A plant fiber material and plant fiber technology, applied in the field of fiber materials, can solve the problems of affecting the quality of use, poor antibacterial effect, human hazards, etc., achieve excellent antibacterial performance, improve antibacterial performance, and increase the effect of absorption

Inactive Publication Date: 2018-11-06
明光市天淼新能源科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, plant fiber fabrics have poor antibacterial effect and are prone to mold growth, which seriously affects their quality of use and is likely to cause harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of antibacterial plant fiber material, its preparation method, specifically comprises the following steps:

[0021] (1) Immerse the plant fibers in the active agent solution for 50 minutes at a temperature of 50-55°C and a pressure of 0.33-0.38Mpa to obtain activated plant fibers;

[0022] (2) Immerse the activated plant fiber in the antibacterial solution at a temperature of 68-72°C and a pressure of 0.41-0.45Mpa, and use ultrasonic vibration for 5 minutes, take it out, dry it and then impregnate it, and repeat it 5 times to get Modified plant fibers;

[0023] (3) Weave the modified plant fiber into a fabric, then immerse it in the sodium alginate solution for 30 minutes, take it out, put it into a constant temperature steam with a temperature of 122-126°C for 5 minutes, and use a temperature of 1.8-2.1°C / min Raise the temperature to 144-148°C and continue the steam treatment at constant temperature for 1 minute to obtain the product.

[0024] Further, the act...

Embodiment 2

[0032] A kind of antibacterial plant fiber material, its preparation method, specifically comprises the following steps:

[0033] (1) Immerse the plant fibers in the active agent solution for 60 minutes at a temperature of 50-55°C and a pressure of 0.33-0.38Mpa to obtain activated plant fibers;

[0034] (2) Immerse the activated plant fiber in the antibacterial solution at a temperature of 68-72°C and a pressure of 0.41-0.45Mpa, and use ultrasonic vibration for 8 minutes, take it out, dry it and then impregnate it, and repeat it 8 times to get Modified plant fibers;

[0035] (3) Weave the modified plant fiber into a fabric, then immerse it in the sodium alginate solution for 45 minutes, take it out, put it into a constant temperature steam with a temperature of 122-126°C for 8 minutes, and use a temperature of 1.8-2.1°C / min The heating rate is raised to 144-148°C and continued to be treated with constant temperature steam for 3 minutes.

[0036] Further, the active agent sol...

Embodiment 3

[0044] A kind of antibacterial plant fiber material, its preparation method, specifically comprises the following steps:

[0045] (1) Immerse the plant fibers in the active agent solution for 55 minutes at a temperature of 50-55°C and a pressure of 0.33-0.38Mpa to obtain activated plant fibers;

[0046] (2) Immerse the activated plant fiber in the antibacterial solution at a temperature of 68-72°C and a pressure of 0.41-0.45Mpa, and use ultrasonic vibration for 6 minutes, take it out, dry it and then impregnate it, and repeat it 6 times to get Modified plant fibers;

[0047] (3) Weave the modified plant fiber into a fabric, then immerse it in the sodium alginate solution for 40 minutes, take it out, put it into a constant temperature steam with a temperature of 122-126°C for 6 minutes, and use a temperature of 1.8-2.1°C / min The heating rate is raised to 144-148° C. and the constant temperature steam treatment is continued for 2 minutes, and the product is obtained.

[0048]F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial plant fiber material. A preparation method of the antibacterial plant fiber material includes the following steps: (1) immersing a plant fiber in an active agent solution at the temperature of 50-55oC and the pressure of 0.33-0.38Mpa for 50-60 minutes to obtain an activated plant fiber; (2) immersing the activated plant fiber into an antibacterial solutionat the temperature of 68-72oC and the pressure of 0.41-0.45Mpa, conducting ultrasonic vibration for 5-8 minutes, taking the fiber out for drying and then immersing the fiber again, repeating 5-8 times to obtain a modified plant fiber; (3) weaving the modified plant fiber into a fabric, then immersing the fabric in a sodium alginate solution for 30-45 minutes, taking the fabric out, placing the fabric into constant temperature steam at 122-126oC for treatment for 5-8 minutes, increasing the temperature to 144-148oC at the temperature increasing speed of 1.8-2.1oC / min, and continuing the constant temperature steam treatment for 1-3 minutes. Through experiments, the broad spectrum antibacterial rate of the antibacterial plant fiber material reaches high up to 99.3%, and the common plant fiber material in the prior art does not have the broad-spectrum antibacterial effect.

Description

technical field [0001] The invention relates to the technical field of fiber materials, in particular to an antibacterial plant fiber material. Background technique [0002] Plant fiber is a kind of thick-walled tissue widely distributed in seed plants. Its cells are slender, sharp at both ends, have thicker secondary walls, often have single pits on the walls, and generally have no living protoplasts when mature. Plant fibers mainly play a role in mechanical support in plants. Plant fibers processed into towel-like fabrics are highly water-absorbent. This towel can absorb water quickly after washing the hair, making the hair dry quickly, and it is very durable for repeated use. [0003] Plant fiber fabrics use pure natural plant fibers as the basic raw materials, remove the sugar and fat in the plant fibers through special technology and production technology, and use advanced technology to eradicate the electrostatic reaction of substances to produce knitwear. There is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/13D06M13/00D06M13/144D06M13/148D06M13/224D06M13/256D06M15/333D06M101/06
CPCD06M13/00D06M13/144D06M13/148D06M13/224D06M13/256D06M15/13D06M15/333D06M16/00D06M2101/06
Inventor 卫武
Owner 明光市天淼新能源科技有限公司