Internalization charging method of power type lead-acid battery

A technology of lead-acid battery and charging method, which is applied in the direction of lead-acid battery, lead-acid battery construction, sustainable manufacturing/processing, etc., which can solve problems such as temperature rise, affecting battery performance, and low conversion efficiency of battery charging power, achieving The effect of reducing the production cycle, optimizing the formation performance, and shortening the battery formation time

Active Publication Date: 2020-08-21
ZIBO TORCH ENERGY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many problems in the process of internal formation of lead-acid batteries, mainly including the following problems: the battery formation process takes too long, which delays the production efficiency of the battery; The conversion of substances, excess electricity will lead to a large amount of outgassing in the battery and the temperature rise in the final stage of battery formation. The erosion of bubbles and high temperature will damage the structure of active materials and affect battery performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] With a density of 1.050g / cm 3 Sulfuric acid electrolyte for tank acid and soak for 1h.

[0031] (1) The first stage: use 0.05C 5 Charging 0.5h;

[0032] (2) The second stage: use 0.16C 5 Charging 0.5h;

[0033] (3) The third stage: use 0.20C 5 Charge for 1h;

[0034] (4) The fourth stage: use 0.30C 5 Charge for 1h;

[0035] (5) The fifth stage: use 0.45C 5 Charge for 7 hours;

[0036] (6) The sixth stage: use 0.35C 5 Charge for 3 hours;

[0037] (7) The seventh stage: use 0.28C 5 Charge for 2 hours;

[0038] (8) The eighth stage: use 0.10C 5 Discharge for 1h;

[0039] (9) The ninth stage: use 0.25C 5 Charge for 3 hours;

[0040] (10) The tenth stage: use 0.20C 5 Charge for 5h.

[0041] Among them: the temperature of the first stage to the fifth stage is controlled at 50°C, the temperature of the subsequent stage is controlled below 50°C, and the electrolyte density of the first stage to the eighth stage is 1.060g / cm 3 , the density of the sulfuric aci...

Embodiment 2

[0043] With a density of 1.050g / cm 3 Sulfuric acid electrolyte for tank acid and soak for 1h.

[0044] (1) The first stage: use 0.1C 5 Charge for 1h;

[0045] (2) The second stage: use 0.2C 5 Charge for 1h;

[0046] (3) The third stage: use 0.25C 5 Charge for 2 hours;

[0047] (4) The fourth stage: use 0.35C 5 Charge for 2 hours;

[0048] (5) The fifth stage: use 0.50C 5 Charging for 6 hours;

[0049] (6) The sixth stage: use 0.40C 5 Charge for 2 hours;

[0050] (7) The seventh stage: use 0.30C 5 Charge for 1h;

[0051] (8) The eighth stage: use 0.15C 5 Discharge 2h;

[0052] (9) The ninth stage: use 0.20C 5 Charge for 3 hours;

[0053] (10) The tenth stage: use 0.25C 5 Charge for 4h.

[0054] Among them: the temperature of the first stage to the fifth stage is controlled at 55°C, the temperature of the subsequent stage is controlled below 50°C, and the electrolyte density of the first stage to the eighth stage is 1.060g / cm 3 , the density of the sulfuric ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an internalization charging method for a power type lead-acid battery, belonging to the technical field of power type lead-acid battery charging. The internalization charging method described in the present invention performs segmental processing according to the principle of the formation process, adopts different internalization charging methods for different charging stages, and solves the problem of long time in the existing internalization charging process and the conversion efficiency of battery charging power Low, low battery production efficiency and other issues. The charging method of the present invention significantly reduces the production cycle, shortens the formation time of the battery, achieves the best formation performance of the pole plate, and obtains the effect of rapid formation; by adopting an appropriate formation system, the formation performance of the pole plate is optimal; by adopting a suitable The formation temperature accelerates the conversion of active materials inside the battery, thereby shortening the formation time.

Description

technical field [0001] The invention relates to an internalization charging method for a power type lead-acid battery, belonging to the technical field of power type lead-acid battery charging. Background technique [0002] At present, the charging method of internal formation has been promoted and used in the domestic market. Compared with the traditional charging method, internal formation of acid cycle can effectively save battery formation time and production efficiency. With the continuous improvement of market demand and charging requirements, how to reduce the production cycle, shorten the battery formation time, and improve the battery formation effect has become the main problem to be solved by internal formation batteries at this stage. [0003] At present, there are many problems in the process of internal formation of lead-acid batteries, mainly including the following problems: the battery formation process takes too long, which delays the production efficiency ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/12
CPCH01M10/12Y02E60/10Y02P70/50
Inventor 王刚吴涛战祥连邓永超田雪李云福
Owner ZIBO TORCH ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com