High abrasion-resistant hard alloy

A hard alloy, high wear-resistant technology, applied in the field of high wear-resistant hard alloy, can solve the problems of tool wear, PCB drill bit life shortening, etc., to achieve the effect of prolonging the service life, solving many defects and high hardness of the bar

Inactive Publication Date: 2018-01-05
天津明源机械设备有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The life of a conventional PCB drill bit is 2000-3000 holes, but as modern electrical appliances are becoming more and more intelligent and miniaturized, the manufacturing technology of printed circuit boards with thin wires and narrow spacing is developing rapidly, and new materials for PCB boards are also getting faster and faster. It is getting harder and harder, because there are many strong materials in the material, the thermal conductivity of the material is low, and the processing speed is getting higher and higher. During the processing, more and more heat will be generated, which will accelerate the wear of the tool and make the PCB The life of the drill bit is greatly shortened. According to statistics, the main failure mode of the PCB drill bit is wear and fracture, which requires the material performance of the micro-drill bit for processing printed circuit board PCB holes to develop in the direction of higher strength, hardness, and wear resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Below, the substantive features and advantages of the present invention will be further described in conjunction with examples, but the present invention is not limited to the listed examples.

[0015] A high wear-resistant hard alloy, said high wear-resistant hard alloy is formed by mixing, granulating and sintering the following raw materials; based on the total weight, the parts by weight of each component in the raw material are: the Fisher grain size is 83-90 parts of WC powder with a size of 1.2-2.0um, 10-17 parts of Co powder with a Fibonacci particle size of 0.6-1.0um, 0.7-1.0 parts of B powder, and 0.2-1.0 parts of C powder;

[0016] The process steps of the preparation method of the high wear-resistant cemented carbide are:

[0017] (1) select each material component by above-mentioned material formula;

[0018] (2) Select a 1Kg stirring ball mill, first add B powder, C powder and Co powder, add hexane in a ratio of 400ml / kg as the grinding medium, add grindi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high abrasion-resistant hard alloy. The high abrasion-resistant hard alloy is prepared by mixing, granulating and sintering of raw materials of, by weight, 83-90 parts of WCpowder with the fisher particle size being 1.2-2.0 [mu]m, 10-17 parts of Co powder with the fisher particle size being 0.6-1.0 [mu]m, 0.7-1.0 part of B powder and 0.2-1.0 part of C powder. Accordingto the prepared high abrasion-resistant hard alloy, B and C are added in the raw materials and se rve as crystal material inhibitors, crystal material refining of the alloy structure is guaranteed, and abrasion resistance of prepared bar materials is enhanced effectively.

Description

technical field [0001] The invention relates to the technical field of hard alloy material manufacture, in particular to a high wear-resistant hard alloy. Background technique [0002] Vias are one of the important components of PCB, and their functions are the electrical connection channels between layers and the fixing or positioning holes of devices. Mechanical drilling with PCB micro-drilling is the most commonly used processing method. The life of a conventional PCB drill bit is 2000-3000 holes, but as modern electrical appliances become more and more intelligent and miniaturized, the manufacturing technology of printed circuit boards with thin wires and narrow spacing is developing rapidly, and new materials for PCB boards are also getting faster and faster. It is getting harder and harder, because there are many strong materials in the material, the thermal conductivity of the material is low, and the processing speed is getting higher and higher. During the processin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/08C22C1/05
Inventor 刘宝祥
Owner 天津明源机械设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products