Nano-composite plate enhancer with insect-preventing effect

A nano-composite and strengthening agent technology, applied in wood treatment, impregnated wood, manufacturing tools, etc., can solve the problems of poor insect-proof performance, surface corrosion of nano-composite board furniture, etc., and achieve poor insect-proof effect

Inactive Publication Date: 2018-12-28
HEFEI LIANSEN YUTENG NEW MATERIAL TECH DEV CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the insect-proof performance of nano-composite boards is poor, so it is necessary to spray insect repellents during use to avoid the occurrence of moths
However, the insect repellants currently on the market are all aimed at ordinary wooden composite furniture. Spraying with this kind of insect repellent will have a certain corrosion effect on the surface of nano-composite board furniture.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A nano-composite plate strengthening agent with an insect-proof effect, prepared by the following components in parts by mass: 50 parts of natural vegetable wax, 30 parts of toad grass processing material, 12 parts of copper naphthenate, 3 parts of sodium lactate, sulfuric acid 5 parts of zinc, 4 parts of sodium sulfate, 1 part of lignin, 25 parts of soaking liquid mixed with diatomaceous earth and magnolia powder, and 100 parts of water.

[0019] Further, the preparation method of the toad grass processed material is as follows:

[0020] (1) Collecting toad grass flowers and toad grass leaves and storing them respectively for subsequent use;

[0021] (2) The sulfuric acid steam with a mass concentration of 10% was used to treat the toadstool flower for 25 minutes under the condition of a pressure of 10.8kPa, and after completion, it was 65°C of far-infrared radiation for 20s with a temperature equivalent to 5% of its weight. % wax gourd seed beating liquid, 2% rutin, ...

Embodiment 2

[0029] A nano-composite plate strengthening agent with an insect-proof effect, prepared by the following components in parts by mass: 80 parts of natural vegetable wax, 40 parts of toad grass processing material, 15 parts of copper naphthenate, 8 parts of sodium lactate, sulfuric acid 9 parts of zinc, 6 parts of sodium sulfate, 3 parts of lignin, 35 parts of diatomaceous earth and magnolia powder mixed soaking solution, and 120 parts of water.

[0030] Further, the preparation method of the toad grass processed material is as follows:

[0031] (1) Collecting toad grass flowers and toad grass leaves and storing them respectively for subsequent use;

[0032] (2) The sulfuric acid steam with a mass concentration of 10% was used to treat the toadstool flower for 30 minutes under the condition of a pressure of 11.2kPa, and after completion, it was irradiated with far-infrared rays at a temperature of 70°C for 30s, and then mixed with an amount equivalent to 70% of its weight. % wa...

Embodiment 3

[0040] A nano-composite plate strengthening agent with an insect-proof effect, prepared by the following components in parts by mass: 70 parts of natural vegetable wax, 35 parts of toad grass processing material, 13 parts of copper naphthenate, 4 parts of sodium lactate, sulfuric acid 6 parts of zinc, 5 parts of sodium sulfate, 2 parts of lignin, 30 parts of soaking solution mixed with diatomaceous earth and magnolia powder, and 110 parts of water.

[0041] Further, the preparation method of the toad grass processed material is as follows:

[0042] (1) Collecting toad grass flowers and toad grass leaves and storing them respectively for subsequent use;

[0043] (2) Sulfuric acid steam with a mass concentration of 10% is used to treat the toadstool flower for 25-30 minutes under the condition of a pressure of 11kPa, and after completion, it is 68°C of far-infrared radiation for 25s with a temperature equivalent to its weight. 6% wax gourd seed beating liquid, 3% rutin, and 0.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nano-composite plate enhancer with an insect-preventing effect. The nano-composite plate enhancer is prepared from the following components of, by mass, 50-80 parts of natural vegetable wax, 30-40 parts of pilea mollis processing materials, 12-15 parts of copper naphthenate, 3-8 parts of sodium lactate, 5-9 parts of zinc sulfate, 4-6 parts of sodium sulfate, 1-3 parts oflignin, 25-35 parts of kieselguhr and mangnolia officinalis powder mixed soak solutions and 100-120 parts of water. Through an experiment, according to the nano-composite plate enhancer with the insect-preventing effect, not any corrosion effect is achieved on the composite plate, meanwhile, the effect of insect prevention and floor reinforcing are achieved effectively, and after insect eggs are inoculated for one month, the bristletail rate of the plate is only 0.1%; and by using a commercially available common furniture insect-preventing agent, the corrosion harmfulness exists in the composite plate, meanwhile, the insect-preventing effect is poor, and the after insect eggs are inoculated for one month, the bristletail rate of furniture reaches up to 5.8%.

Description

technical field [0001] The invention relates to the technical field of plate maintenance, in particular to a nanocomposite plate strengthening agent with an insect-proof effect. Background technique [0002] Among the current home decoration building materials, after the wood is made into furniture, the surface of the furniture is sprayed with paint, which can play a role in moisture-proof and waterproof. Otherwise, in the long-term use process, it is easy to cause moisture damage to the furniture, resulting in certain economic losses. It is inconvenient for people to use. Composite panel furniture is a new type of furniture, which has good waterproof and moisture-proof performance, and has a broad market prospect. [0003] At present, the insect-proof performance of nano-composite boards is poor, so insect-proof agents need to be sprayed during use to avoid insect-eaten situations. However, the insect repellents currently on the market are all aimed at ordinary wooden com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52
CPCB27K3/52B27K2240/20
Inventor 程华风
Owner HEFEI LIANSEN YUTENG NEW MATERIAL TECH DEV CO LTD