Environment-friendly building board and preparation method thereof

A technology for building panels and environmental protection, applied in the field of environmentally friendly building panels and its preparation, can solve the problems that building panels cannot meet environmental protection and light weight, and achieve the effects of good performance, low energy consumption, lower temperature and energy consumption

Active Publication Date: 2016-03-09
SHENZHEN KANGYA ECOLOGICAL ENVIRONMENT CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For this reason, the technical problem to be solved by the present invention lies in the fact that the building panels in the prior art cannot meet the performance requirements of environmental protection and light weight, and then provide an environmentally friendly building panel that can be used for outdoor wall insulation and indoor wall insulation. The above-mentioned boards have the properties of light weight, heat preservation and high strength, and can meet the environmental protection requirements of indoor construction at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly building board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0028] Cement 5kg, coal gangue 15kg, paraffin 8kg, urea 7kg, sulfomethyl phenolic resin 8kg, glass fiber 6kg, bentonite 15kg, methyl cellulose 3kg, mullite 5kg, medical stone 2kg, zeolite 5kg, sulfomethyl lignite 1kg, hydroxyethyl cellulose 15 and foaming agent 0.5kg.

[0029] The environmentally friendly building panels described in this example are prepared by the following steps:

[0030] (1) Get described cement, gangue, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and foaming agent of selected weight 1 / 4 according to selected weight, mix and sieve, spare;

[0031] (2) Take the paraffin, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected parts by weight, mix well and heat to 110°C to carry out Low temperature foaming...

Embodiment 2

[0036] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0037] Cement 10kg, coal gangue 4kg, paraffin 2kg, urea 13kg, sulfomethyl phenolic resin 4kg, glass fiber 14kg, bentonite 8kg, methyl cellulose 9kg, mullite 1kg, medical stone 5kg, zeolite 2kg, sulfomethyl lignite 6kg, hydroxyethyl cellulose 4kg and foaming agent 1.5kg.

[0038] The environmentally friendly building panels described in this example are prepared by the following steps:

[0039] (1) Get the blowing agent of described cement, coal gangue, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and 1 / 3 of selected parts by weight according to the selected parts by weight, mix well And sieve, set aside;

[0040] (2) Take the paraffin, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected parts by weight, mix well and heat t...

Embodiment 3

[0045] The environmentally friendly building board described in this embodiment is prepared from the following components in parts by weight:

[0046] Cement 6kg, coal gangue 10kg, paraffin 6kg, urea 9kg, sulfomethyl phenolic resin 7kg, glass fiber 9kg, bentonite 13kg, methyl cellulose 5kg, mullite 4g, medical stone 3kg, zeolite 4kg, sulfomethyl lignite 2kg, 11kg of hydroxyethyl cellulose and 0.7kg of blowing agent.

[0047] The environmentally friendly building panels described in this example are prepared by the following steps:

[0048] (1) Get the foaming agent of described cement, coal gangue, mullite, medical stone, bentonite, zeolite, sulfomethyl lignite and selected parts by weight according to the selected weight, mix and sieve ,spare;

[0049](2) Take the paraffin wax, urea, sulfomethyl phenolic resin, glass fiber, methyl cellulose, hydroxyethyl cellulose and the remaining foaming agent according to the selected weight, mix and heat to 110 ° C for low temperature f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention specifically relates to a lightweight, heat-preserving, high-strength and environment-friendly building board and a preparation method thereof, belonging to the field of building materials. The environment-friendly building board is prepared from the following components by weight: 5 to 10 parts of cement, 4 to 15 parts of gangue, 2 to 8 parts of paraffin, 7 to 13 parts of urea, 4 to 8 parts of sulfomethyl phenol formaldehyde resin, 6 to 14 parts of a glass fiber, 8 to 15 parts of bentonite, 3 to 9 parts of methyl cellulose, 1 to 5 parts of mullite, 2 to 5 parts of Chinese medical stone, 2 to 5 parts of zeolite, 1 to 6 parts of sulfomethyl lignite, 4 to 15 parts of hydroxyethyl cellulose and 0.5 to 1.5 parts of a foaming agent. The board provided by the invention has good performances like lightweight, heat preservation, fire resistance and high strength, and the performance index of the board is much higher than national and industrial standard requests in China.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a light-weight, heat-preserving and high-strength environment-friendly building board and a preparation method thereof. Background technique [0002] With the rapid development of social economy, more and more buildings have sprung up, showing high-level requirements for "building height, building form and building quality". Among them, building insulation is a measure to reduce the indoor heat dissipation of buildings to the outside. It plays an important role in creating a suitable indoor thermal environment and saving energy. It is also an important requirement and guarantee for building quality. [0003] According to the different construction locations, building environmental protection measures are mainly divided into two methods: the external structure of the building and the internal wall of the building. Among them, building insulation from the peripheral c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B28/00
Inventor 金峰
Owner SHENZHEN KANGYA ECOLOGICAL ENVIRONMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com