Wear-proof fluorescent colored glaze and preparation method

A glass and fluorescent technology, applied in glass manufacturing equipment, glass blowing, manufacturing tools, etc., can solve the problems of easy to wear color, not beautiful enough, glass clarity difficult to meet people's requirements, etc., to achieve beautiful color and good gloss , color dazzling effect

Inactive Publication Date: 2018-01-19
新沂市港发商贸有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process can only be completed after dozens of careful manual operations, and a slight negligence can cause failure or flaws. Therefore, the preparation method of colored glaze is highly demanding. The quality evaluation of colored glaze mainly comes from its transparency and clarity, while The clarification of the glass made at present is still relatively difficult to meet people's requirements
[0003] The current glass is easy to wear and the color is not beautiful enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: A kind of wear-resistant fluorescent colored glass, comprises the raw material of following weight part:

[0035] The soda is 20 parts, the quartz powder is 100 parts, the nitrate is 2 parts, the antimony oxide is 8 parts, the zinc oxide is 2 parts, the lead oxide is 0.8 parts, and the caustic soda is 10 parts, 4 parts of the fluorescent powder, 5 parts of the pigment, 2 parts of the clarifying agent, 5 parts of the wear-resistant agent and 1 part of the curing agent.

Embodiment 2

[0036] Embodiment 2: Similar in structure to Embodiment 1, the difference is:

[0037] The soda is 30 parts, the quartz powder is 80 parts, the nitrate is 5 parts, the antimony oxide is 4 parts, the zinc oxide is 6 parts, the lead oxide is 0.1 part, and the caustic soda is 8 parts, 6 parts of the fluorescent powder, 3 parts of the pigment, 3 parts of the clarifying agent, 3 parts of the wear-resistant agent and 4 parts of the curing agent.

Embodiment 3

[0038] Embodiment 3: Similar in structure to Embodiment 1, the difference is:

[0039] The soda is 25 parts, the quartz powder is 85 parts, the nitrate is 3 parts, the antimony oxide is 6 parts, the zinc oxide is 4 parts, the lead oxide is 0.6 parts, and the caustic soda is 8.5 parts, 5 parts of the fluorescent powder, 4.5 parts of the pigment, 2.5 parts of the clarifying agent, 4.5 parts of the wear-resistant agent and 2.5 parts of the curing agent.

[0040] The preparation method of a kind of wear-resistant fluorescent colored glass described in embodiment 1 to embodiment 3 is carried out according to the following steps:

[0041] 1. Chemical materials: Mix soda, quartz powder, nitrate, antimony oxide, zinc oxide, lead oxide, aluminum oxide, caustic soda, fluorescent powder, pigment, clarifying agent, wear-resistant agent and curing agent evenly, and put them into the smelting Furnace smelting, the temperature is 1350-450 degrees, and the molten glass is rotated on the iron...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-proof fluorescent colored glaze and a preparation method thereof. The colored glaze consists of the following raw materials in parts by weight: 20 to 30 parts of soda, 80 to 100 parts of quartz powder, 2 to 5 parts of nitrate, 4 to 8 parts of antimony oxide, 2 to 6 parts of zinc oxide, 0.1 to 0.8 part of lead oxide, 8 to 10 parts of caustic soda, 4 to 6 parts of fluorescent powder, 3 to 5 parts of a pigment, 2 to 3 parts of a clarifying agent, 3 to 5 parts of a wear-proof agent and 1 to 4 parts of a curing agent, wherein the wear-proof agent is wear-proof particles. The wear-proof fluorescent colored glaze disclosed by the invention has the advantages of few impurities, wear resistance, no crack, excellent glossiness, bright colors, shine with dazzling brilliance and the like, and particularly meets the requirement of young people on bright colors.

Description

technical field [0001] The invention relates to the technical field of colored glaze and its preparation, in particular to fluorescent colored glaze. Background technique [0002] Liuli refers to crystal works made of artificial crystals of various colors as raw materials and dewaxed at high temperature by the ancient bronze dewaxing casting method. Its color is flowing and beautiful, and its quality is crystal clear and dazzling. This process can only be completed after dozens of careful manual operations, and a slight negligence can cause failure or flaws. Therefore, the preparation method of colored glaze is highly demanding. The quality evaluation of colored glaze mainly comes from its transparency and clarity, while The clarification of the glass made at present is also difficult to meet people's requirements. [0003] The current glass is easy to wear and the color is not beautiful enough. In order to overcome the above-mentioned shortcomings, the inventor actively ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03B9/00
Inventor 刘亚林
Owner 新沂市港发商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com