Corrosion-resistant Ta-containing magnesium alloy suitable for cold chamber die casting and processing technology thereof

A cold-chamber die-casting and corrosion-resistant technology, applied in the field of alloys, can solve the problems of toxic gas pollution, increase costs, flux inclusions, etc., and achieve excellent mechanical properties, increase production costs, and improve the effect of die casting yield.

Inactive Publication Date: 2018-07-06
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these two methods have their unavoidable defects, such as easy to produce toxic gas to pollute the environment and cause flux inclusions to damage the properties of the alloy
In addition, the smelting and pouring equipment and processes are complicated, which increases the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A corrosion-resistant Ta-containing magnesium alloy suitable for cold chamber die-casting smelted at 750 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 0.6wt.%, Ta: 1.8wt.%; Mn: 2.3wt.%, Si: 6.2wt.%, Sc: 0.6wt.%, B: 0.5wt.% .%, and the balance is magnesium. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 750 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 750°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 12m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare magnesium-calcium alloy castings with compl...

Embodiment 2

[0020]A corrosion-resistant Ta-containing magnesium alloy suitable for cold chamber die-casting smelted at 770 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 0.5wt.%, Ta: 1.6wt.%; Mn: 2.4wt.%, Si: 6.5wt.%, Sc: 0.6wt.%, B: 0.5wt .%, and the balance is magnesium. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 770 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 770°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots. The ingot moves down at a speed of 12m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare magnesium-calcium alloy castings with complex ...

Embodiment 3

[0023] A corrosion-resistant Ta-containing magnesium alloy suitable for cold chamber die-casting smelted at 790 degrees. In terms of weight percentage, the chemical composition of the alloy is: Ca: 0.7wt.%, Ta: 1.8wt.%; Mn: 2.3wt.%, Si: 6.8wt.%, Sc: 0.7wt.%, B: 0.5wt.% .%, and the balance is magnesium. The preparation method of the alloy: add the above-mentioned raw materials into the atmosphere-protected induction furnace, and use a silicon carbide crucible; induction heat to 790 degrees to form an alloy solution, and use the electromagnetic stirring effect to fully stir for about 10 minutes; put the alloy liquid in After standing at 790°C for 10 minutes, it is cast into the equipment at the same level as the hot top for semi-continuous casting into the required square and round ingots, with the ingot moving down at a speed of 14m / min. The ingot can be used as casting raw material for pressure casting in the subsequent process to prepare magnesium-calcium alloy castings with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses corrosion-resistant Ta-containing magnesium alloy suitable for cold chamber die casting and a processing technology thereof. The alloy is prepared from the following componentsin percentage by weight: 0.5-0.8wt.% of Ca, 1.6-1.9wt.% of Ta, 2.0-2.4wt.% of Mn, 5.0-8.2wt.% of Si, 0.5-0.8wt.% of Sc, 0.4-0.9wt.% of B and the balance of magnesium. The magnesium-calcium alloy hasexcellent die casting properties and excellent corrosion resistance and is expected to have a promotion effect of enabling fine new materials independently researched and developed in China to occupythe market of international fine new materials.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a magnesium-calcium alloy. Background technique [0002] Magnesium alloy is an alloy composed of magnesium and other elements. It is the lightest metal structure material used in aircraft, spacecraft and rocket missile manufacturing industries. Magnesium is lighter in weight and lower in strength than aluminum, and is mainly used in the manufacture of low-load parts. Magnesium alloy has high anti-vibration ability, can absorb large energy when subjected to impact load, and has good heat absorption performance, so it is an ideal material for manufacturing aircraft hubs. Magnesium alloy is very stable in gasoline, kerosene and lubricating oil, suitable for manufacturing engine gear casings, oil pumps and oil pipes, and is used to manufacture rocker arms, flaps, Moving parts such as doors and rudder surfaces. Magnesium alloy products are widely used in civil aircraft and military ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/00C22C1/02B22D17/00C22F1/06C22F1/02
CPCC22C23/00B22D17/00C22C1/02C22F1/02C22F1/06
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com