PVC (polyvinyl chloride) board with high inflaming retardance
A PVC board and high flame retardant technology, applied in the field of high flame retardant PVC board, can solve the problems of poor flame retardant effect and low safety performance, and achieve the effect of good flame retardant effect, normal color and high hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] A high flame-retardant PVC board is composed of the following components by weight: 120 parts of PVC waste, 40 parts of calcium powder, 10 parts of stabilizers, 5 parts of tribasic lead sulfate, 3 parts of chlorinated paraffin, foaming 1 part of agent, 0.3 part of white foaming agent, 4 parts of flame retardant, 0.1 part of pigment;
[0032] The preparation steps are as follows:
[0033] (1) Weigh the raw materials by weight and mix them evenly at 65°C;
[0034] (2) Feed the uniformly mixed raw materials into the extruder for foaming, and then extrude through the extrusion die. The temperature of the extruder is controlled to 185°C, and the temperature of the cooling water flowing into the extrusion die is 12 ℃;
[0035] (3) Cool and shape the molten material leaving the extrusion die to obtain the high flame retardant PVC board.
Embodiment 2
[0037] A high flame-retardant PVC board is composed of the following components by weight: 130 parts of PVC waste, 65 parts of calcium powder, 15 parts of stabilizer, 8 parts of tribasic lead sulfate, 5 parts of chlorinated paraffin, foaming 3 parts of white foaming agent, 6 parts of flame retardant, 0.3 parts of pigment;
[0038] The preparation steps are as follows:
[0039] (1) Weigh the raw materials by weight and mix them evenly at 65°C;
[0040] (2) Feed the uniformly mixed raw materials into the extruder for foaming, and then extrude through the extrusion die. The temperature of the extruder is controlled to 185°C, and the temperature of the cooling water flowing into the extrusion die is 12 ℃;
[0041] (3) Cool and shape the molten material leaving the extrusion die to obtain the high flame-retardant PVC board.
Embodiment 3
[0043] A high flame retardant PVC board is composed of the following components by weight: 125 parts of PVC waste, 63 parts of calcium powder, 11 parts of stabilizers, 7 parts of tribasic lead sulfate, 4 parts of chlorinated paraffin, foaming 2 parts of white foaming agent, 0.4 parts of white foaming agent, 5 parts of flame retardant, 0.2 parts of pigment;
[0044] The preparation steps are as follows:
[0045] (1) Weigh the raw materials by weight and mix them evenly at 65°C;
[0046] (2) Feed the uniformly mixed raw materials into the extruder for foaming, and then extrude through the extrusion die. The temperature of the extruder is controlled to 185°C, and the temperature of the cooling water flowing into the extrusion die is 12 ℃;
[0047] (3) Cool and shape the molten material leaving the extrusion die to obtain the high flame retardant PVC board.
PUM
Property | Measurement | Unit |
---|---|---|
Shore hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap