A gypsum material and lampshade technology, which is applied in the chemical industry, can solve problems such as single surface structure, insufficient strength, and easy peeling off of the paint layer, achieving high stability, good aesthetic effect, and improved aesthetics

Inactive Publication Date: 2018-11-06
浙江泰华集成家居科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the strength of the gypsum lampshade of a single material is insufficient, and the surface structure of the existing gypsum lampshade is single, all of which are white materials, and in order to increase its aesthetics, it is usually additionally coated with paint on its surface
However, the adhesion between the paint and the plaster material is unstable, and the paint layer is easy to fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The flashing plaster material used for lampshades is characterized by including the following components:

[0022] Component A: In proportion, it includes 105 parts of glass particles, 10 parts of limestone ore powder, and 200 parts of green gypsum;

[0023] Component B: Anhydrous sodium sulfate;

[0024] Component C: fluorogypsum;

[0025] Component D: plasticizer;

[0026] The weight ratio of the above components A:B:C:D is 900:0.3:20:1.

[0027] The plasticizer is dioctyl phthalate. According to actual conditions, it is also feasible that the plasticizer is diisodecyl phthalate.

[0028] The glass particles are colored glass.

[0029] The diameter of the glass particles is 2 mm.

[0030] The gypsum lampshade formed by the flashing gypsum material for the lampshade has uniformly distributed glass particles on its surface, and the glass particles have various colors, including red, green and blue. The multi-color mixed glass particles effectively improve the aesthetics of the gyps...

Embodiment 2

[0032] The flashing plaster material used for lampshades is characterized by including the following components:

[0033] Component A: In proportion, it includes 120 parts of glass particles, 20 parts of limestone ore powder, and 240 parts of green gypsum;

[0034] Component B: Anhydrous sodium sulfate;

[0035] Component C: fluorogypsum;

[0036] Component D: plasticizer;

[0037] The weight ratio of the above components A:B:C:D is 900:1:40:3.

[0038] The plasticizer is dioctyl phthalate. According to actual conditions, it is also feasible that the plasticizer is diisodecyl phthalate.

[0039] The glass particles are colored glass.

[0040] The diameter of the glass particles is 4 mm.

[0041] The gypsum lampshade formed by the flashing gypsum material for the lampshade has uniformly distributed glass particles on its surface, and the glass particles have various colors, including red, green and blue. The multi-color mixed glass particles effectively improve the aesthetics of the gypsum...

Embodiment 3

[0043] The flashing plaster material used for lampshades is characterized by including the following components:

[0044] Component A: In proportion, it includes 110 parts of glass particles, 15 parts of limestone ore powder, and 230 parts of green gypsum;

[0045] Component B: Anhydrous sodium sulfate;

[0046] Component C: fluorogypsum;

[0047] Component D: plasticizer;

[0048] The weight ratio of the above components A:B:C:D is 900:0.6:27:2.

[0049] The plasticizer is dioctyl phthalate. According to actual conditions, it is also feasible that the plasticizer is diisodecyl phthalate.

[0050] The glass particles are colored glass.

[0051] The diameter of the glass particles is 3 mm.

[0052] The gypsum lampshade formed by the flashing gypsum material for the lampshade has uniformly distributed glass particles on its surface, and the glass particles have various colors, including red, green and blue. The multi-color mixed glass particles effectively improve the aesthetics of the gyps...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a flash gypsum material for a lampshade, belongs to the technical field of the chemical industry and solves the problem of poor stability in the prior art. The flash gypsum material for the lampshade is prepared from components A, B, C and D, wherein the component A contains 100-120 parts of glass particles, 10-30 parts of limestone mineral powder and 200-260 parts of raw gypsum; the component B is anhydrous sodium sulfate; the component C is fluorgypsum; the component D is a plasticizer; a weight ratio of the components A, B, C and D is 900:(0.3-1):(20-40):(1-3). The flash gypsum material for the lampshade is high in stability.

Description

Technical field [0001] The invention belongs to the technical field of chemical engineering, and relates to a flashing gypsum material for lampshades. Background technique [0002] Gypsum is a monoclinic mineral, and its main chemical component is calcium sulfate (CaSO4) hydrate. Gypsum is a widely used industrial material and building material. It can be used for cement retarder, gypsum building products, model making, medical food additives, sulfuric acid production, paper filler, paint filler, etc. [0003] At the same time, because of its easy modeling and relatively low cost, it is also widely used in interior decoration. However, the existing interior decoration is mainly statues of various artistic images. [0004] Some people also use plaster lampshades. However, the strength of a single-material gypsum lampshade is insufficient. In addition, the existing gypsum lampshade has a single surface structure and is made of white material. In order to increase its aesthetics, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14F21V3/06
CPCC04B28/142F21V3/06C04B14/22C04B14/28C04B11/00C04B22/147C04B24/045
Inventor 曾光
Owner 浙江泰华集成家居科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap