground glaze glaze material is prepared from the following raw materials in parts by weight: 50 parts of white feldspar, 12 parts of quartz, 18 parts of calcite, 6 parts of Baiyao 4 parts, 4 parts of antimonite, 10 parts of ashes; its blue spot glaze is prepared from the following raw materials in parts by weight: 12 parts of this medicine, 40 parts of feldspar, 10 parts of quartz, 13 parts of limestone, 5 parts of porphyrin, 10 parts of iron ore, 2 parts of tin block, 8 parts of bone ashes.

[0041] The preparation method of above-mentioned white background basket spot glaze specifically comprises the steps:

[0042] (1) Preparation of white bottom glaze glaze slurry and blue spot glaze glaze slurry:

[0043] ①Preparation of the white ground glaze glaze slurry: add the above white ground glaze raw materials into an appropriate amount of water to mix, ball mi...

Embodiment 3

[0055] A blue-spotted glaze on a white background, comprising a white-ground glaze and a blue-spotted glaze, the white-ground glaze glaze is prepared from the following raw materials in parts by weight: 49 parts of white feldspar, 13 parts of quartz, 19 parts of calcite, 6.2 parts of Baiyao 10 parts, 4 parts of antimonite, 11 parts of ashes; its blue spot glaze is prepared from the following raw materials in parts by weight: 10 parts of this medicine, 39 parts of feldspar, 12 parts of quartz, 14 parts of limestone, 4.5 parts of porphyrin, 11 parts of iron ore, 2 parts of tin block, and 8 parts of bone ashes.

[0056] The preparation method of above-mentioned white background basket spot glaze specifically comprises the steps:

[0057] (1) Preparation of white bottom glaze glaze slurry and blue spot glaze glaze slurry:

[0058] ①Preparation of the white ground glaze glaze slurry: add the above white ground glaze raw materials into an appropriate amount of water to mix, ball mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides white ground blue spot glaze which comprises white ground glaze and blue spot glaze, wherein the white ground glaze material is prepared from the following raw materials in parts by weight: 47-53 parts of white feldspar, 9-15 parts of quartz, 15-21 parts of calcite, 5-7 parts of Chinese loive, 3.5-4.5 parts of antimony ore and 8-12 parts of bone ash; and the blue spot glaze material is prepared from the following raw materials in parts by weight: 9-15 parts of original medicines, 37-43 parts of melilite, 7-13 parts of quartz, 10-16 parts of limestone, 4-6 parts of spot fossil, 7-13 parts of iron ore, 1.5-2.5 parts of tin bar and 7-9 parts of bone ash. Compared with the prior art, the white ground blue spot glaze disclosed by the invention has the advantages that due to the scientific and reasonable ratio of the raw materials and the controlled firing process, the white ground blue spot glaze is stable in color generation, natural in color development, low in cost and high in yield which can reach 91% or above.

Description

technical field [0001] The invention relates to a glaze material, in particular to a white background blue spot glaze and a preparation method thereof. Background technique [0002] Jun porcelain is based on the thickness of the glaze. Its color is either sunken at the bottom of the glaze, or suspended in the glaze, or floating on the surface of the glaze. Jun porcelain is transformed into a god by the kiln, and the natural transformation of the kiln is the essence of Jun porcelain art, and it is also the rarity of Jun porcelain that is famous all over the world and famous in the porcelain forest. The same kind of glaze is applied during firing, and once fired, it will be colorful, that is, "one color in the kiln, and thousands of colors in the kiln". Containing white and red in white, the five colors permeate and complement each other, and it is said that "Jun porcelain is unparalleled, and kiln transformation is unparalleled". The "white glaze" in Jun porcelain is pure i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B33/34C04B41/89
CPCC03C8/14C04B33/34C04B41/009C04B41/52C04B41/89
Inventor 王建伟
Owner 禹州市大龙山钧瓷文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com