Processing technology for flame-retardant anti-radiation fabric

A processing technology and radiation protection technology, which is applied in the processing of textile materials, spraying/jetting textile materials, fabric surface trimming, etc., can solve the problems of inconvenient processing and no processing technology for radiation protection fabrics, and achieve the effect of convenient processing.

Inactive Publication Date: 2018-08-31
HAINING TIANFU WARP KNITTING
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the anti-radiation fabric disclosed in this patent can achieve the effect of anti-radiation, the anti-radiation fabric does not have a corresponding pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology for flame-retardant anti-radiation fabric
  • Processing technology for flame-retardant anti-radiation fabric

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] The following are specific embodiments of the present invention in conjunction with the accompanying drawings to further describe the technical solutions of the present invention, but the present invention is not limited to these embodiments.

[0028] The processing technology of the flame-retardant and anti-radiation fabric includes the following steps: a. Weaving the warp yarn and the weft yarn into the required fabric, the warp yarn is a blended yarn of silver fiber and cotton fiber, and the weft yarn is a blended yarn of bamboo fiber and polyester fiber. B. Weigh 5-10 parts by weight of magnesium hydroxide, 4-6 parts by weight of aluminum hydroxide, 1-3 parts by weight of defoaming agent and 50-70 parts by weight of water and put them into the blender, fully stir to obtain a coating C. Spray the agitated coating solution on the surface of the woven fabric through a spraying machine; d. Put the sprayed fabric into an oven, the heating temperature is 75-85℃, and the heati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a processing technology for a flame-retardant anti-radiation fabric. The technical problems that corresponding processing technologies are not used in an existing anti-radiationfabric, and processing is inconvenient are solved. The processing technology for the flame-retardant anti-radiation fabric includes the following steps that a, warp yarn and weft yarn are woven intoa required fabric, wherein the warp yarn adopts blended yarn of sliver fibers and cotton fibers, and the weft yarn adopts blended yarn of bamboo fibers and polyester fibers; b, 5-10 parts by weight ofmagnesium hydrate, 4-6 parts by weight of aluminum hydroxide, 1-3 parts by weight of antifoaming agent and 50-70 parts by weight of water are weighed and put into a stirring machine together, and spraying liquid is prepared; c, the stirred spraying liquid is sprayed to the surface of the woven fabric through a spraying machine; d, the sprayed fabric is put into a drying oven; e, the hot-dried fabric is put into a baking machine; f, the baked fabric is put into a shaping machine, and the flame-retardant anti-radiation fabric is prepared. The processing technology for the flame-retardant anti-radiation fabric has the advantage that processing is convenient.

Description

technical field [0001] The invention relates to a processing technology of flame-retardant and radiation-proof fabric. Background technique [0002] Anti-radiation fabric refers to the color silver fiber adopting the international leading technology, fully combining silver ions with the fiber, and placing the silver in the fiber core layer; it has stronger protection ability, and at the same time is light and comfortable, soft and breathable, washable, and has Better comfort and value for money. [0003] After searching, for example, Chinese patent literature discloses a radiation-proof fabric [application number: 201410447893.4; publication number: CN 104228196A]. This anti-radiation fabric comprises a base fabric layer and a fabric layer, and is characterized in that: a radiation-proof layer is arranged between the base fabric layer and the fabric layer, the radiation-proof layer is metal fiber, and the metal fiber Arranged in a network structure. [0004] Although the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D06B1/02D06B15/00D06C7/02D06M11/44D06M11/45D06M101/06D06M101/32D06M101/04D03D15/217D03D15/258D03D15/283D03D15/47
CPCD06B1/02D06B15/00D06C7/02D06M11/44D06M11/45D06M2101/32D06M2101/04D06M2101/06D10B2101/20D10B2201/02D10B2331/04D10B2201/10D03D15/47
Inventor 薛六明
Owner HAINING TIANFU WARP KNITTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka