Solar sand-in-water and preparation method thereof

A technology of solar energy and water bag, applied in the field of paint, can solve the problem of color affecting the development of real stone paint, etc., and achieve the effect of high heat absorption efficiency and low light reflection efficiency

Inactive Publication Date: 2018-09-04
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The raw materials of various colors of water-in-sand paint can be realized by industrial production, while the color of real stone paint is completely dependent on the color of natural colored sand. At present, as natural colored sand resources become less and less, the color is extremely uncontrollable. Greatly affected the development of real stone paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of solar power generation sand-in-water, which includes protective glue, toning base paint and continuous phase mixed in equal proportions; wherein, the continuous phase contains 1 part of nano-titanium dioxide and 1 part of selenium sulfide or cadmium sulfide.

[0036] In the above scheme, the continuous phase also includes: 8 parts of deionized water, 0.5 parts of bentonite, 70 parts of silicone acrylic resin, 3 parts of 2,2,4-trimethyl-1,3-pentylene glycol Monoisobutyrate, 5 parts of propylene glycol, 0.1 part of 2-amino-2-methyl-1-propanol and 0.1 part of ACRYSOL TT-935.

[0037] In the above scheme, the toning base paint includes: 25 parts of deionized water, 0.1 part of tricresyl phosphate, 0.5 part of hydroxyethyl cellulose 250HBR, 0.1 part of the antifreeze agent, 0.1 part of FoamStarA10, 5 parts of kaolin, 0.5 parts of one or two mixtures of 2-amino-2-methyl-1-propanol and butyl ethanolamine, 10 parts of the silicone acrylic resin, 0.1 parts of wetting a...

Embodiment 2

[0048] A kind of solar power generation sand-in-water, which includes protective glue, toning base paint and continuous phase mixed in equal proportions; wherein, the continuous phase contains 5 parts of nano-titanium dioxide and 5 parts of selenium sulfide or cadmium sulfide.

[0049] In the above scheme, the continuous phase also includes: 15 parts of deionized water, 2 parts of bentonite, 90 parts of silicone acrylic resin, 10 parts of 2,2,4-trimethyl-1,3-pentylene glycol Monoisobutyrate, 10 parts of propylene glycol, 0.5 parts of butyl ethanolamine and 0.8 parts of ACRYSOL TT-935.

[0050]In the above scheme, the toning base paint includes: 40 parts of deionized water, 0.5 parts of tricresyl phosphate, 1 part of hydroxyethyl cellulose HS10W, 1 part of the propylene glycol, 0.5 parts of FoamStar A10, 10 parts of kaolin, 1.5 parts of butyl ethanolamine, 25 parts of the silicone acrylic resin, 1 part of wetting agent, 2 parts of 2,2,4-trimethyl-1,3-pentylene glycol monoisobut...

Embodiment 3

[0061] A kind of solar power generation sand-in-water, which includes protective glue, toning base paint and continuous phase mixed in equal proportions; wherein, the continuous phase contains 2 parts of nano-titanium dioxide and 3 parts of selenium sulfide or cadmium sulfide.

[0062] In the above scheme, the continuous phase also includes: 10 parts of deionized water, 1.5 parts of bentonite, 2 parts of nano-titanium dioxide, 3 parts of selenium sulfide and cadmium sulfide mixed in equal proportions, 80 parts of organic silicon acrylic resin, 7 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 8 parts of propylene glycol, 0.3 parts of 2-amino-2-methyl-1-propanol and butyl ethanolamine The mixture and 0.6 parts of ACRYSOL TT-935, wherein 2-amino-2-methyl-1-propanol and butyl ethanolamine are mixed in a mass ratio of 2:1.

[0063] In the above scheme, the toning base paint includes: 30 parts of deionized water, 0.2 parts of tricresyl phosphate, 0.8 parts of a mixture of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a solar sand-in-water, which comprises a protective adhesive, a tinting base paint and a continuous phase that are mixed in equal proportion. Specifically, the continuous phase comprises 1-5 parts of nano titanium dioxide and 1-5 parts of selenium sulfide or cadmium sulfide by mass. According to the solar sand-in-water provided by the invention, nano titanium dioxide can convert light energy into electric energy, so that the solar sand-in-water coated on the outer wall of a building can convert solar energy into electric energy, effectively utilizes the solar energy and realizes the new function of paint, and the solar sand-in-water provided by the invention has the advantages of high heat absorption efficiency and low light reflection efficiency.

Description

technical field [0001] The present invention relates generally to the field of coatings, and in particular, to solar sand-in-water and methods of making the same. Background technique [0002] With the continuous improvement of material living standards, people can no longer be satisfied with the original monochrome paint. There will be more and more stone-like and personalized designs. The sand-in-water paint with excellent decorative effects will undoubtedly become the best choice for designers and customers. good choice. [0003] Compared with the traditional real stone paint, the sand-in-water paint has better color stability than real stone paint. The raw materials of various colors of water-in-sand paint can be realized by industrial production, while the color of real stone paint is completely dependent on the color of natural colored sand. At present, as natural colored sand resources become less and less, the color is extremely uncontrollable. Greatly affected the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/32C09D7/61C09D7/63
CPCC08K2003/2241C08K2003/3009C08K2003/324C08K2201/011C09D5/32C09D133/04C09D7/61C09D7/63C08L1/284C08K13/02C08K3/22C08K3/30C08K5/103C08K3/346C08K3/32C08K3/34C08K5/523
Inventor 胡效晶戴国军胡中源董立志
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap