Lightweight wood plastic foam board and preparation method thereof

A wood-plastic foaming, lightweight technology, applied in the field of wood-plastic board manufacturing, can solve the problems of reduced practical performance of finished wood-plastic boards, affecting product appearance and sales, poor mechanical properties, etc., to improve production efficiency and production quality, Good consistency and long service life

Inactive Publication Date: 2018-08-28
HEFEI SHANGHAN DECORATION ENG CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The PVC foamed wood-plastic material prepared by the current process formula is prone to problems such as delamination, uneven bubbles, and poor mechanical properties when producing floors, which not only affects the appearance and sales of the product, but also greatly reduces the practical performance of the finished wood-plastic board. , therefore, need to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lightweight wood plastic foam board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A lightweight wood-plastic foam board, weighing the following raw materials: 60kg of PVC resin, 20g of terpene resin, 10kg of methyl acrylate, 25kg of modified ramie fiber, 6kg of corn straw powder, 4kg of barium feldspar powder, and faujasite powder 3kg, methyl pentachlorostearate 2kg, oxidized polyethylene wax 1kg, azobisisoheptanonitrile 1kg, N-methylolacrylamide 1kg, calcium zinc stabilizer 1kg, triethoxybutane 1kg, silicone resin Polyether emulsion 1kg, silane coupling agent KH1721kg and trihydroxymethyl phosphorus oxide 1kg;

[0027] Preparation of modified ramie fiber:

[0028] Step 1: Take 25 kg of raw ramie fibers, cut them to a length of less than or equal to 3 mm by a chopping device to obtain chopped ramie fibers; put the chopped ramie fibers into hydrogen peroxide with a volume concentration of 8% for 50 minutes, take them out, and wash them until medium Drying in an oven with a working temperature of 80°C for 35 minutes;

[0029] Step 2: put the chopped ...

Embodiment 2

[0036] A lightweight wood-plastic foam board, weighing the following raw materials: PVC resin 70kg, terpene resin 25kg, methyl acrylate 15kg, modified ramie fiber 30kg, corn straw powder 8kg, feldspar powder 6kg, faujasite powder 4kg, methyl pentachlorostearate 3kg, oxidized polyethylene wax 2kg, azobisisoheptanonitrile 1.5kg, N-methylolacrylamide 1.25kg, calcium zinc stabilizer 1.5kg, sodium azobisisobutyronitrile 3kg, polyacrylamide 1.5kg, silane coupling agent KH5503kg and diphenyl phosphate 2kg;

[0037] Preparation of modified ramie fiber:

[0038] Step 1: Take 30kg of raw ramie fibers, cut them to a length less than or equal to 2mm by a chopping device to obtain chopped ramie fibers; put the chopped ramie fibers into hydrogen peroxide with a volume concentration of 10% for 55 minutes, take them out, and wash them until medium Drying treatment in an oven with a working temperature of 85°C for 40 minutes;

[0039] Step 2: put the chopped ramie fiber treated in step 1 int...

Embodiment 3

[0046] A lightweight wood-plastic foam board, weighing the following raw materials: PVC resin 80kg, terpene resin 30kg, methyl acrylate 20kg, modified ramie fiber 35kg, corn straw powder 10kg, feldspar powder 8kg, faujasite powder 5kg, methyl pentachlorostearate 4kg, oxidized polyethylene wax 3kg, azobisisoheptanonitrile 2kg, N-methylolacrylamide 1.5kg, calcium zinc stabilizer 2kg, azodicarbonamide 5kg, polyethylene Alcohol foam stabilizer 2kg, silane coupling agent KH1715kg and dipentaerythritol 3kg;

[0047] Preparation of modified ramie fiber:

[0048] Step 1: Take 35 kg of raw ramie fibers, cut them to a length of less than or equal to 3 mm by a chopping device to obtain chopped ramie fibers; put the chopped ramie fibers into hydrogen peroxide with a volume concentration of 12% and soak them for 60 minutes, take them out, and wash to medium Drying in an oven with a working temperature of 90°C for 45 minutes;

[0049] Step 2: put the chopped ramie fiber treated in step 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a lightweight wood plastic foam board and a preparation method thereof and relates to the technical field of wood plastic board manufacturing. The foam board is prepared from the following raw materials: PVC resin, terpene resin, methyl acrylate, modified ramie fibers, corn straw powder, barium feldspar powder, faujasite powder, methylpentachlorostearate, oxidized polyethlene wax, azo-bis-iso-heptonitrile, N-hydroxymethyl acrylamide, a calcium-zinc stabilizer, a foaming agent, a foam stabilizer, a coupling agent and a flame retardant. The preparation method of the lightweight wood plastic foam board is characterized in that the lightweight wood plastic foam board is prepared by mixing and extruding the raw materials. The wood plastic foam board disclosed by the invention has the characteristics of simple and convenient preparation, stable mechanical property, high yield strength, good toughness, heat insulation, flame retardance, water resistance and impermeability.

Description

technical field [0001] The invention relates to the technical field of wood-plastic board manufacture, in particular to a lightweight wood-plastic foam board and a preparation method thereof. Background technique [0002] Wood-plastic board is a new type of environmentally friendly wood-plastic composite material product. The wood powder produced during the production of medium and high-density fiberboards is added to recycled plastics to make wood-plastic composite materials through granulation equipment, and then extruded into production groups. Made into wood-plastic flooring. The PVC foamed wood-plastic material prepared by the current process formula is prone to problems such as delamination, uneven bubbles, and poor mechanical properties when producing floors, which not only affects the appearance and sales of the product, but also greatly reduces the practical performance of the finished wood-plastic board. , therefore, needs to be improved. Contents of the inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L45/00C08L1/02C08L97/02C08L23/30C08K13/02C08K3/34C08K5/101C08K5/523C08K5/06C08J9/14C08J9/10
CPCC08J9/103C08J9/0023C08J9/0038C08J9/0061C08J9/0066C08J9/102C08J9/142C08J2203/04C08J2203/12C08J2327/06C08J2401/02C08J2423/30C08J2445/00C08J2497/02C08K3/34C08K5/06C08K5/101C08K5/523C08K13/02
Inventor 俞克波
Owner HEFEI SHANGHAN DECORATION ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap