Method for preparing antioxidative polyester sheet
A polyester sheet, anti-oxidation technology, applied in the direction of coating, etc., can solve the problems of low fastness and poor durability, and achieve the effect of good anti-oxidation durability, low price, and good light transmission
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] The invention provides a preparation method of an anti-oxidation polyester sheet, the steps are as follows:
[0025] (1) Weigh 40 parts by mass of methyl acrylate, 25 parts by mass of ethyl acrylate, 20 parts by mass of n-butyl acrylate, and 15 parts by mass of methacrylic acid and mix them uniformly to obtain a mixed reaction monomer; weigh 100 parts by mass of the mixed reaction monomer Parts by mass, a combination of emulsifier AEO-9 and K-12 (mass ratio 1:1) 2 parts by mass, initiator sodium persulfate 0.2 parts by mass and antioxidant 1010 0.5 parts by mass; Add the combination of AEO-9 and K-12 (mass ratio 1:1) at 50°C, add 1 / 4 (mass) sodium persulfate at 80°C, and then drop the mixed reaction monomer and 3 / 4 (mass) Sodium persulfate and continue to heat up; 3h dropwise addition is completed, at 90°C for 2h at a constant temperature; cooling down, adding antioxidant 1010 at a temperature of 50°C, keeping it warm for 1h, then cooling down to normal temperature to o...
Embodiment 2
[0029] The invention provides a preparation method of an anti-oxidation polyester sheet, the steps are as follows:
[0030] (1) Weigh 47 parts by mass of methyl acrylate, 23 parts by mass of ethyl acrylate, 18 parts by mass of n-butyl acrylate, and 12 parts by mass of methacrylic acid and mix them uniformly to obtain a mixed reaction monomer; weigh 100 parts by mass of the mixed reaction monomer Parts by mass, a combination of emulsifier AEO-9 and K-12 (mass ratio 1:1) 3 parts by mass, initiator sodium persulfate 0.4 parts by mass, antioxidant 1076 0.75 parts by mass, and antioxidant 168 0.75 parts by mass; Reactor Add water into the medium and raise the temperature, add the combination of AEO-9 and K-12 (mass ratio 1:1) at 30°C, add 1 / 4 (mass) sodium persulfate at 70°C; when the temperature rises to 75°C, drop Add mixed reaction monomers and 3 / 4 (mass) sodium persulfate and continue to heat up; 4 hours to complete the dropwise addition, and react at a constant temperature of ...
Embodiment 3
[0034] The invention provides a preparation method of an anti-oxidation polyester sheet, the steps are as follows:
[0035] (1) Weigh 44 parts by mass of methyl acrylate, 20 parts by mass of ethyl acrylate, 18 parts by mass of n-butyl acrylate, and 18 parts by mass of methacrylic acid and mix them uniformly to obtain a mixed reaction monomer; weigh 100 parts by mass of the mixed reaction monomer Parts by mass, 4 parts by mass of the combination of emulsifier AEO-9 and K-12 (mass ratio 1:1), 0.6 parts by mass of initiator sodium persulfate and 1 part by mass of antioxidant 1076; Add the combination of AEO-9 and K-12 at 40°C, add 1 / 4 (mass) sodium persulfate at 70°C; add the mixed reaction monomer and 3 / 4 (mass) persulfuric acid dropwise when the temperature rises to 75°C Add sodium and continue to heat up; 5h dropwise addition is completed, and react at a constant temperature of 85°C for 3h; cool down, add antioxidant 1076 at a temperature of 40°C, keep warm for 1.5h, and then ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com