Weathering resistance enhancing coating varnish and preparation method and application thereof

A varnish and weather-resistant technology, which is applied in coatings, reflective/signal coatings, polyurea/polyurethane coatings, etc., can solve the problems of difficult to improve the weather resistance of coatings supporting coatings, achieve the best decorative effect, good construction performance, The effect of high solids content

Inactive Publication Date: 2018-05-18
ZHEJIANG SHUREN UNIV
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to: through the light transmittance influence and test research of the finish varnish, achieve the purpose of strengthening the weather resistance of the supporting coating by reducing the light transmittance of the coating, and solve the general difficulty in the weather resistance of the supporting coating of the coating in the prior art. raised questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Weathering resistance enhancing coating varnish and preparation method and application thereof
  • Weathering resistance enhancing coating varnish and preparation method and application thereof
  • Weathering resistance enhancing coating varnish and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0078] Ratio of main raw materials: main agent: curing agent = 100 parts: 30 parts.

[0079] in:

[0080] Main agent:

[0081]

[0082]

[0083] Wherein the main agent solvent ratio is:

[0084] Butyl propionate 16.0 parts

[0085] Heavy aromatics 5.0 parts

[0086] Ethylene glycol butyl ether acetate 2.0 parts

[0087] hardener:

[0088] Polyisocyanate 21.5 parts

[0089] Water absorbent 1.0 parts

[0090] Solvent 8.4 parts

[0091] Wherein the solvent ratio in the hardener is:

[0092] Butyl propionate 6.8 parts

[0093] Heavy aromatics 1.0 parts

[0094] Ethylene glycol butyl ether acetate 0.6 parts.

Embodiment 2

[0096] Ratio of main raw materials: main agent: curing agent = 100 parts: 50 parts.

[0097] in:

[0098] Main agent:

[0099]

[0100] Wherein the main agent solvent ratio is:

[0101] Butyl propionate 9.2 parts

[0102] 1.7 parts of heavy aromatics

[0103] Ethylene glycol butyl ether acetate 2.1 parts

[0104] hardener:

[0105] 31.5 parts of polyisocyanate

[0106] 1.5 parts of water absorbent

[0107] Solvent 18.35 parts

[0108] Wherein the solvent ratio in the hardener is:

[0109] Butyl propionate 16.6 parts

[0110] 1.7 parts of heavy aromatics

[0111] Ethylene glycol butyl ether acetate 0.05 parts.

Embodiment 3

[0113] Ratio of main raw materials: main agent: curing agent = 100 parts: 40 parts

[0114] Main ingredient:

[0115]

[0116] Wherein the main agent solvent ratio is:

[0117] Butyl propionate 14.0 parts

[0118] 2.5 parts of heavy aromatics

[0119] Ethylene glycol butyl ether acetate 1.4 parts

[0120] hardener:

[0121] Polyisocyanate 27.5 parts

[0122] Water absorbent 1.2 parts

[0123] Solvent 12.38 parts

[0124] Wherein the solvent ratio in the hardener is:

[0125] Butyl propionate 10.8 parts

[0126] Heavy aromatics 1.0 parts

[0127] Ethylene glycol butyl ether acetate 0.58 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
adhesivityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a weathering resistance enhancing coating varnish and a preparation method and application thereof. The weathering resistance enhancing coating varnish is prepared from a mainagent and a hardener, wherein the parts by weight of the main agent and the hardener are (100:30) to (100:50). The weathering resistance enhancing coating varnish is prepared from the main agent usingpolyurethane acrylate resin along with filler, catalyst, defoaming agent, leveling agent, light absorbent, light stabilizer, solvent and other materials and then cooperating with polyisocyanate, water absorbent, solvent and the like of the hardener. The coating varnish can be applied on a matched coating layer under the condition of self-dying or medium-and-low-temperature baking, and the thickness of a varnish film applied once is 30 Mu m to 40 Mu m. The coating varnish enhances the weathering resistance of the original matched coating, solves the problem that ordinary coating varnish only has decorativeness and cannot effectively enhance the weathering resistance of coating, and in particular, plays an important role in enhancing the weathering resistance of non-flashing finishing paint.

Description

technical field [0001] The invention relates to the technical field of enhanced protection for spray-coated substrate products matched with coatings, in particular to a preparation method and application of an acrylic polyurethane finish varnish with enhanced weather resistance. Background technique [0002] Coating and coating matching has always focused on the improvement of weather resistance on the top coat, but this performance has developed to a certain bottleneck stage, and it is difficult to improve without new materials. Because the transparency of the varnish will make the matching coating film look plump and bright, but the light will directly destroy the topcoat through the varnish coating, so that the weather resistance of the topcoat is the same as that of the supporting coating . For a long time, the matching of paint coating is to spray finish varnish on the metallic paint coating and the solid color topcoat is not sprayed with finish varnish. Accompanied b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D5/33C09D7/20C09D7/47C09D7/65
CPCC09D175/14C08K2201/011C08L2201/08C08L2201/10C08L2205/025C08L2205/03C09D5/004C08L83/04C08K5/1345C08K3/34
Inventor 饶桂维
Owner ZHEJIANG SHUREN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com