A wide-width thin-walled 6-series aluminum alloy profile for high-speed EMUs and its preparation method

A technology for high-speed EMUs and aluminum alloy profiles, which is applied to the 6-series aluminum alloy profiles for wide-width thin-walled skirts of high-speed EMUs and their preparation fields, can solve the problems of inability to form extrusion and low production efficiency.

Active Publication Date: 2020-07-28
中铝特种铝材(重庆)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of this, the present invention solves the problems that extrusion cannot be formed and the production efficiency is low in the process of preparing aluminum alloy profiles for high-speed EMU skirts with a width-to-thickness ratio greater than 500 in the prior art. The present invention provides a high-speed EMU Wide and thin-walled 6-series aluminum alloy profile and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A wide-width thin-walled 6-series aluminum alloy profile for high-speed EMUs and its preparation method
  • A wide-width thin-walled 6-series aluminum alloy profile for high-speed EMUs and its preparation method
  • A wide-width thin-walled 6-series aluminum alloy profile for high-speed EMUs and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Such as figure 1 Shown is a method for preparing a wide-width thin-walled 6-series aluminum alloy profile for a high-speed EMU, comprising the following steps:

[0044] A. Ingredients: Calculate the amount of each aluminum alloy raw material and prepare the aluminum alloy raw material according to the ratio. The ratio of the mass percentage of each element of the aluminum alloy raw material is as follows:

[0045] element Si Fe Cu mn Mg Cr Zn Ti Impurities Al content 0.65 0.25 0.10 0.1 0.45 0.05 0.05 0.10 0.15 margin

[0046] B. Casting: Put the prepared aluminum alloy raw materials into the smelting furnace and evenly mix them to melt them into liquid aluminum alloys. The aluminum alloy is melted and cast into aluminum alloy cast rods. The diameter range of the aluminum alloy cast rods is 457±5mm and the length is 6m. A1-5Ti-B wire refining agent is added during the refining process. The online degassing adopts double ro...

Embodiment 2

[0057] The difference between Example 2 and Example 1 is that in step E, the temperature at the head end of the short aluminum alloy ingot is controlled at 440°C, the temperature at the tail end is controlled at 380°C, and the extrusion speed of the 6N01 aluminum alloy thin-walled profile in step F is 9m / min.

[0058] The wide-width thin-walled skirt plate aluminum alloy profiles for high-speed EMUs prepared in Example 2 have a width of 640 mm and a wall thickness of 1.2 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of preparation of aluminum alloy sections, and relates to a wide-range thin-wall series-6 aluminum alloy section for a high speed train and a preparation method of the wide-range thin-wall series-6 aluminum alloy section. Aluminum alloy comprises the following elements in percentages by weight: 0.50-0.65% of Si, less than or equal to 0.25% of Fe, less than or equal to 0.10% of Cu, 0.03-0.15% of Mn, 0.45-0.55% of Mg, less than or equal to 0.05% of Cr, less than or equal to 0.05% of Zn, less than or equal to 0.10% of Ti, less than or equal to 0.05% ofa single impurity, less than or equal to 0.15% of total impurities and the balance of Al. Deformation resistance and friction resistance in an extruding process are reduced by reasonably controllingthe temperature relationship of an ingot casting, an extrusion barrel and a die, the extruding speed is increased to be 8-13 m / min, the quenching temperature of the product is ensured, thus, any coarse grain rings are not generated when a thin-walled apron board is extruded at high speed, after being subjected to on-line quenching, the product is directly subjected to artificial ageing at the temperature of 175+ / - 5 DEG C for 4-8 hours, the mechanical property of the product can meet requirements in TB / T.3260.4-2011 TO 1.2 mm thin-walled sections, the actual tensile strength reaches 250-270 MPa, the yield strength reaches 210-230 MPa, the specific elongation is 8-10%, and the grade of the grain size of an aluminum section microscopic structure reaches and even exceeds 4.

Description

technical field [0001] The invention belongs to the technical field of preparation of aluminum alloy profiles, and relates to a wide-width thin-walled 6-series aluminum alloy profile for high-speed EMUs and a preparation method thereof, in particular to a 6-series aluminum for high-speed EMUs wide-width thin-walled skirt boards Alloy profile and its preparation method. Background technique [0002] Most of the key equipment of the high-speed EMU is hoisted under the car body, in order to avoid the unexpected situation of high-speed impact of stones, ice or other objects on the equipment under the train, and at the same time to reduce air resistance, protect and repair the equipment under the train, and ensure high-speed For the safe operation of EMUs, skirts with diversion, protection and maintenance functions must be installed under high-speed EMUs. The apron is generally made of 6N01 aluminum alloy extruded profiles. The 6N01 series aluminum alloy has the advantages of lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C21/08C22C1/06C22F1/043C22F1/047C22F1/05
CPCC22C1/06C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
Inventor 吴博李洪涛
Owner 中铝特种铝材(重庆)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More