Gold alloy with excellent elastic performance and for 18K gold

An elastic performance, 18K technology, applied in the field of gold alloys, can solve problems such as lack of progress, and achieve the effect of solving the problem of large hot cracking tendency, hindering dendrite growth and low production cost

Inactive Publication Date: 2018-11-13
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Regrettably, however, no substant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A gold alloy for 18K gold with excellent elastic properties. By weight percentage, the composition of the alloy is: Sr: 0.8wt.%, Ge: 1.0wt.%, Ho: 0.2wt.%, Pr: 0.2wt.%, V: 0.3wt.%, S: 0.1wt.%. %, Ag: 8.0wt.%, Au: 74.0wt.%, and the balance is platinum.

[0019] The above-mentioned preparation method of 18K gold alloy with excellent elastic properties comprises the following steps: adding the raw materials proportioned as above into an argon-protected induction furnace, and using a graphite crucible; after the metal is melted, a low-flow argon is used. Gas protection to avoid serious burning of alloy elements due to large air flow; heat preservation at 1150 degrees for 10 minutes during smelting, and uniform electromagnetic stirring by high-frequency induction furnace; 100-200mm steel mold, and use water cooling to cool down. The obtained ingot is rolled at room temperature, and the rolling reduction per pass is 30-40%; the intermediate annealing temperature is 680 degre...

Embodiment 2

[0022] A gold alloy for 18K gold with excellent elastic properties. By weight percentage, the composition of the alloy is: Sr: 1.0wt.%, Ge: 1.2wt.%, Ho: 0.3wt.%, Pr: 0.4wt.%, V: 0.5wt.%, S: 0.3wt.%. %, Ag: 10.0wt.%, Au: 76.0wt.%, and the balance is platinum. The above-mentioned preparation method of 18K gold alloy with excellent elastic properties comprises the following steps: adding the raw materials proportioned as above into an argon-protected induction furnace, and using a graphite crucible; after the metal is melted, a low-flow argon is used. Gas protection to avoid serious burning of alloy elements due to large air flow; heat preservation at 1150 degrees for 10 minutes during smelting, and uniform electromagnetic stirring by high-frequency induction furnace; 100-200mm steel mold, and use water cooling to cool down. The obtained ingot is rolled at room temperature, and the rolling reduction per pass is 30-40%; the intermediate annealing temperature is 680 degrees after...

Embodiment 3

[0025] A gold alloy for 18K gold with excellent elastic properties. According to the weight percentage, the composition of the alloy is: Sr: 0.9wt.%, Ge: 1.1wt.%, Ho: 0.2wt.%, Pr: 0.3wt.%, V: 0.4wt.%, S: 0.2wt. %, Ag: 9.0wt.%, Au: 75.0wt.%, and the balance is platinum. The above-mentioned preparation method of 18K gold alloy with excellent elastic properties comprises the following steps: adding the raw materials proportioned as above into an argon-protected induction furnace, and using a graphite crucible; after the metal is melted, a low-flow argon is used. Gas protection to avoid serious burning of alloy elements due to large air flow; heat preservation at 1150 degrees for 10 minutes during smelting, and uniform electromagnetic stirring by high-frequency induction furnace; 100-200mm steel mold, and use water cooling to cool down. The obtained ingot is rolled at room temperature, and the rolling reduction per pass is 30-40%; the intermediate annealing temperature is 680 de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a gold alloy with excellent elastic performance and for 18K gold. The alloy comprises the following components in percentage by weight: 0.8wt.%-1.0wt.% of Sr, 1.0wt.%-1.2wt.% of Ge, 0.2wt.%-0.3wt.% of Ho, 0.2wt.%-0.4wt.% of Pr, 0.3wt.%-0.5wt.% of V, 0.1wt.%-0.3wt.% of S, 8.0wt.%-10.0wt.% of Ag, 74.0wt.%-76.0wt.% of Au and the balance platinum. According to the alloy, the current situations of low elasticity and lagged technology of a present 18K gold material are improved. Through an advanced material design, the phenomenon of brittle failure of the alloy after being used at a low temperature is solved while the elastic performance of 18K gold is greatly improved. Implementation and industrialization for the material are predicted to achieve rich economic gain and social benefits.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a gold alloy. Background technique [0002] Gold is a precious metal and one of the earliest metals discovered and exploited by human beings. It is an important raw material for making jewelry and coins, and an important reserve material for the country. It is known as the king of metals. It is not only regarded as a symbol of beauty and wealth, but also benefits human life with its unique value. An important area of ​​application for gold is decorative materials, including jewelry. Gold can also be used for daily necessities, such as gold-plated clocks, belt buckles, lighters, pens, etc. The watch kingdom of Switzerland is not a big country, but its jewelry industry uses about 40 tons of gold every year, of which 95% is used in the watchmaking industry. A single watch factory in Japan consumes 1 ton of gold salt a year, which is equivalent to 680 kilograms of gold. Gold is u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C5/02C22C1/02C22F1/14
CPCC22C5/02C22C1/02C22F1/14
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap