High-strength heat-resistant cable jacket material and preparation method thereof

A cable sheath, high-strength technology, used in rubber insulators, organic insulators, etc., can solve problems such as insufficient heat resistance and strength, and achieve the effect of improving mechanical strength, excellent heat resistance, and ensuring vulcanization effect.

Inactive Publication Date: 2018-12-07
HEFEI ZHENXUN LOW TEMPERATURE TECH CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cable sheath material of this invention simply uses EPDM rubber, which has problems of insufficient heat resistance and strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength heat-resistant cable jacket material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The high-strength heat-resistant cable sheath material of this embodiment is made of the following raw materials in parts by weight: 40 parts of nitrile rubber, 15 parts of EPDM rubber, 10 parts of chlorosulfonated polyethylene, 2 parts of vulcanizing agent, two 10 parts of tetramethylthiuram sulfide, 5 parts of benzoyl peroxide, 3 parts of ethylene-vinyl acetate copolymer, 2 parts of zinc stearate, 3 parts of active zinc oxide, N, N'-m-phenylene bis-hormone 2 parts of imide, 1 part of highly dispersed white carbon black, 2 parts of modified sepiolite powder, 3 parts of nano silicon dioxide, 0.5 parts of hydroxyl silicone oil, 3 parts of calcined metakaolin powder, 2 parts of modified phenolic resin, three parts 1 part of antimony oxide, 3 parts of magnesium hydroxide, 0.5 part of accelerator, 0.4 part of antioxidant, and 0.3 part of plasticizer.

[0032] Wherein, the vulcanizing agent is a mixture of sulfur, vulcanizing agent DCP and auxiliary vulcanizing agent TAIC in...

Embodiment 2

[0046] The high-strength heat-resistant cable sheath material of this embodiment is made of the following raw materials in parts by weight: 60 parts of nitrile rubber, 30 parts of EPDM rubber, 20 parts of chlorosulfonated polyethylene, 5 parts of vulcanizing agent, 20 parts of tetramethylthiuram sulfide, 10 parts of benzoyl peroxide, 6 parts of ethylene-vinyl acetate copolymer, 4 parts of zinc stearate, 8 parts of active zinc oxide, N, N'-m-phenylene bis-hormone 5 parts of imide, 3 parts of highly dispersed white carbon black, 4 parts of modified sepiolite powder, 5 parts of nano silicon dioxide, 1 part of hydroxyl silicone oil, 5 parts of calcined metakaolin powder, 4 parts of modified phenolic resin, three parts 3 parts of antimony oxide, 6 parts of magnesium hydroxide, 1.5 parts of accelerator, 00.8 parts of anti-aging agent, and 0.7 parts of plasticizer.

[0047] Wherein, the vulcanizing agent is a mixture of sulfur, vulcanizing agent DCP and auxiliary vulcanizing agent TA...

Embodiment 3

[0061] The high-strength heat-resistant cable sheath material of this embodiment is made of the following raw materials in parts by weight: 50 parts of nitrile rubber, 22 parts of EPDM rubber, 15 parts of chlorosulfonated polyethylene, 3.5 parts of vulcanizing agent, two 15 parts of tetramethylthiuram sulfide, 7.5 parts of benzoyl peroxide, 4.5 parts of ethylene-vinyl acetate copolymer, 3 parts of zinc stearate, 5.5 parts of active zinc oxide, N, N'-m-phenylene bis-hormone 3.5 parts of imide, 2 parts of highly dispersed white carbon black, 3 parts of modified sepiolite powder, 4 parts of nano-silica, 0.7 parts of hydroxyl silicone oil, 4 parts of calcined metakaolin powder, 3 parts of modified phenolic resin, three parts 2 parts of antimony oxide, 4.5 parts of magnesium hydroxide, 1 part of accelerator, 0.6 part of antioxidant, and 0.5 part of plasticizer.

[0062] Wherein, the vulcanizing agent is a mixture of sulfur, vulcanizing agent DCP and auxiliary vulcanizing agent TAIC...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-strength heat-resistant cable jacket material and a preparation method thereof and belongs to the technical field of cable jacket materials. The high-strength heat-resistant cable jacket material is prepared from the following raw materials: nitrile rubber, EPDM, chlorosulfonated polyethylene, a vulcanizing agent, tetramethyl thiuram disulfide, benzoyl peroxide, an ethylene-vinyl acetate copolymer, zinc stearate, activated zinc oxide, N,N'-m-phenylene bismaleimide, highly dispersed white carbon black, modified sepiolite powder, nano silicon dioxide, hydroxyl silicone oil, calcined metakaolin powder, modified phenolic resin, antimonous oxide, magnesium hydroxide, an accelerant, an anti-aging agent and a plasticizer. The cable jacket material is high in strength, good in heat resistance, ageing-resistant and long in service life.

Description

technical field [0001] The invention relates to the technical field of cable sheathing materials, in particular to a high-strength heat-resistant cable sheathing material and a preparation method thereof. Background technique [0002] The cable sheath is an indispensable intermediate structural part of the cable, which plays the role of protecting the cable, ensuring the safety of the cable, and isolating the copper wire from water, air and other media to avoid leakage. PVC sheath is widely used in cable sheathing due to its soft texture, corrosion resistance, corrosion resistance, flame retardant, good oil resistance, and low price. However, the current ordinary PVC sheath has poor heat resistance, so its service life is short, and it is not suitable for use in harsh environments. [0003] After searching the existing technology, a Chinese patent (application number: 201210283037.0) discloses a formula for a composite wire and cable sheath material, including polystyrene, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L23/16C08L23/34C08L23/08C08L83/04C08L61/14C08K13/06C08K9/04C08K3/34C08K5/40C08K5/098C08K3/22C08K3/36H01B3/28
Inventor 周青松
Owner HEFEI ZHENXUN LOW TEMPERATURE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap