Holocellulose composite material and preparation method thereof

A composite material and whole cellulose technology, which is applied in the field of full cellulose composite materials and its preparation, can solve the problems of not being suitable for bioplastic products and lack of thermoplasticity, and achieve the effect of improving mechanical properties and interfacial compatibility

Active Publication Date: 2018-12-21
JIAXING UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method is limited to cellulose and is limited to the preparation of whole cellulose films by partial dissolution method, which is not thermoplastic and not suitable for industrial production of bioplastic products by thermal processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Holocellulose composite material and preparation method thereof
  • Holocellulose composite material and preparation method thereof
  • Holocellulose composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In order to illustrate the content of the present invention more clearly, specific examples are used to illustrate the following, and the specific examples do not limit the scope of the content of the present invention.

[0020] Because the mechanical properties of this cellulose composite mainly depend on the degree of acetylation substitution, crystal structure, morphology and so on of the added cellulose. Focus on optimizing the preparation process of acetylated cellulose, and adjust the degree of substitution of acetylation of cellulose and the crystallinity of cellulose itself by controlling the time for the preparation of acetylated cellulose catalyzed by iodine, so that cellulose acetate can be improved with acetic acid through acetylation The compatibility of cellulose can ensure sufficient mechanical strength. Finally, the mechanical properties of thermoplastic cellulose are significantly improved.

[0021] Preparation of semi-crystalline acetylated derivative...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of acetylationaaaaaaaaaa
crystallinityaaaaaaaaaa
crystallinityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a holocellulose composite material and a preparation method thereof. Cellulose with the acetylated surface layer is prepared by adopting iodine catalysis and is adopted as a mechanical-enhancement filler fiber, and the surface of cellulosic fiber is gradually acetylated under iodine catalysis. Through the acetylation treatment of the cellulosic fiber, the compatibility ofthe cellulosic fiber and cellulose acetate is improved, but the crystallinity of the cellulose is also reduced, and the tensile strength of fiber is weakened, so that the substitution of acetyl on thefiber is controlled by the reaction time so as to balance two contrary functions, and thus the optimization is realized. The cellulose used as the mechanical-enhancement filler is partially acetylated and modified and is hot blended with plasticized CDA so as to prepare a full cellulose acetate composite material, and a matrix and a filler are provided with acetyl on the surfaces and have the similar chemical structures, so that by adding partially acetylated cellulose, the interfacial compatibility between the CDA matrix and the acetylated cellulosic fiber can be promoted to be improved, andfinally, the mechanical performance of the composite material is improved.

Description

technical field [0001] The invention relates to the technical field of biological composite materials, in particular to an all-cellulose composite material and a preparation method thereof. Background technique [0002] In the past ten years, due to the advantages of biomaterials such as degradability, renewability, and inexhaustibility, research on the replacement of traditional plastics by biocomposites has received extensive attention. Cellulose and its derivatives, as the most abundant and inexhaustible raw materials on earth, are considered to be ideal bio-based polymer materials, which can meet the industry's growing demand for eco-friendly and environmentally friendly biomaterials in the future. In industry, cellulose acetate (CDA), as the main cellulose derivative, has been widely used in textile, packaging, cigarette filter and other industries. However, as a biodegradable plastic material, further improvement of its mechanical properties is needed to meet industri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/12C08B3/06
CPCC08B3/06C08L1/12C08L2205/025
Inventor 陈超赵健伟陈峰刘连梅程娜贺园园
Owner JIAXING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com