Sound-proof modified asphalt waterproof roll and preparation method thereof
A technology of modified asphalt and waterproof membranes, which is applied in building insulation materials, building components, buildings, etc. It can solve the problems of low tensile strength, poor sound insulation, and small elongation, and achieve high elongation at break and sound insulation. Good performance, good waterproof performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0047] The present invention also provides a method for preparing sound insulation modified asphalt waterproof coiled material, which includes the following steps:
[0048] a) Add tris hydrochloride and surfactant to the water, stir well, adjust the pH of the solution to 8.5 with sodium hydroxide, and add dopamine hydrochloride, stir well, add asphalt, and stir again After uniformity, let it stand for 24 hours to obtain modified asphalt;
[0049] b) Add the modified asphalt, EPDM rubber, silane coupling agent, asbestos lint, carbon fiber, vulcanizing agent, vulcanizing agent, antioxidant, and filler obtained in step a) to the high-speed mixing mixer at 50~70℃ Stir for 60-100min to obtain a mixture;
[0050] c) Add the mixture obtained in step a) to the rubber mixer for plasticizing and then mixing. The mixing temperature is controlled at 80~90℃, and the mixing time is 30~50min. After the mixing is completed, use a two-roll calender to mix the material Calendered into a semi-finishe...
Example Embodiment
[0057] Example 1
[0058] a) Add tris hydrochloride and surfactant to the water, stir well, adjust the pH of the solution to 8.5 with sodium hydroxide, and add dopamine hydrochloride, stir well, add asphalt, and stir again After uniformity, let stand for 24 hours to obtain polydopamine modified asphalt; the mass ratio of water, tris hydrochloride, dopamine hydrochloride, surfactant and asphalt is 30:4:1.5:3:60;
[0059] b) 75 parts by weight of modified asphalt, 28 parts by weight of EPDM rubber, 2.8 parts by weight of silane coupling agent, and 10 parts by weight of the modified asphalt obtained in step a) Asbestos wool, 1.4 parts by weight of carbon fiber, 1.6 parts by weight of vulcanizing agent, 2.6 parts by weight of vulcanizing agent, 0.8 parts by weight of antioxidant, 28 parts by weight Add the filler, 0.6 parts by weight of anti-ultraviolet agent and 1.1 parts by weight of antioxidant to the high-speed mixing mixer, and stir at 60°C for 85 minutes to obtain a mixture;
[0...
Example Embodiment
[0062] Example 2
[0063] a) Add tris hydrochloride and surfactant to the water, stir well, adjust the pH of the solution to 8.5 with sodium hydroxide, and add dopamine hydrochloride, stir well, add asphalt, and stir again After homogenization, stand for 24 hours to obtain polydopamine modified asphalt; the mass ratio of water, tris hydrochloride, dopamine hydrochloride, surfactant and asphalt is 32:3.8:1.7:3.2:62;
[0064] b) The weight parts obtained in step a) are 65 parts of modified asphalt, 26 parts by weight of EPDM rubber, 2.6 parts by weight of silane coupling agent, and 11 parts by weight. Asbestos lint, 1.6 parts by weight of carbon fiber, 1.8 parts by weight of vulcanizing agent, 3 parts by weight of vulcanizing agent, 1.1 parts by weight of antioxidant, and 22 parts by weight The filler, 0.75 parts by weight of anti-ultraviolet agent and 1.3 parts by weight of anti-aging agent are added to the high-speed mixing mixer, and stirred at 50°C for 90 minutes to obtain a mix...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap