A kind of preparation method of badminton head

A badminton and ball head technology, applied in the field of badminton, can solve the problems of increased production cost, easy separation of the front half and the back half, and easy cracking of the ball head when punching holes, etc. strong effect

Active Publication Date: 2021-03-02
安徽太阳体育用品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Therefore, at present, the materials of the front half and the back half of the badminton head are different, and glue must be used to fix the connection during processing. The problem caused by this is that the front half and the back half are easy to separate. The surface of the part and the second half is covered with a layer of sheepskin or other materials, which increases the production cost, and is prone to cracks at the hole of the ball head

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing a badminton ball head, comprising the following steps:

[0027] (1) Preheat the ball head mold, the heating temperature is 200°C, keep it warm for 10 minutes, then lower the temperature to 120°C, keep it warm for 15 minutes, and then use cold water below 5°C to lower the arc part of the bottom of the mold by 10°C;

[0028] (2) Smear a layer of m-xylene on the arc part of the bottom of the ball head mold, inject the ball head raw material into the ball head mold, compress it with a compacting block, and keep it warm for 3 hours to obtain a ball head semi-finished product;

[0029] (3) Heat up the mold with the ball head semi-finished product to 220°C, keep it warm for 8 minutes, cool it down to room temperature quickly, let it stand for 2 minutes, and take out the ball head semi-finished product;

[0030] (4) cut flat the end face of the half-finished ball head, polish it, evenly punch holes, and coat a layer of viscose around the top of the hole. ...

Embodiment 2

[0032] A method for preparing a badminton ball head, comprising the following steps:

[0033] (1) Preheat the ball head mold, the heating temperature is 250°C, keep it warm for 15 minutes, then lower the temperature to 160°C, keep it warm for 20 minutes, and then use cold water below 5°C to lower the arc part of the bottom of the mold by 10°C;

[0034] (2) Smear a layer of m-xylene on the arc part of the bottom of the ball mold, inject the ball raw material into the ball mold, compress it with a compacting block, keep it warm for 3.5h, and make the semi-finished ball;

[0035] (3) Heat up the mold with the ball head semi-finished product to 260°C, keep it warm for 10 minutes, cool it down to room temperature quickly, let it stand for 3 minutes, and take out the ball head semi-finished product;

[0036] (4) cut flat the end face of the half-finished ball head, polish it, evenly punch holes, and coat a layer of viscose around the top of the hole. The thickness of the viscose is ...

Embodiment 3

[0039] A method for preparing a badminton ball head, comprising the following steps:

[0040] (1) Preheat the ball head mold, the heating temperature is 220°C, keep it warm for 12 minutes, then lower the temperature to 140°C, keep it warm for 18 minutes, and then use cold water below 5°C to lower the arc part of the bottom of the mold by 10°C;

[0041] (2) Smear a layer of m-xylene on the arc part of the bottom of the ball head mold, inject the ball head raw material into the ball head mold, compress it with a compacting block, and keep it warm for 3 hours to obtain a ball head semi-finished product;

[0042] (3) Heat up the mold with the ball head semi-finished product to 240°C, keep it warm for 9 minutes, cool it down to room temperature quickly, let it stand for 2 minutes, and take out the ball head semi-finished product;

[0043] (4) cut flat the end face of the half-finished ball head, polish it, evenly punch holes, and coat a layer of viscose around the top of the hole. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a badminton head, and relates to the field of badminton. The preparation method of the badminton head comprises the steps that (1) a badminton head moldis preheated with heating temperature of 200-250 DEG C and heat preservation for 10-15min; and then the heating temperature is cooled to 120-160 DEG C, heat preservation is carried out for 15-20 min,and the temperature of the arc part at the bottom of a mold is reduced by 10 DEG C by using cold water below 5 DEG C; (2) the arc part at the bottom of the badminton head mold is coated with a layerof m-xylene, badminton head raw materials are injected into the badminton head mold, the badminton head raw materials are compressed with a compaction block, and heat preservation is carried out for 3-3.5h to obtain a semi-finished badminton head product; (3) the temperature of the mold with the semi-finished badminton head product is increased to 220-260 DEG C, heat preservation is carried out for 8-10 min, the mold is quickly cooled to room temperature with standing of 2-3 min, the semi-finished badminton head product is taken out; (4) the end surface of the semi-finished badminton head product is cut flat, polished and evenly perforated, and the periphery of the top end of a hole is coated with a layer of adhesive, thickness of the adhesive is 0.2-0.3 mm, and the badminton head is obtained. By adopting a mold forming method, the material of the prepared badminton head has uniform components, good integrity and is not prone to being damaged.

Description

Technical field: [0001] The invention relates to the field of badminton, in particular to a method for preparing a badminton head. Background technique: [0002] Badminton ball heads are mainly divided into four categories: foam ball heads, double ball heads, triple ball heads, and all-natural cork ball heads. The foam ball head is a white foam. The double ball head is the most common. It is usually a double fight small particle regenerated cork ball head. Cork, to achieve the strength of natural cork, the second half is table fiber, generally expressed as: "Small particles of regenerated cork double ball head, XXmm table fiber", XX represents the thickness of table fiber, there are double ball heads It is a pair of cork, the first half is natural cork, and the second half is table fiber, generally expressed as: "Natural cork double ball head, XXmm table fiber", XX represents the thickness of table fiber, and the triple ball head is generally natural cork + Taiwan fiber + ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C69/00C09J161/14C09J11/06C09J11/08C08L75/04C08L63/00C08L97/02C08L53/02B29K75/00A63B67/187B29L31/54
CPCA63B67/187B29C69/001B29K2075/00B29L2031/54C08L75/04C08L2205/035C08L2205/16C09J11/06C09J11/08C09J161/14C08L5/00C08L29/14C08L45/00C08L1/286C08L5/04C08K13/02C08K5/13C08K5/098C08L63/00C08L97/02C08L53/02
Inventor 沈在国
Owner 安徽太阳体育用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products