Polyester Chenille yarn and textile technology and application of polyester Chenille yarn

A process, polyester and snow technology, applied to all-polyester chenille yarn, its textile technology and application field can solve the problems of easy occurrence of hair loss, unsatisfactory anti-hair loss effect, and aggravated fiber slippage.

Inactive Publication Date: 2018-01-12
三问家居股份有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, chenille fabrics made from chenille yarns on the market are prone to shedding
The reason is that the fiber in the chenille fabric has a small forward and reverse friction coefficient, less curl, and less friction and cohesion with other surrounding fibers, and it is easy to slide out of the surface of the fabric and become noil.
At the same time, in order to maintain the soft and fluffy style of the fabric, a smaller twist coefficient and lower density are usually used, which reduces the cohesion between the fibers in the fabric and aggravates the slippage of the fibers.
[0004] At pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester Chenille yarn and textile technology and application of polyester Chenille yarn
  • Polyester Chenille yarn and textile technology and application of polyester Chenille yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The ES fiber single yarn and the polyester fiber single yarn are twisted into strands to obtain the core yarn. The blending ratio of the ES fiber single yarn to the polyester fiber single yarn is 30:70. The twist direction of the twisted strands is preferably Z twist, the twist coefficient is preferably 300, and the twist is preferably 50 pieces / 10cm to obtain a core wire with a linear density of 130 tex.

[0064] Another polyester fiber with a linear density of 160tex is used as a decorative thread, passed through the hollow spindle at a linear speed of 8m / min, and wound on a spacer with a specification of 1.2mm to form a yarn loop, and the yarn loop moves with the rotation of the roller sheet , when encountering a blade, it is cut into short feathers;

[0065] The two core wires are fed into the textile equipment at a linear speed of 7.5m / min under the traction of the rollers, and under the action of the rollers and the spacers, the short feathers are clamped between...

Embodiment 2

[0076] Obtain full polyester chenille yarn according to the spinning method of embodiment 1, different from embodiment 1 is that the fiber quantity ratio of described ES fiber single yarn and polyester fiber single yarn is 25:75, the fully polyester chenille yarn that finally obtains The linear density of the Seoul yarn is 308tex.

[0077] The described all-polyester chenille yarn that linear density is 308tex obtains all-polyester chenille carpet fabric sample according to the weaving method of embodiment 1, and detects the amount of hair loss and the amount of hair loss of sample according to the detection method that embodiment 1 provides Withdrawal force performance. The experimental results show that the average amount of hair shedding of the all polyester chenille carpet fabric sample prepared by the present embodiment is 9.5mg / 100cm 2 The pull-out force of the surface hair slipping or breaking of the all-polyester chenille carpet fabric sample is 7cN, and the number of...

Embodiment 3

[0079] Obtain full polyester chenille yarn according to the weaving method of embodiment 1, different from embodiment 1 is that the fiber number ratio of described ES fiber single yarn and polyester fiber single yarn is 20:80, the fully polyester chenille yarn that finally obtains The linear density of the Seoul yarn is 316tex.

[0080] The described all-polyester chenille yarn that linear density is 316tex obtains all-polyester chenille carpet fabric sample according to the weaving method of embodiment 1, and detects the shedding amount and the amount of wool of sample according to the detection method that embodiment 1 provides Withdrawal force performance. The experimental results show that the average amount of hair shedding of the all polyester chenille carpet fabric sample prepared by the present embodiment is 11.8mg / 100cm 2 The pull-out force of the surface wool slipping or breaking of the all-polyester chenille carpet fabric sample is 5cN, and the number of fibers sli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specificationaaaaaaaaaa
Linear densityaaaaaaaaaa
Linear densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a textile technology of polyester Chenille yarn. The textile technology comprises the steps that firstly, low-melting-point hot-melting binder fibers and polyester fibers are blended, and center yarn is prepared; secondly, decoration yarn is sandwiched between the center yarn for spinning through twisting, and a semi-finished product of the polyester Chenille yarn is obtained, wherein the decoration yarn is made of polyester fibers; thirdly, the semi-finished product of the polyester Chenille yarn is heated at the temperature of 0-200 DEGC, and the polyester Chenille yarn is obtained. According to the polyester Chenille yarn, the center yarn is prepared in the mode that the low-melting-point hot-melting binder fibers and the polyester fibers are blended, the polyester fibers are used as the decoration yarn, and after heat treatment, the low-melting-point hot-melting binder fiber skin layer is melted while the central layer is not changed, so that point-like bonding structures are formed between the fibers, the binding power of the fibers is increased, the slippage phenomena of the fibers are reduced, and the picking-resistant effect is good. The polyester Chenille fabric prepared from the yarn is not prone to picking, and the original hand feeling and style are maintained; meanwhile, the textile technology is simple and easy to implement, no auxiliary equipment is needed, and the cost is low.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a full polyester chenille yarn, its textile technology and its application. Background technique [0002] Chenille yarn is also called chenille or plush yarn. As a fancy yarn, chenille yarn has the characteristics of full pile, fluffy, soft touch and bright colors. The fabric woven with it is thick and light, so it is widely used in home textile decorative fabrics, woven knitting Many fields such as clothing, automobile decoration supplies and antique fabrics are deeply loved by people. [0003] However, the chenille fabrics made of chenille yarns on the market are prone to shedding. The reason is that the fiber in the chenille fabric has a small forward and reverse friction coefficient, less curl, and less friction and cohesion with other surrounding fibers, and it is easy to slide out of the fabric surface and become noil. At the same time, in order to maintain the soft and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D02G3/42D02G3/02A47G27/02
Inventor 王耀民
Owner 三问家居股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap