Environmental-friendly flame-retardant antibacterial fiberboard for reinforced wood floor

A technology of laminated wood flooring and antibacterial fiber, applied in the field of materials, can solve problems such as easy deformation, peculiar smell, breeding bacteria, etc., and achieve the effect of reducing effective combustion heat and mass loss rate

Active Publication Date: 2019-01-08
陕西森尚建材科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high-density board made of this adhesive and auxiliary materials or the further produced laminate flooring will release harmful substances such as formaldehyde, which has certain toxicity and peculiar smell and is easy to deform. Once it is damp, it is easy to mildew and breed Bacteria, Pests, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-friendly flame-retardant antibacterial fiberboard for reinforced wood floor
  • Environmental-friendly flame-retardant antibacterial fiberboard for reinforced wood floor
  • Environmental-friendly flame-retardant antibacterial fiberboard for reinforced wood floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] An environmentally friendly flame-retardant and antibacterial fiberboard for laminate flooring, the preparation process of which comprises the following steps:

[0068] The first step, wood fiber is dried to moisture content 10wt%;

[0069] In the second step, the dried wood fiber is put into a high-speed mixer and stirred at 1500 rpm for thinning for 1 minute to obtain thinned wood fiber;

[0070] The third step is to mix the thinned wood fiber and 3% of its weight of nano-bentonite evenly, pave it into the mold, pre-press it through a pre-press, and cut off the burrs to obtain a slab;

[0071] The fourth step is to heat-press the slab using a hot-press machine, with a hot-pressing pressure of 4 MPa and a temperature of 170°C. After hot-pressing for 4 minutes, stop the hot-pressing;

[0072] The fifth step is to place the hot-pressed board in an indoor environment of 20° C. for 15 days to obtain the environmentally friendly flame-retardant and antibacterial fiber boar...

Embodiment 2

[0074] An environmentally friendly flame-retardant and antibacterial fiberboard for laminate flooring, the preparation process of which comprises the following steps:

[0075] In the first step, wood fibers are treated with magnetically immobilized laccase;

[0076] In the second step, the wood fiber treated with magnetically immobilized laccase is dried to a moisture content of 10wt%;

[0077] In the third step, the dried wood fibers are put into a high-speed mixer and stirred at 1500 rpm for thinning for 1 minute to obtain thinned wood fibers;

[0078] The fourth step is to mix the thinned wood fiber and 3% of its weight of nano-bentonite evenly, pave it into the mold, pre-press it through a pre-press, and cut off the burr to obtain a slab;

[0079] The fifth step is to heat-press the slab with a hot-pressing machine, the hot-pressing pressure is 4MPa, the temperature is 170°C, and after hot-pressing for 4 minutes, stop the hot-pressing;

[0080] The sixth step is to place...

Embodiment 3

[0087] An environmentally friendly flame-retardant and antibacterial fiberboard for laminate flooring, the preparation process of which comprises the following steps:

[0088] In the first step, wood fibers are treated with magnetically immobilized laccase;

[0089] In the second step, the wood fiber treated with magnetically immobilized laccase is dried to a moisture content of 10wt%;

[0090] In the third step, the dried wood fibers are put into a high-speed mixer and stirred at 1500 rpm for thinning for 1 minute to obtain thinned wood fibers;

[0091] The fourth step is to mix the thinned wood fiber and 3% of its weight of nano-bentonite evenly, pave it into the mold, pre-press it through a pre-press, and cut off the burr to obtain a slab;

[0092] The fifth step is to heat-press the slab with a hot-pressing machine, the hot-pressing pressure is 4MPa, the temperature is 170°C, and after hot-pressing for 4 minutes, stop the hot-pressing;

[0093] The sixth step is to place...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly flame-retardant antibacterial fiberboard for a reinforced wood floor. The producing process of the environment-friendly flame-retardant antibacterial fiberboard for the reinforced wood floor comprises the steps of wood fiber drying, thinning, prepressing, hot pressing and balanced placing. By means of the environment-friendly flame-retardant antibacterial fiberboard for the reinforced wood floor, the effective combustion heat and mass loss rate of the fiberboard are reduced, the quantity of generated combustible volatile matters is reduced, and the flame retardant performance of the fiberboard is obviously improved; and meanwhile, different from the surface bacteriostasis of other fiberboards, bacteriostatic components are added into the fiberboard to effectively prevent and inhibit harmful microorganisms, ensure the mechanical properties of the fiberboard, and endow the fiberboard with excellent bacteriostasis and mildew resistance performance.

Description

technical field [0001] The invention relates to the field of material technology, in particular to an environmentally friendly flame-retardant and antibacterial fiberboard for laminate flooring. Background technique [0002] The laminate flooring currently on the market is made of high-density fiberboards, which are made of wood fibers or straw fibers and adhesives. Adhesives are mainly urea-formaldehyde resins, phenolic resins, etc., and auxiliary materials are generally insect repellents of chemically synthesized materials. The high-density board made of this adhesive and auxiliary materials or the further produced laminate flooring will release harmful substances such as formaldehyde, which has certain toxicity and peculiar smell and is easy to deform. Once it is damp, it is easy to mildew and breed Bacteria, pests, etc. [0003] The invention of application number 201510756424.5 discloses an environmentally friendly flame-retardant and antibacterial laminate flooring a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/04B27N3/12
CPCB27N3/04B27N3/12
Inventor 魏开宇
Owner 陕西森尚建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap