Waterproof TPU film technology and formula

A film technology and formula technology, applied in the field of waterproof TPU film technology and formula, can solve problems such as affecting production and processing stability, unable to guarantee waterproof performance, increasing production cost, etc., to facilitate heating operation, improve waterproof effect, and ensure smooth operation. sexual effect

Inactive Publication Date: 2019-01-08
RUIAN HONGRI PLASTIC
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The sub-chain of TPU is generally composed of hard segment and soft segment. The soft segment is generally hydroxyl-terminated polyether, polyester and polyolefin, etc. The hard segment is generally formed of polyurethane by chain extender and isocyanate. Various industries such as medical treatment and chemistry, but the existing TPU ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A waterproof TPU film process and formula, the waterproof TPU film process and formula include TUF particles 70%, ABS-g-maleic anhydride 6%, silicon dioxide 3%, natural polyphenol 6%, epoxy resin 10% and light Stabilizer 5%.

[0045] As preferably, described waterproof TPU film technology and formula comprise the steps:

[0046] S1. Raw material screening: After the TPU particles are pulverized by a pulverizer, they are screened through a 400-mesh to 500-mesh screen, and the raw material particles are selected for use.

[0047] S2. Melting: Add the selected raw material particles, ABS-g-maleic anhydride, silicon dioxide, natural polyphenols, epoxy resin and light stabilizer into the reactor, heat the temperature to 170 degrees Celsius to 190 degrees Celsius, and stir evenly, The raw material is melted into a molten state.

[0048] S3. Film blowing: Add molten raw materials into the film blowing machine, and blow out the film at a temperature of 140 degrees Celsius to ...

Embodiment 2

[0062] A waterproof TPU film process and formula, the waterproof TPU film process and formula include 71% TUF particles, ABS-g-maleic anhydride 5%, silicon dioxide 2%, natural polyphenol 8%, epoxy resin 10% and light Stabilizer 4%.

[0063] As preferably, described waterproof TPU film technology and formula comprise the steps:

[0064] S1. Raw material screening: After the TPU particles are pulverized by a pulverizer, they are screened through a 400-mesh to 500-mesh screen, and the raw material particles are selected for use.

[0065] S2. Melting: Add the selected raw material particles, ABS-g-maleic anhydride, silicon dioxide, natural polyphenols, epoxy resin and light stabilizer into the reactor, heat the temperature to 170 degrees Celsius to 190 degrees Celsius, and stir evenly, The raw material is melted into a molten state.

[0066] S3. Film blowing: Add molten raw materials into the film blowing machine, and blow out the film at a temperature of 140 degrees Celsius to ...

Embodiment 3

[0080] A waterproof TPU film process and formula, the waterproof TPU film process and formula include 70% TUF particles, ABS-g-maleic anhydride 7%, silicon dioxide 2%, natural polyphenol 6%, epoxy resin 12% and light Stabilizer 3%.

[0081] As preferably, described waterproof TPU film technology and formula comprise the steps:

[0082] S1. Raw material screening: After the TPU particles are pulverized by a pulverizer, they are screened through a 400-mesh to 500-mesh screen, and the raw material particles are selected for use.

[0083] S2. Melting: Add the selected raw material particles, ABS-g-maleic anhydride, silicon dioxide, natural polyphenols, epoxy resin and light stabilizer into the reactor, heat the temperature to 170 degrees Celsius to 190 degrees Celsius, and stir evenly, The raw material is melted into a molten state.

[0084] S3. Film blowing: Add molten raw materials into the film blowing machine, and blow out the film at a temperature of 140 degrees Celsius to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a waterproof TPU film technology and a formula. The waterproof TPU film technology and the formula are characterized in that the formula is prepared from 70 to 80 percent of TUF particles, 5 to 8 percent of ABS-g-maleic anhydride, 1 to 3 percent of silica, 6 to 10 percent of natural polyphenol, 10 to 15 percent of epoxy resin and 3 to 5 percent of a light stabilizer. According to the waterproof TPU film technology and the formula provided by the invention, by changing the compositions and the ratio of raw materials and adding a crosslinking agent, the smooth finish of the waterproof TPU film can be improved and particulate matters in a TPU film are eliminated; in addition, structural tightness and stability of raw materials can be ensured and the waterproof effect is improved; by improving the processing technology, the process is simplified, heat supply operation is facilitated, and the production cost is effectively reduced, so that the use stability can be greatly improved and the smoothness of production and processing is ensured.

Description

technical field [0001] The invention relates to the field of film technology, in particular to a waterproof TPU film process and formula. Background technique [0002] TPU is a polymer polymerized by polymer compounds. It is widely used in industry and industrial production, and its development has been very rapid in recent years. [0003] The sub-chain of TPU is generally composed of hard segment and soft segment. The soft segment is generally hydroxyl-terminated polyether, polyester and polyolefin, etc. The hard segment is generally formed of polyurethane by chain extender and isocyanate. Various industries such as medical treatment and chemistry, but the existing TPU material film cannot guarantee its waterproof performance in the material ratio. In high-demand industries, the stability of the product is poor. The production cost is increased, and it is also inconvenient to control during the production process, which is not conducive to the operation of workers and affe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08L55/02C08L63/00C08K3/36C08J5/18
CPCC08J5/18C08J2375/04C08J2455/02C08J2463/00C08K3/36
Inventor 陈维兴
Owner RUIAN HONGRI PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap