Waterproof putty powder and preparation method thereof

A water-resistant putty and putty powder technology, which is applied in the field of paint fillers, can solve the problems that water-resistant putty powder has not yet appeared, and achieve the effects of less volatile gas, simple production process, and low cost

Inactive Publication Date: 2018-03-09
NANJING YIHE CULTURE CREATIVE CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of the times, people's concept of healthy life is rising, and the environment-friendly water-resistant putty powder has not yet appeared.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A water-resistant putty powder, which is composed of the following components according to the following weight fractions: 41 parts of kaolin powder, 6 parts of montmorillonite, 4 parts of hydroxypropyl methylcellulose, 0.5 parts of polyacrylamide, 8 parts of titanium dioxide, polydimethyl 1 part of base siloxane, 15 parts of sepiolite powder, 5.6 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0017] A kind of preparation method of water-resistant putty powder,

[0018] Step 1: Weigh the ingredients and prepare them;

[0019] Step 2: mixing and pulverizing;

[0020] Step 3: Add water and stir the mold to form a paste;

[0021] Step 4: The paste obtained in Step 3 is pulverized;

[0022] Step 5: Defoaming and grinding the material obtained in Step 3, the particle size is less than 0.025mm, to obtain water-resistant putty powder.

[0023] Furthermore, the amount of water added in step 3 is 45% of the total weight of ingredients.

Embodiment 2

[0025] A water-resistant putty powder, which is composed of the following components according to the following weight fractions: 35 parts of kaolin powder, 5 parts of montmorillonite, 2 parts of hydroxypropyl methylcellulose, 0.1 part of polyacrylamide, 7 parts of titanium dioxide, polydimethylsiloxane 1 part of base siloxane, 13 parts of sepiolite powder, 0.3 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0026] A kind of preparation method of water-resistant putty powder,

[0027] Step 1: Weigh the ingredients and prepare them;

[0028] Step 2: mixing and pulverizing;

[0029] Step 3: Add water and stir the mold to form a paste;

[0030] Step 4: The paste obtained in Step 3 is pulverized;

[0031] Step 5: Defoaming and grinding the material obtained in Step 3, the particle size is less than 0.025mm, to obtain water-resistant putty powder.

[0032] Furthermore, the amount of water added in step 3 is 30% of the total weight of ingredients.

Embodiment 3

[0034] A water-resistant putty powder, which is composed of the following components according to the following weight fractions: 50 parts of kaolin powder, 7 parts of montmorillonite, 5 parts of hydroxypropyl methylcellulose, 0.7 parts of polyacrylamide, 10 parts of titanium dioxide, polydimethyl 3 parts of base siloxane, 17 parts of sepiolite powder, 7 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.

[0035] A kind of preparation method of water-resistant putty powder,

[0036] Step 1: Weigh the ingredients and prepare them;

[0037] Step 2: mixing and pulverizing;

[0038] Step 3: Add water and stir the mold to form a paste;

[0039] Step 4: The paste obtained in Step 3 is pulverized;

[0040] Step 5: Defoaming and grinding the material obtained in Step 3, the particle size is less than 0.025mm, to obtain water-resistant putty powder.

[0041] Furthermore, the amount of water added in step 3 is 60% of the total weight of ingredients.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-resistant putty powder and a preparation method thereof, belonging to the field of fillers for coatings. Composed of the following components according to the following weight fractions: 35-50 parts of kaolin powder, 5-7 parts of montmorillonite, 2-5 parts of hydroxypropyl methylcellulose, 0.1-0.7 parts of polyacrylamide, 7-10 parts of titanium dioxide , 1-3 parts of polydimethylsiloxane, 13-17 parts of sepiolite powder, 0.3-7 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate. The putty powder provided by the invention has high water resistance, acid and alkali corrosion resistance, resistance to cold and hot temperature changes, and high bonding strength. The invention is safe and healthy, the material is easy to obtain, and the cost is low, and the preparation method is simple.

Description

technical field [0001] The invention belongs to the field of fillers for coatings, and in particular relates to a water-resistant putty powder and a preparation method thereof. Background technique [0002] The main purpose of water-resistant putty powder is to fill the pores of the construction surface and correct the curve deviation of the construction surface, laying a good foundation for obtaining a uniform and smooth paint surface. Water-resistant putty powder, as one of the categories, is mainly used on walls or surfaces that require waterproofing. Water resistance and high bonding strength are required to ensure that under the long-term erosion of water vapor in the air, there will be no hollowing, peeling, cracking, etc., and it can still be tightly combined with the substrate and not easy to fall off. If it is used as a relocation coating, acid and alkali resistance is also required, and the temperature tolerance range is large. At present, the water resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 王军红
Owner NANJING YIHE CULTURE CREATIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com