Novel environment-friendly silicon-containing alloy material tube and preparation method thereof

A material tube and alloy technology, which is applied in the field of environmental protection silicon-containing new alloy material tube and its preparation field, can solve the problem that bronze alloy cannot meet the requirements, and achieve the effect of retaining mechanical properties, meeting environmental protection performance, and meeting requirements

Inactive Publication Date: 2018-01-23
绵阳旺通科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing tin bronze materials often add lead elements in order to achieve their chip-easy performance, but with the increasing awareness of environmental protection, bronze alloys containing lead elements can no longer meet the requirements of high-end markets at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An environmentally friendly silicon-containing new type alloy material tube, which is composed of the following components: zinc accounting for 1% of the total weight of the alloy material tube, tin accounting for 1% of the total weight of the alloy material tube, aluminum accounting for 0.5% of the total weight of the alloy material tube, accounting for The total weight of the alloy material tube is 0.05% of antimony, 0.5% of the total weight of the alloy material tube is silicon, and the balance is copper.

[0027] Put zinc, tin, aluminum, antimony, silicon, and electrolytic copper in a power frequency electric furnace according to the above ratio, heat to 1250-1300 degrees to completely melt and then keep warm to 12 degrees; use special graphite tools to fully stir the completely melted alloy liquid Finally, cover it with high-purity flaky graphite powder to prevent its oxidation, with a thickness of 11-13cm; after 1.2-1.5 hours of heat preservation, use the German im...

Embodiment 2

[0030] An environmentally friendly silicon-containing new type alloy material tube, which is composed of the following components: zinc accounting for 2% of the total weight of the alloy material tube, tin accounting for 2% of the total weight of the alloy material tube, aluminum accounting for 1.5% of the total weight of the alloy material tube, accounting for The total weight of the alloy material tube is 0.25% of antimony, 0.75% of the total weight of the alloy material tube is silicon, and the balance is copper.

[0031] Put zinc, tin, aluminum, antimony, silicon, and electrolytic copper in a power frequency electric furnace according to the above ratio, heat to 1250-1300 degrees to completely melt and then keep warm to 1200 degrees; use special graphite tools to fully stir the completely melted alloy liquid Finally, cover it with high-purity flaky graphite powder to prevent its oxidation, with a thickness of 11-13cm; after 1.2-1.5 hours of heat preservation, use the German...

Embodiment 3

[0034] An environmentally friendly silicon-containing new alloy material tube, which is composed of the following components: zinc accounting for 3% of the total weight of the alloy material tube, tin accounting for 3% of the total weight of the alloy material tube, aluminum accounting for 2.5% of the total weight of the alloy material tube, accounting for The total weight of the alloy material tube is 0.5% of antimony, 1% of the total weight of the alloy material tube is silicon, and the balance is copper.

[0035]Put zinc, tin, aluminum, antimony, silicon, and electrolytic copper in a power frequency electric furnace according to the above ratio, heat to 1250-1300 degrees to completely melt and then keep warm to 1200 degrees; use special graphite tools to fully stir the completely melted alloy liquid Finally, cover it with high-purity flaky graphite powder to prevent its oxidation, with a thickness of 11-13cm; after 1.2-1.5 hours of heat preservation, use the German imported ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a novel environment-friendly silicon-containing alloy material tube and a preparation method thereof. The alloy material tube is composed of, by the total weight of the alloy material tube, 1-3% of zinc, 1-3% of tin, 0.5-2.5% of aluminum, 0.05-0.5% of stibium, 0.5-1% of silicon, 0-1% of titanium and the balance copper. The traditional lead element is replaced with the silicon element, zinc, tin, aluminum, stibium, silicon and copper are blended at a proper temperature according to a certain component ratio, by continuously casting a blank tube, a tin bronze tube containing the lead element can be completely replaced with the tube extruded through an extruding machine, thus, under the condition that the cost is not increased, the mechanical properties such as turningof existing tin bronze are reserved, and the requirement for the environmental protection performance of alloy is met.

Description

technical field [0001] The invention relates to the field of alloy pipes, in particular to an environmentally friendly silicon-containing novel alloy material pipe and a preparation method thereof. Background technique [0002] The existing tin bronze materials often add lead elements in order to achieve their chip-easy performance. However, with the increasing awareness of environmental protection, bronze alloys containing lead elements can no longer meet the requirements of high-end markets at home and abroad. Contents of the invention [0003] The purpose of the present invention is to provide a new type of environmentally friendly silicon-containing alloy material tube and its preparation method, which not only retains the mechanical properties of the existing tin bronze chips, but also meets the environmental protection performance of the alloy without increasing the cost. requirements. [0004] In order to realize the foregoing invention object, the technical scheme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/02C22C9/04C22C1/02B21C37/06
Inventor 郑小明
Owner 绵阳旺通科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com