High-thermal-conductivity cast aluminum alloy

A casting aluminum alloy, high thermal conductivity technology, applied in the field of alloys, can solve the problems of not meeting the heat dissipation requirements of electronic products, low thermal conductivity, etc., achieve good thermal conductivity, improve tensile strength and hardness, high corrosion resistance and The effect of abrasion resistance

Pending Publication Date: 2018-12-07
SHENZHEN XINMAOXIN IND CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thermal conductivity of this alloy is low, only 90W / m·K, which cannot meet the heat dissipation requirements of existing electronic products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-thermal-conductivity cast aluminum alloy
  • High-thermal-conductivity cast aluminum alloy
  • High-thermal-conductivity cast aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high thermal conductivity cast aluminum alloy, by weight percentage, the composition of the aluminum alloy is:

[0022]

[0023]

[0024] According to the above component distribution ratio, the sample is prepared, and then the induction heating furnace is used for melting, the pure aluminum is melted first, and then the intermediate alloy is added. , the cast aluminum alloy was produced.

Embodiment 2

[0026] A high thermal conductivity cast aluminum alloy, by weight percentage, the composition of the aluminum alloy is:

[0027]

[0028] According to the above component distribution ratio, the sample is prepared, and then the induction heating furnace is used for melting, the pure aluminum is melted first, and then the intermediate alloy is added. , the cast aluminum alloy was produced.

Embodiment 3

[0030] A high thermal conductivity cast aluminum alloy, by weight percentage, the composition of the aluminum alloy is:

[0031]

[0032] According to the above component distribution ratio, the sample is prepared, and then the induction heating furnace is used for melting, the pure aluminum is melted first, and then the intermediate alloy is added. , the cast aluminum alloy was produced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-thermal-conductivity cast aluminum alloy. The aluminum alloy comprises the following components in percentage by weight: 10%-12% of silicon, 0.1%-1% of copper, 0.3%-1% of iron, 0.1%-0.6% of manganese, 0.2%-0.6% of magnesian and the balance aluminum, wherein impurity metals with a total amount of less than 0.2% are further allowed to exist in the alloy. The aluminum alloy is excellent in casting performance and thermal conduction characteristic, and the thermal conductivity can reach 140W / m.K and above.

Description

Technical field: [0001] The invention relates to the field of alloys, in particular to a cast aluminum alloy with high thermal conductivity. Background technique: [0002] Aluminum alloy has good processing performance, especially hypoeutectic aluminum-silicon alloy, which not only has good processing performance, but also has light specific gravity, beautiful surface and corrosion resistance, good casting performance, good comprehensive mechanical properties of products, and the strength can be greatly improved after heat treatment. Excellent cast aluminum alloys can be used for various parts with complex shapes and are widely used in many fields. As electronic products become thinner, lighter and more functional, the requirements for heat dissipation are increased. Therefore, cast aluminum alloys with high thermal conductivity have important application prospects. [0003] Since electronic products usually require complex and precise structural parts, die-casting alloys h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/02C22C1/03
CPCC22C1/026C22C1/03C22C21/02
Inventor 刘秋华
Owner SHENZHEN XINMAOXIN IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products