Porous ceramic with good low-temperature-resisting effect and preparation method thereof
A technology of porous ceramics and low temperature resistance, applied in the field of porous ceramics, can solve the problems of inconvenient use, short service life, and easy aging of porous ceramics, and achieve the effect of improving mechanical properties, meeting the needs of use, and solving low temperature aging problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] A porous ceramic with good low temperature resistance effect, comprising the following raw materials in parts by weight: 12 parts of reed, 45 parts of diatomaceous earth, 0.6 part of lignocellulose, 10 parts of alumina, 4 parts of nano-zirconia, 30 parts of bentonite, zeolite powder 26 parts of potassium feldspar, 24 parts of potassium feldspar, 16 parts of clay, 1.5 parts of potassium chloride, 3 parts of vitrified microbeads, 8 parts of resin, 3 parts of glycerin, 16 parts of ethanol and 6 parts of water lily. The resin is a mixture of polypropylene and polyvinyl chloride, and the particle size of alumina is 0.1mm.
[0022] The preparation method of the porous ceramic with good low temperature resistance effect, the specific steps are as follows:
[0023] Step 1: Soak the reed in acetone and ultrasonically treat it for 60 minutes, wash it with deionized water 4 times and then dry it in vacuum. Put the treated reed in a 0.25mol / L sodium hydroxide solution and stir for ...
Embodiment 2
[0030] A porous ceramic with good low temperature resistance effect, comprising the following raw materials in parts by weight: 0.1 parts of alloy powder, 14 parts of reed, 52 parts of diatomite, 1.3 parts of lignocellulose, 15 parts of alumina, 6 parts of nano-zirconia, bentonite 36 parts of zeolite powder, 33 parts of zeolite powder, 25 parts of potassium feldspar, 20 parts of clay, 3 parts of potassium chloride, 4.5 parts of vitrified microbeads, 12 parts of resin, 4 parts of glycerin, 18 parts of ethanol and 8 parts of water lily.
[0031] The preparation method of the porous ceramic with good low temperature resistance effect, the specific steps are as follows:
[0032] Step 1, soak the reed in acetone and ultrasonically treat it for 75 minutes, wash it with deionized water three times and then dry it in vacuum. Put the treated reed in 0.3mol / L sodium hydroxide solution and stir for 36 minutes, and dry it at 60 degrees Celsius Send into carbonization furnace afterward, th...
Embodiment 3
[0039] A porous ceramic with good low temperature resistance effect, comprising the following raw materials in parts by weight: 0.25 parts of alloy powder, 16 parts of reed, 56 parts of diatomite, 1.8 parts of lignocellulose, 18 parts of alumina, 8 parts of nano-zirconia, bentonite 40 parts, 35 parts of zeolite powder, 28 parts of potassium feldspar, 24 parts of clay, 4 parts of potassium chloride, 6 parts of vitrified microbeads, 15 parts of resin, 5 parts of glycerin, 20 parts of ethanol and 10 parts of water lily. The resin is a mixture of polypropylene, polyvinyl chloride, polytetrafluoroethylene and natural rubber, and the particle size of aluminum oxide is 0.7mm.
[0040] The preparation method of the porous ceramic with good low temperature resistance effect, the specific steps are as follows:
[0041] Step 1, soak the reed in acetone and ultrasonically treat it for 90 minutes, wash it with deionized water for 4 times and then dry it in vacuum. Put the treated reed in 0...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap