A water-repellent and cloth-based technology, applied in coatings, textiles, and papermaking, can solve problems such as poor waterproof performance, and achieve the effects of improving wear resistance and water resistance, strong operability, and glossiness
Inactive Publication Date: 2018-08-28
SIYANG SHENJIU HOME TEXTILE FABRIC CO LTD
View PDF7 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The current TNC fabric has poor waterproof performance, and it cannot impro
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] A wear-resistant TNC fabric with excellent water resistance, comprising a TNC fabric layer and wear-resistant and waterproof layers arranged on the upper and lower sides of the TNC fabric layer, the wear-resistant and waterproof layer is calculated in parts by weight, and its raw material formula is as follows :
[0016] 1000 parts of isopropyl tris(dioctyl phosphate acyloxy) titanate, 1300 parts of N,N-dimethyldodecylamide, 1000 parts of nitrocellulose with a particle size of 5-15 μm, 1200 parts of polypropylene, and ethyl acrylic acid 1200 parts of ester, 50 parts of high alumina bauxite, 10 parts of PVC resin, and 80 parts of nano-alumina.
Embodiment 2
[0018] A wear-resistant TNC fabric with excellent water resistance, comprising a TNC fabric layer and wear-resistant and waterproof layers arranged on the upper and lower sides of the TNC fabric layer, the wear-resistant and waterproof layer is calculated in parts by weight, and its raw material formula is as follows :
[0019] 1,500 parts of isopropyl tris(dioctyl phosphate acyloxy) titanate, 1,000 parts of N,N-dimethyldodecylamide, 1,500 parts of nitrocellulose with a particle size of 5-15 μm, 800 parts of polypropylene, ethyl acrylic acid 1800 parts of ester, 35 parts of high alumina bauxite, 20 parts of PVC resin, and 50 parts of nano-alumina.
Embodiment 3
[0021] A wear-resistant TNC fabric with excellent water resistance, comprising a TNC fabric layer and wear-resistant and waterproof layers arranged on the upper and lower sides of the TNC fabric layer, the wear-resistant and waterproof layer is calculated in parts by weight, and its raw material formula is as follows :
[0022] 1200 parts of isopropyl tris(dioctyl phosphate acyloxy) titanate, 1000 parts of N,N-dimethyldodecylamide, 1200 parts of nitrocellulose with a particle size of 5-15 μm, 1000 parts of polypropylene, and ethyl acrylic acid 1500 parts of ester, 45 parts of high alumina bauxite, 15 parts of PVC resin, 60 parts of nano-alumina.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a wear-resistant TNC fabric with excellent waterproof performance. The wear-resistant TNC fabric comprises a TNC fabric layer and a wear-resistant waterproof layer arranged oneach of the upper side and the lower side of the TNC fabric layer; the wear-resistant waterproof layer comprises the following raw materials in part by weight: 1000-1500 parts of isopropyl tris (dioctyl phosphate acyloxy) titanate, 1000-1300 parts of N,N-dimethyl dodecylamine, 1000-1500 parts of nitrocellulose with a particle size of 5-15 mum, 800-1200 parts of polypropylene, 1200-1800 parts of ethyl acrylate, 35-50 parts of high bauxite, 10-20 parts of PVC resin, 50-80 parts of nanometer aluminum trioxide, 60-90 parts of dipentaerythritol and 30-60 parts of isocyanate. The wear-resistant TNCfabric disclosed by the invention has the advantages of being free from by-products, strong in operability, effectively-controllable in production cost and the like; the isopropyl tris (dioctyl phosphate acyloxy) titanate in a formula can improve the wear resistance and the waterproof performance of the TNC fabric, and meanwhile, the brightness and the glossiness of the TNC fabric can be improved.
Description
technical field [0001] The present invention relates to a wear-resistant and water-repellent excellent TNC cloth. Background technique [0002] TNC fabrics use high-tech fibers, that is, super fibers (nylon, polyester) combined with high-count cotton yarns, that is, the latest popular fabrics woven with three-in-one composite fibers. The fabric takes advantage of the characteristics of polyester, nylon, and cotton fibers, and integrates the advantages of the three fibers. It has good wear resistance, good elastic recovery rate, good strength, delicate and smooth hand feeling, comfortable and breathable, and novel style. Chic, it is an ideal clothing fabric. The current TNC fabric has poor waterproof performance and cannot take into account its abrasion resistance while improving waterproof performance. Contents of the invention [0003] The technical problem to be solved by the invention is to overcome the existing defects and provide a TNC fabric with excellent wear res...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more