Making method for bionic ceramic dental prosthesis

A manufacturing method and prosthesis technology, which can be used in dental preparations, dental prostheses, dentistry, etc., can solve problems such as stress-free buffering, insufficient, excessive wear of jaw teeth, aesthetic transparency, etc., and achieve the effect of ensuring overall strength and facilitating popularization and application.

Inactive Publication Date: 2018-10-09
PEKING UNIV SCHOOL OF STOMATOLOGY
View PDF9 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the above deficiencies, the present invention provides a method for making a bionic ceramic dental restoration, which can solve the problems of excessive wear and tear on the opposing teeth of the high-strength, single-color single-layer full zirconia restoration and the problem of insufficient aesthetic transparency. The problem of no stress buffer in porcelain restoration, the problem of long-term fracture of the restoration when all bionic and wear-resistant ceramic materials are used, and the problem of interlaminar fracture of the double-layer ceramic restoration due to the difference in sintering shrinkage ratio, can be achieved in The local wear performance of the occlusal surface is bionic (synchronous with the speed of physiological wear, equal wear), and at the same time, it realizes the protection of the natural tooth root and the osseointegration interface of the implant when subjected to excessive occlusal force, and ensures high overall strength and is not easy to break. The bionic color effect of the restoration can be realized, which is conducive to popularization and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention.

[0015] A kind of manufacture method of bionic ceramic dental restoration of the present invention has the following steps:

[0016] 1), select conventional high-strength, low-transparency 3mol% yttrium-stabilized zirconia ceramics and low-strength, high-transparency ceramics as two kinds of prefabricated powders, and mix the two kinds of prefabricated powders according to the following different volume ratios: the mixing ratios are respectively 1:9, 2:8, 3:7, 4:6, 5:5, 6:4, 7:3, 8:2, 9:1 uniformly mixed powder, keep it for later use; 2), use The cold isostatic pressing equipment presses the billet block / disk in layers. The billet is divided into three layers, the upper layer is the bionic performance / color layer, the middle layer is the transition buffer layer, and the lower layer is the high-strength anti-fracture layer; 3), the trans...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a making method for a bionic ceramic dental prosthesis. The method comprises the steps that conventional 3mol% yttrium-stabilized zirconium dioxide ceramic with high strengthand low transparency and ceramic with high transparency are selected as prefabricated powder; a blank block / disc is pressed in a layered mode; in a transition buffer layer from the lower surface of ablank to the upper surface, the proportion of the 3mol% yttrium-stabilized zirconium dioxide ceramic is gradually decreased from 100% to 0, and the proportion of the ceramic with low strength and hightransparency is gradually increased from 0 to 100%; an occlusal surface or an attractive area of a CAD digital model of the dental prosthesis is placed on a bionic performance / color layer, and an axial surface area is placed on a high-strength anti-fracture layer; and making is completed by utilizing dental prosthesis manufacturing equipment. The method has the advantages that the problems that ajaw tooth is excessively worn by a high-strength single-layer full zirconia prosthesis, no stress buffer exists in the all-ceramic prosthesis implanting process, and the prosthesis is prone to beingfractured in the long time when totally adopting a bionic abrasion-resistant ceramic material can be solved, and meanwhile, the bionic color effect of the prosthesis can be achieved.

Description

technical field [0001] The invention relates to the production of a dental prosthesis, in particular to a production method of a bionic ceramic dental prosthesis. Background technique [0002] At present, zirconia has become a commonly used material for repairing tooth defects and dentition defects due to its excellent biocompatibility and bending strength. However, due to the overstrengthening of the mechanical properties of the currently used full zirconia crowns, there are problems of excessive wear on the opposing teeth during clinical use and no stress buffering during implant all-ceramic restorations. And because the color is single, it cannot meet the needs of aesthetic restoration. [0003] The invention can solve the problems of high strength, single-color single-layer full zirconia restoration on the excessive wear of the opposing teeth and insufficient aesthetic transparency, the problem of no stress buffering when implanting all-ceramic restorations, and the res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K6/02C04B35/48
CPCA61K6/802A61K6/818A61K6/82A61K6/822C04B35/48C04B2235/3201C04B2235/3217C04B2235/3225C04B2235/3244C04B2235/3272C04B2235/3418
Inventor 孙玉春周永胜王勇李榕赵一姣杨欣
Owner PEKING UNIV SCHOOL OF STOMATOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products