High temperature-resistant high strength stainless steel plate for hearth plate and production method

A technology of stainless steel plate and production method, which is applied in the field of special steel, can solve the problems of not being able to fundamentally guarantee the high-level mechanical properties of the heat-resistant stainless steel furnace bottom plate, increasing the direct cost and time cost of production, and the difficulty of large-scale promotion. , to achieve the effect of reducing the tendency of crack formation, improving creep resistance and durability, and reducing the content of harmful inclusions

Inactive Publication Date: 2018-12-18
武汉钢铁有限公司
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the several patents mentioned above, it is mentioned that the composition system of the furnace floor based on the addition of alloy elements or rare elements does not change much in the process, but the plan of using composite materials and changing the internal and external str

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High temperature-resistant high strength stainless steel plate for hearth plate and production method
  • High temperature-resistant high strength stainless steel plate for hearth plate and production method
  • High temperature-resistant high strength stainless steel plate for hearth plate and production method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] A stainless steel plate for high-temperature and high-strength furnace bottom plate. The production process includes: smelting by using a combined blowing method of electric furnace + oxygen lance oxygen blowing, adding lime, fluorite and dephosphorization agent to perform deep P removal, and the tapping temperature is at 1655°C. Afterwards, the LF furnace is used for refining, various alloys are added in the LF furnace, alloy adjustment is carried out, lime and fluorite are added, and S is deep removed; Al powder is added for deoxidation; the whole process of the LF furnace is nitrogen increased by bottom blowing nitrogen. In the VD station, a high vacuum of 670Pa is used for 20 minutes. After the vacuum is broken, FeTi and carbonized rice husks are added and soft blown for 10 minutes (Ar:N controlled at 2:1), and then die-casting. After the steel ingot is demoulded and slowly cooled, it is annealed, the cap and the bottom of the ingot are sawn off, th...

Example Embodiment

[0033] Example 2

[0034] A stainless steel plate for high-temperature and high-strength furnace bottom plate. The production process includes: smelting by using a combined blowing method of electric furnace + oxygen lance oxygen blowing, adding lime, fluorite and dephosphorization agent to perform deep P removal, and the tapping temperature is at 1671°C. Afterwards, the LF furnace is used for refining, various alloys are added in the LF furnace, alloy adjustment is carried out, lime and fluorite are added, and S is deep removed; Al powder is added for deoxidation; the whole process of the LF furnace is nitrogen increased by bottom blowing nitrogen. In the VD station, a high vacuum of 1330Pa is used for 20 minutes. After the vacuum is broken, FeTi and carbonized rice husks are added and soft blown for 10 minutes (Ar:N controlled at 2:1), and then die-casting. After the steel ingot is demoulded and slowly cooled, it is annealed, the cap and the bottom of the ingot are sawn off, t...

Example Embodiment

[0035] Example 3

[0036] A stainless steel plate for high-temperature and high-strength furnace bottom plate. The production process includes: smelting by using a combined blowing method of electric furnace + oxygen lance oxygen blowing, adding lime, fluorite and dephosphorization agent to perform deep P removal, and the tapping temperature is at 1681°C. Afterwards, the LF furnace is used for refining, various alloys are added in the LF furnace, alloy adjustment is carried out, lime and fluorite are added, and S is deep removed; Al powder is added for deoxidation; the whole process of the LF furnace is nitrogen increased by bottom blowing nitrogen. In the VD station, a high vacuum of 3350Pa is used for 20 minutes. After the vacuum is broken, FeTi and carbonized rice husks are added and soft blown for 10 minutes (Ar:N controlled at 1:1), and then die-casting. After the steel ingot is demoulded and slowly cooled, it is annealed, the cap and the bottom of the ingot are sawn off, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high temperature-resistant high strength stainless steel plate for a hearth plate and a production method thereof. The strength stainless steel plate for a hearth plate hasthe yield strength being greater than or equal to 30 MPa under the high temperature of 1200 DEG C, and comprises the following components in weight percent: 0.05-0.08% of C; 0.40-0.80% of Si; 1.00-1.60% of Mn; less than or equal to 0.010% of P; less than or equal to 0.010% of S; 0.02-0.09% of N; 10.0-12.0% of Ni; 22.00-24% of Cr; 0.10-0.50% of Mo; 0.02-0.05% of Nb; 0.040-0.090% of V; 0.01-0.04% ofTi; and the balance Fe and inevitable impurities. According to the invention, improvements are made from the component and the production method, the high-temperature strength of the hearth plate isimproved, and the service life of the hearth plate is prolonged.

Description

technical field [0001] The invention belongs to the technical field of special steel, and in particular relates to a stainless steel plate for a high-temperature-resistant high-strength furnace floor and a production method. Background technique [0002] With the rapid development of my country's silicon steel project, the domestic production of cold-rolled oriented silicon steel has reached 1.2 million tons. Annular annealing furnace (ROF furnace) is a new annealing furnace developed on the basis of oriented silicon steel tunnel annealing furnace technology. The application of ROF furnace can greatly reduce energy consumption, improve productivity, and the length of the plant can be greatly shortened. The annual capacity of each ROF furnace is about 80,000 tons. The furnace bottom plate is used to carry heat-treated steel coils in the ROF furnace for high-temperature annealing. It is a high-consumption part. The working diagram of the furnace bottom plate is shown in figu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D8/02C22C38/02C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58C21C7/072
CPCC21C7/072C21D8/0221C22C38/001C22C38/002C22C38/02C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50C22C38/58
Inventor 周千学杨治争官计生朱丛茂罗毅李德发严翔熊玉章付勇涛
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap