Mesoporous photocatalyst, and preparation method and application thereof

A photocatalyst and mesoporous technology, applied in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve undiscovered problems and achieve short reaction time, cost reduction, and low energy consumption.

Active Publication Date: 2018-03-06
DAQO GROUP CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, no complexation-calcination method has been found in mesoporous g-C 3 N 4 Simultaneous introduction of metallic Cu and non-metallic Cl elements to prepare dual-doped Cu / Cl-g-C 3 N 4 mesoporous photocatalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mesoporous photocatalyst, and preparation method and application thereof
  • Mesoporous photocatalyst, and preparation method and application thereof
  • Mesoporous photocatalyst, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1: 0.77wt% double doped Cu / Cl-g-C 3 N 4 Preparation of Mesoporous Photocatalysts

[0032] 1. Preparation of mesoporous g-C 3 N 4 catalyst of light

[0033] 1. Weigh urea, dry it in an oven at 80°C for 24 hours, grind it and put it into a crucible, cover it, and place it in a muffle furnace at 2°C min -1 The heating rate is from room temperature to 550°C, and calcined for 4h.

[0034] 2. Use 1mol L after taking it out -1 Soak and stir in nitric acid for 24 hours, filter, then wash with distilled water 7-8 times until neutral, and dry in an oven at 80°C for 24 hours.

[0035] 3. Take out the sample and grind it, place it in a crucible, and calcinate it in a muffle furnace at 500°C for 4 hours without a cover to obtain thermally exfoliated g-C 3 N 4 catalyst of light.

[0036] 2. Preparation of 0.77wt% double-doped Cu / Cl-g-C 3 N 4 mesoporous photocatalyst

[0037] 1. Accurately weigh 0.0023g cuprous chloride, dissolve it in 5mL ammonia water, and ultras...

Embodiment 2

[0043] Embodiment 2: 1.53wt% double doping Cu / Cl-g-C 3 N 4 Preparation of Mesoporous Photocatalysts

[0044] 1. Preparation of mesoporous g-C 3 N 4 catalyst of light

[0045] 1. Weigh a certain amount of urea, dry it in an oven at 80°C for 24 hours, grind it and put it into a crucible, cover it, and place it in a muffle furnace at 2°C min -1 The heating rate was heated from room temperature to 550°C, and calcined for 4h.

[0046] 2. Use 1mol L after taking it out -1 Soak in nitric acid and stir for 24 hours, then filter, then wash with distilled water 7-8 times until neutral, and dry in an oven at 80°C for 24 hours.

[0047] 3. Take out the sample and grind it, place it in a crucible, and calcinate it in a muffle furnace at 500°C for 4 hours without a cover for thermal exfoliation to obtain mesoporous g-C 3 N 4 catalyst of light.

[0048] 2. Preparation of 1.53wt% double-doped Cu / Cl-g-C 3 N 4 mesoporous photocatalyst

[0049] 1. Accurately weigh 0.0046g of cuprous ...

Embodiment 3

[0055] Embodiment 3: 4.57wt% double doping Cu / Cl-g-C 3 N 4 mesoporous photocatalyst

[0056] 1. Preparation of mesoporous g-C 3 N 4 catalyst of light

[0057] 1. Weigh a certain amount of urea, dry it in an oven at 80°C for 24 hours, grind it and put it into a crucible, cover it, and place it in a muffle furnace at 2°C min -1 The heating rate was heated from room temperature to 550°C, and calcined for 4h.

[0058] 2. Use 1mol L after taking it out -1 Soak in nitric acid and stir for 24 hours, then filter, then wash with distilled water 7-8 times until neutral, and dry in an oven at 80°C for 24 hours.

[0059] 3. Take out the sample and grind it, place it in a crucible, and calcinate it in a muffle furnace at 500°C for 4 hours without a cover for thermal exfoliation to obtain mesoporous g-C 3 N 4 catalyst of light.

[0060] 2. Preparation of 4.57wt% double-doped Cu / Cl-g-C 3 N 4 mesoporous photocatalyst

[0061] 1. Accurately weigh 0.0137g of cuprous chloride, dissol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of synthesis of a photocatalyst, and in particular relates to a mesoporous photocatalyst, and a preparation method and application thereof. The double doped Cu / Cl-g-C3N4 mesoporous photocatalyst is prepared by precisely controlling the reaction condition and the quantity of reactants; and the characterization result indicates that after pure g-C3N4 is doubly doped with metal Cu and non-metal Cl, the inherent mesoporous structure feature of the g-C3N4 is not changed, the specific surface area and the surface active sites are increased, the response range on visible light is expanded and the separation efficiency of current carriers is improved.

Description

technical field [0001] The invention belongs to the technical field of photocatalyst synthesis, and uses a complexation-calcination method to synthesize Cu / Cl-g-C double-doped with metallic Cu and non-metallic Cl elements 3 N 4 Mesoporous photocatalyst for visible light degradation of tetracycline hydrochloride pollutants. Background technique [0002] In recent years, antibiotics have been widely used in the treatment of diseases in humans and animals. Due to the large amount of use, it has caused a certain degree of environmental pollution. Among them, tetracycline hydrochloride, as a kind of antibiotics, ranks second in the global production and use, and its environmental residues will cause a series of ecological pollution; at the same time, it will also produce drug resistance to bacteria and affect human health. Therefore, it is imminent to effectively remove tetracycline hydrochloride residues in the environment. After research, it was found that some conventional...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/24B01J35/10C02F1/30C02F101/38C02F101/34C02F101/36
CPCC02F1/30B01J27/24C02F2305/10C02F2101/34C02F2101/38C02F2101/36B01J35/64B01J35/39
Inventor 李春梅吴海君董红军刘春波车慧楠张晓旭艾俊哲
Owner DAQO GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com