Preparation method of corrosion-resistant heating fabric

A technology of heating fabrics and production methods, which can be applied to fabric surface trimming, weaving, fabrics, etc., can solve the problems of corrosion-resistant, warm and breathable fabrics without production methods and low production efficiency, and achieve the effect of rapid and continuous production

Inactive Publication Date: 2018-09-25
HAINING TIANFU WARP KNITTING
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the corrosion-resistant, warm-keeping and breathable fabric disclosed in this patent is very warm to wear in winter, there is no c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of corrosion-resistant heating fabric
  • Preparation method of corrosion-resistant heating fabric

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] The following are specific embodiments of the present invention in conjunction with the accompanying drawings to further describe the technical solutions of the present invention, but the present invention is not limited to these embodiments.

[0030] The manufacturing method of the corrosion-resistant heating fabric includes the following steps: a. Knitting: interlacing warp and weft into the desired fabric, both warp and weft are blended yarn strips, and the blended yarn strips are made of polyester fiber and nylon fiber , Corn fiber and heating fiber blended; b. Preparation of finishing solution: According to weight parts, 30-45 parts of polyvinyl formal, 5-10 parts of polyurethane resin, 2-4 parts of crosslinking agent and 50-part water Put 60 parts into the blender and stir, the stirring time is 15-20min, the stirring speed is 150-200rpm, and the finishing solution is prepared; c. Padding: padding the fabric in the finishing solution, one dipping and one rolling, the l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of corrosion-resistant heating fabric. The technical problems that the existing corrosion-resistant thermal air-permeable fabric does not have a corresponding preparation method and is low in preparation efficiency are solved. The preparation method of the corrosion-resistant heating fabric comprises the following steps: a, weaving: weaving warp yarns and weft yarns in staggered way to form the needed fabric, wherein the warp yarns and the weft yarns are blended yarn strips, and the blended yarn strips are formed by blending polyester fiber, polyamide fiber, corn fiber and heating fiber; b, preparing finishing liquid: putting 30 to 45 parts by weight polyvinyl formal, 5 to 10 parts by weight of polyurethane resin, 2 to 4 parts by weight of crosslinking agent and 50 to 60 parts by weight of water into a stirring machine and stirring to prepare the finishing liquid; c, pad-rolling; pad-rolling the fabric in the finishing liquid and padding while rolling; d, drying: putting the fabric into a drying oven and drying; e, washing: putting the fabric into cold water, washing and spin-drying; and f, shaping: putting the fabric into a shaping machine and shaping. The preparation method of the corrosion-resistant heating fabric has the advantage of rapidness in preparation.

Description

technical field [0001] The invention relates to a method for manufacturing a corrosion-resistant heating fabric. Background technique [0002] During the textile dyeing and finishing process, fabrics will be exposed to water, acid, alkali, salt and other chemical substances to varying degrees. At the same time, fabrics will also be exposed to various chemicals during use, such as detergents, finishing agents, etc. Therefore, as a fabric, it must have certain chemical resistance to meet the requirements of textile dyeing and finishing processing and product use. [0003] After searching, for example, Chinese patent literature discloses a corrosion-resistant warm-keeping breathable fabric [application number: 201110334340.4; publication number: CN 102501471A]. This corrosion-resistant warm-keeping breathable fabric is characterized in that it includes: a first fabric layer, a film layer, and a second fabric layer, the film layer is placed between the first fabric layer and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D06C15/00D06M15/347D06M15/564D06M101/32D06M101/34D03D15/283D03D15/47D03D15/52
CPCD06C15/00D06M15/347D06M15/564D06M2101/04D06M2101/32D06M2101/34D10B2201/01D10B2331/02D10B2331/04D03D15/47
Inventor 薛六明
Owner HAINING TIANFU WARP KNITTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap