DH590MPa acid rolling production technology control method

A technology of production process and control method, which is applied in the field of dual-phase steel rolling, can solve problems such as easy cracking, and achieve considerable economic benefits

Active Publication Date: 2018-01-09
BEIJING SHOUGANG COLD ROLLED SHEET
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a method for controlling the production process of DH590MPa acid rolling, which solves the technical problem of easy occurrence of cracking defects in the stamping process in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The hot rolling raw material composition is: C: 0.14%, Mn: 1.6%, Si: 0.4%, P: 0.015%, S: 0.003%, Alt: 0.5%.

[0040] After the smelting process is completed, the finishing temperature of the hot rolling is 893°C, the coiling temperature is 654°C, the yield strength of the hot rolling raw material is 418MPa, and the microstructure of the hot rolling raw material is ferrite and pearlite. Laser welding process parameters are: power 11000w, welding speed 4.5m / min, wire feeding speed 4.5m / min, annealing current 110A. The elongation rate of tension leveling machine: 0.8%; the insertion amount of 1# bending unit: 35mm; the insertion amount of 2# bending unit: 34mm; the insertion amount of 3# straightening unit: 16mm. Pickling speed: 60~199m / min, pickling temperature: 76.7℃.

[0041] The reduction distribution ratio of the rolling mill: the reduction distribution ratio of the stands F1-F5 are: 33.1%, 31.5%, 24.6%, 25.4%, 0.5%. The unit tension between the five stands from the...

Embodiment 2

[0043] The hot rolling raw material composition is: C: 0.13%, Mn: 2.05%, Si: 0.37%, P: 0.014%, S: 0.005%, Alt: 0.45%.

[0044] After the smelting process is completed, the hot rolling finishing temperature is 885°C, the coiling temperature is 643°C, the yield strength of the hot rolling raw material is 421MPa, and the hot rolling raw material structure is ferrite and pearlite. Laser welding process parameters are: power 11000w, welding speed 4.3m / min, wire feeding speed 4.2m / min, annealing current 110A. The elongation rate of tension leveling machine: 1.5%; the insertion amount of 1# bending unit: 38mm; the insertion amount of 2# bending unit: 26mm; the insertion amount of 3# straightening unit: 18mm. Pickling speed: 74~190m / min, pickling temperature: 87.6℃.

[0045]The reduction distribution ratio of the rolling mill: the reduction distribution ratio of the stands F1-F5 are: 28.7%, 28.7%, 26.6%, 25.4%, 0.4%. The unit tension between the five stands from the mill entrance to...

Embodiment 3

[0047] The hot rolling raw material composition is: C: 0.148%, Mn: 1.65%, Si: 0.43%, P: 0.014%, S: 0.005%, Alt: 0.55%.

[0048] After the smelting process is completed, the finishing temperature of the hot rolling is 918°C, the coiling temperature is 655°C, and the yield strength of the hot rolling raw material is 432MPa. The laser welding process parameters are: power 11000w, welding speed 5m / min, wire feeding speed 4.8m / min, annealing current 110A. The elongation rate of tension leveling machine: 1.3%; the insertion amount of 1# bending unit: 34mm; the insertion amount of 2# bending unit: 38mm; the insertion amount of 3# straightening unit: 19mm. Pickling speed: 75-205m / min, pickling temperature: 85.5°C.

[0049] The reduction distribution ratio of the rolling mill: the reduction distribution ratio of the stands F1-F5 are: 33.8%, 33.6%, 29.0%, 27.4%, 0.55%. The unit tension between the five stands from the mill entrance to the mill exit is: 55N / mm 2 , 155N / mm 2 , 165N / mm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of dual-phase steel rolling, and discloses a DH590MPa acid rolling production technology control method. The method includes the following steps of hot-rolled coil unwinding, coiled plate welding, coiled plate withdrawal and straightening, acid pickling, cold continuous rolling and reeling into cold hardened coils. A hot-rolled coil comprises 0.13%-0.148% of C, 1.6%-2.05% of Mn, 0.37%-0.43% of Si, 0.014%-0.015% of P, 0.003%-0.005% of S and 0.45%-0.55% of Alt. Dual-phase steel with good plate shape and thickness deviation is provided.

Description

technical field [0001] The invention relates to the technical field of dual-phase steel rolling, in particular to a production process control method for DH590MPa acid rolling. Background technique [0002] With the development of energy saving, emission reduction and lightweight in the automobile industry, dual-phase steel is the most widely used due to its good comprehensive mechanical properties. [0003] However, in the process of use, it was found that the traditional dual-phase steel is still difficult to form on many high-drawability parts, and it is difficult to meet the complex stamping structural parts of automobile design, which directly leads to cracking during the stamping process. For this reason, the majority of automobile factories have proposed the demand for DH steel (duplex steel with enhanced plasticity). [0004] However, currently in the related art, DH590Mpa dual-phase steel with enhanced plasticity cannot be produced in the acid rolling industrial pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/06C21D8/02
Inventor 李振程晓杰宋浩源孙建华李勇马永伟孙海
Owner BEIJING SHOUGANG COLD ROLLED SHEET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com