Smooth and delicate PVC door sealing material and preparation method thereof
A PVC resin and smooth technology, which is applied in the field of refrigerator door seal materials and preparation, can solve the problems of poor hand touch, scratches, and poor softness of airbags.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0017] Using the above-mentioned preparation method of smooth and delicate PVC door seal material, the specific steps are as follows:
[0018] Step 1: Weighing: Accurately weigh each component according to the number of parts in claim 1;
[0019] Step 2: Mixing powder: Use a high-speed mixing pot to fully mix the accurately weighed PVC resin, hand-feeling agent, elastomer, stabilizer, lubricant, and antibacterial and anti-fungal agent. After mixing slowly for 1min to 2min, it will follow the rights All the plasticizers that are accurately weighed in the weight ratio in 1 are put into the barrel of the high-speed mixing pot and slowly added to the high-speed mixing pot to increase the temperature of the high-speed mixing pot. When the temperature of the high-speed mixing pot rises When the temperature reaches 100℃, all the plasticizers in the high-speed mixing pot barrel are added to the high-speed mixing pot. When the temperature of the high-speed mixing pot rises to 105℃, the fill...
Example Embodiment
[0022] Example one:
[0023] The refrigerator door seal material of the present invention is accurately weighed according to the following material parts:
[0024] PVC resin is 100 parts, plasticizer is 50-75 parts, filler is 40-110 parts, hand-feeling agent is 1-3 parts, elastomer is 5-20 parts, stabilizer is 1-5 parts, lubricant is 0.2~1 part, 0.2~2 part of antibacterial and antifungal agent,
[0025]
[0026] Mix the accurately weighed PVC resin, hand-feeling agent, elastomer, stabilizer, lubricant and anti-bacterial and anti-fungal agent in a high-speed mixing pot. After mixing slowly for 1 to 2 minutes, the weight ratio will be accurately weighed. Put all the plasticizers in the high-speed mixing pot barrel slowly into the high-speed mixing pot to increase the temperature of the high-speed mixing pot. When the temperature of the high-speed mixing pot reaches 100℃, the high-speed mixing pot The plasticizer in the barrel is all added to the high-speed mixing pot. When the temper...
Example Embodiment
[0033] Embodiment two:
[0034] The refrigerator door seal material of the present invention is accurately weighed according to the following material parts:
[0035]
[0036]
[0037] Mix accurately weighed PVC resin, feel agent, elastomer, stabilizer, lubricant and antibacterial and antifungal agent in a high-speed mixing pot. The mixing time is 1min~3min. After the mixture is fully mixed, it will be The plasticizer with the above weight ratio accurately weighed is put into the barrel of the high-speed mixing pot and slowly added into the high-speed mixing pot to increase the temperature of the high-speed mixing pot. When the temperature of the high-speed mixing pot rises to 100 When the temperature is ℃, all the plasticizers in the barrel of the high-speed mixing pot are added to the high-speed mixing pot. When the temperature of the high-speed mixing pot rises to 105°C, the filler is added through the barrel of the high-speed mixing pot to mix at high speed. The mixing pot con...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap