Matt coated paper preparation method

A technology of coated paper and quality, applied in pulp beating method, special paper, paper, etc., can solve the problems of readers' eyes discomfort, reduce printing gloss, poor gloss of coated paper, etc., and achieve remarkable matte effect , highlight the effect of high quality and outstanding printing effect

Inactive Publication Date: 2018-02-02
安徽文峰新材料科技股份有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly used for printing covers and illustrations of high-end books and periodicals, color pictures, various exquisite product advertisements, samples, product packaging, trademarks, etc.; by coating white paint on the surface of the base paper, the surface printability of the coated paper can be improved; but the existing Although the gloss of the coated paper is high, the gloss is uneven, and the coated paper is dazzled when reading, which makes the reader's eyes feel very uncomfortable.
[0003] The existing patent "001108522" is a production method of high-grade matt coated paper, which discloses the use of hardwood pulp, softwood pulp, and self-made oxygen-alkali bleached wheat straw pulp to make base paper, using ultra-fine calcium carbonate, plastic pigments and high The coating made of glossy porcelain clay is used to coat the surface of the base paper. The glossiness of the coated paper made by it is small (printing glossiness-paper surface glossiness), the printability of graphics and texts is poor, and the matte effect is average. At the same time, it uses The high Guangze porcelain clay not only has a higher price and cost, but also has the negative impact of increasing roughness and reducing printing gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing matte coated paper, comprising the following steps:

[0021] (1) Base paper preparation: Mix coniferous wood pulp and reed pulp at a mass ratio of 1:10 to obtain a mixed pulp, add 5% starch by mass and 8% calcium sulfate by mass to the mixed pulp, and perform PFI grinding and beating , and then carry out papermaking and drying to obtain base paper;

[0022] (2) Preparation of coating: the coating is made of the following components in parts by weight: sizing material 70, starch 12, dispersant 1, flake zinc powder 3, flake sericite powder 3, spherical calcium carbonate 1; The mass ratio of flaky zinc powder, flaky sericite powder, and spherical calcium carbonate is 3:3:1;

[0023] (3) Coating: The coating prepared in step (2) is coated with a double-sided film coater, dried with hot air after coating, and then finished with a four-roll double-sided soft-tight calender , that is.

[0024] Further, the number of beating revolutions of the PFI mill...

Embodiment 2

[0033] A method for preparing matte coated paper, comprising the following steps:

[0034] (1) Base paper preparation: Mix coniferous wood pulp and reed pulp at a mass ratio of 1:12 to obtain a mixed pulp, add 5% of its mass of starch and 10% of its mass of calcium sulfate to the mixed pulp, and perform PFI grinding and beating , and then carry out papermaking and drying to obtain base paper;

[0035] (2) Preparation of coating: the coating is made of the following components in parts by weight: sizing material 80, starch 15, dispersant 3, flake zinc powder 9, flake sericite powder 9, spherical calcium carbonate 3; The mass ratio of flaky zinc powder, flaky sericite powder, and spherical calcium carbonate is 3:3:1;

[0036] (3) Coating: The coating prepared in step (2) is coated with a double-sided film coater, dried with hot air after coating, and then finished with a four-roll double-sided soft-tight calender , that is.

[0037] Further, the number of beating revolutions ...

Embodiment 3

[0046] A method for preparing matte coated paper, comprising the following steps:

[0047] (1) Base paper preparation: Mix coniferous wood pulp and reed pulp at a mass ratio of 1:11 to obtain a mixed pulp, add 5% starch by mass and calcium sulfate 9% by mass to the mixed pulp, and perform PFI grinding and beating , and then carry out papermaking and drying to obtain base paper;

[0048] (2) Preparation of coating: the coating is made of the following components in parts by weight: sizing material 75, starch 14, dispersant 2, flake zinc powder 6, flake sericite powder 6, spherical calcium carbonate 2; The mass ratio of flaky zinc powder, flaky sericite powder, and spherical calcium carbonate is 3:3:1;

[0049] (3) Coating: The coating prepared in step (2) is coated with a double-sided film coater, dried with hot air after coating, and then finished with a four-roll double-sided soft-tight calender , that is.

[0050] Further, the number of beating revolutions of the PFI mill...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a matt coated paper preparation method, and relates to the technical field of coated paper. The matt coated paper preparation method comprises the following steps: (1) raw paper preparation, (2) coating preparation, and (3) coating. The matt coated paper is not glaring during reading, difference between gloss of a printed product and gloss of paper is large, thus, high quality of the printed product is highlighted, images and texts are bright in color, and the printing adaptability is good.

Description

technical field [0001] The invention belongs to the technical field of coated paper, and in particular relates to a method for preparing matte coated paper. Background technique [0002] Coated paper is a high-grade printing paper made of base paper coated with white paint. It is mainly used for printing covers and illustrations of high-end books and periodicals, color pictures, various exquisite product advertisements, samples, product packaging, trademarks, etc.; by coating white paint on the surface of the base paper, the surface printability of the coated paper can be improved; but the existing Although high-quality coated paper has high gloss, the gloss is not uniform, and the coated paper is dazzling when reading, which makes the reader's eyes feel very uncomfortable. [0003] The existing patent "001108522" is a production method of high-grade matt coated paper, which discloses the use of hardwood pulp, softwood pulp, and self-made oxygen-alkali bleached wheat straw ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H11/04D21D1/02D21F11/00D21H23/22D21H25/06D21G1/00D21H17/28D21H17/66D21H19/54D21H19/64D21H19/38D21H19/40
CPCD21H27/00D21D1/02D21F11/00D21G1/00D21H11/04D21H17/28D21H17/66D21H19/385D21H19/40D21H19/54D21H19/64D21H23/22D21H25/06
Inventor 桑幸运
Owner 安徽文峰新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com