Steel structure machining process

A processing technology and steel structure technology, applied in the field of building component preparation, can solve the problems of unreasonable processing technology, affecting product quality, and high production cost, and achieve the effects of improving corrosion resistance, reasonable processing process, and improving product performance.

Inactive Publication Date: 2018-12-25
云南宏盛铁塔实业有限公司
View PDF8 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, there are still many problems in the existing steel structure processing. For example, the existing processing technology is unreasonable, resulting in repeated or excessive processing of steel components, which seriously affects product quality and high production costs.
In addition, most of the existing steel structures use spray paint to prevent corrosion, and most of them need to be sprayed 3 to 4 times, and they are easy to fall off and unsightly. Therefore, it is necessary to invent a steel structure processing technology to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] A steel structure processing technology, comprising the steps of:

[0082] 1) Raw material inspection:

[0083] Raw material inspection to ensure that all raw materials meet the current national and industry standards; among them, the steel materials in the raw materials are Q345B steel and Q235B steel; the bolts are 10.9-grade torsional shear type high-strength bolts; the anti-skid coefficient of the Q345B steel surface should not be less than 0.45 , the anti-skid coefficient of Q235B and steel of the same material shall not be less than 0.4;

[0084] 2) Lofting and nesting:

[0085] Stake out before processing, and check whether there is any error in the drawing. After checking, use the drawing for nesting. Before nesting, familiarize yourself with the drawing and process requirements, and then carry out the numbering; after the steel plate is marked, mark the reference line and center line and inspection control points; the joints of the components need to be clear...

Embodiment 2

[0121] A steel structure processing technology, comprising the steps of:

[0122] 1) Raw material inspection:

[0123] Raw material inspection to ensure that all raw materials meet the current national and industry standards; among them, the steel materials in the raw materials are Q345B steel and Q235B steel; the bolts are 10.9-grade torsional shear type high-strength bolts; the anti-skid coefficient of the Q345B steel surface should not be less than 0.45 , the anti-skid coefficient of Q235B and steel of the same material shall not be less than 0.4;

[0124] 2) Lofting and nesting:

[0125] Stake out before processing, and check whether there is any error in the drawing. After checking, use the drawing for nesting. Before nesting, familiarize yourself with the drawing and process requirements, and then carry out the numbering; after the steel plate is marked, mark the reference line and center line and inspection control points; the joints of the components need to be clear...

Embodiment 3

[0161] A steel structure processing technology, comprising the steps of:

[0162] 1) Raw material inspection:

[0163] Raw material inspection to ensure that all raw materials meet the current national and industry standards; among them, the steel materials in the raw materials are Q345B steel and Q235B steel; the bolts are 10.9-grade torsional shear type high-strength bolts; the anti-skid coefficient of the Q345B steel surface should not be less than 0.45 , the anti-skid coefficient of Q235B and steel of the same material shall not be less than 0.4;

[0164] 2) Lofting and nesting:

[0165] Stake out before processing, and check whether there is any error in the drawing. After checking, use the drawing for nesting. Before nesting, familiarize yourself with the drawing and process requirements, and then carry out the numbering; after the steel plate is marked, mark the reference line and center line and inspection control points; the joints of the components need to be clear...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a steel structure machining process. The steel structure machining process is characterized by comprising the steps that (1) raw materials are inspected; (2) laying off and jacking are carried out; (3) discharging and cutting are carried out; (4) material receiving is carried out; (5) H-shaped steel assembling and welding are carried out; (6) steel columns are manufactured;(7) roofing beams are manufactured; (8) crane beams are manufactured; (9) drilling is carried out; (10) rust removal and corrosion resistant are carried out; and (11) assembly is carried out. According to the steel structure machining process, the obtained steel structure has high quality, the percent of pass reaches more than 99%, the machining process sequence is reasonable, the cost is effectively reduced, meanwhile, the corrosion resistant performance of steel components is improved, the service life is prolonged, and the product performance is improved.

Description

technical field [0001] The invention belongs to the technical field of building component preparation, and in particular relates to a steel structure processing technology. Background technique [0002] Steel structure is a structure composed of steel materials, which is one of the main types of building structures. The structure is mainly composed of beam steel, steel column, steel truss and other components made of section steel and steel plate, and adopts rust removal and antirust technology. The components or components are usually connected by welds, bolts or rivets. Because of its light weight and easy construction, it is widely used in large factories and other fields. The steel structure system has comprehensive advantages such as light weight, factory manufacturing, fast installation, short construction period, good seismic performance, fast investment recovery, and less environmental pollution. With the unique advantages of development in three aspects, steel st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
CPCB23P15/00
Inventor 沈思义杨德兴杨庆兰
Owner 云南宏盛铁塔实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap