Water-based quenching equipment and quenching method for phi76.2mm steel balls made of GCr15SiMn steel

A technology of water-based quenching and water-based quenching agent, applied in the direction of quenching agent, quenching device, heat treatment equipment, etc., to achieve the effect of ensuring the heart tissue, improving the hardness of the heart, and cooling uniformly

Inactive Publication Date: 2019-01-08
LUOYANG LYC BEARING
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface hardness after oil quenching and alkaline water quenching can meet the technical requi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1:

[0019] Bearing parts model: φ76.2mm steel ball, material: GCr15SiMn. 500 capsules. Technical requirements: surface hardness HRC60~64, core hardness ≥HRC57.

[0020] GCr15SiMn steel Ф76.2mm water-based quenching method, the heat treatment, quenching and tempering equipment is a pit furnace, and the quenching cooling medium is a water-based quenching liquid (ZHY-101 type water-based quenching agent and water from Dalian Sanjin Lubricating Oil Co., Ltd. 1:1 ratio solution), medium temperature 40 ℃. Its implementation steps are as follows:

[0021] 1. Loading: The steel balls are evenly distributed on the flat material tray, and the number of layers is one layer;

[0022] 2. Pit furnace heating: heating temperature 810℃, heating time 180min;

[0023] 3. Quenching and cooling in the quenching tank: After the steel balls are heated, they are lifted out together with the material tray, and placed in the quenching tank for cooling. The operation time from rel...

Example Embodiment

[0027] Example 2:

[0028] Bearing parts model: φ76.2mm steel ball, material: GCr15SiMn. 800 capsules. Technical requirements: surface hardness HRC60~64, core hardness ≥HRC57.

[0029] GCr15SiMn steel Ф76.2mm water-based quenching method, the heat treatment, quenching and tempering equipment is a pit furnace, and the quenching cooling medium is a water-based quenching liquid (ZHY-101 type water-based quenching agent and water from Dalian Sanjin Lubricating Oil Co., Ltd. 1:1 ratio solution), medium temperature 30 ℃. Its implementation steps are as follows:

[0030] 1. Loading: The steel balls are evenly distributed on the flat material tray, and the number of layers is one layer;

[0031] 2. Pit furnace heating: heating temperature 805℃, heating time 175min;

[0032] 3. Quenching and cooling in the quenching tank: After the steel balls are heated, they are lifted out together with the material tray, and placed in the quenching tank for cooling. The operation time from rel...

Example Embodiment

[0036] Example 3:

[0037] Bearing parts model: φ76.2mm steel ball, material: GCr15SiMn. 800 capsules. Technical requirements: surface hardness HRC60~64, core hardness ≥HRC57.

[0038] GCr15SiMn steel Ф76.2mm water-based quenching method, the heat treatment, quenching and tempering equipment is a pit furnace, and the quenching cooling medium is a water-based quenching liquid (ZHY-101 type water-based quenching agent and water from Dalian Sanjin Lubricating Oil Co., Ltd. 1:1 ratio solution), medium temperature 45 ℃. Its implementation steps are as follows:

[0039] 1. Loading: The steel balls are evenly distributed on the flat material tray, and the number of layers is one layer;

[0040] 2. Pit furnace heating: heating temperature 815℃, heating time 190min;

[0041] 3. Quenching and cooling in the quenching tank: After the steel balls are heated, they are lifted out together with the material tray, and placed in the quenching tank for cooling. The operation time from rel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Heart hardnessaaaaaaaaaa
Heart hardnessaaaaaaaaaa
Heart hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses water-based quenching equipment and a water-based quenching method for phi76.2mm steel balls made of GCr15SiMn steel. By the water-based quenching method for the phi76.2mm steel balls made of the GCr15SiMn steel, water-based quenching liquid obtained through reasonable formulation of a water-based quenching agent and water is used as a cooling medium to control the steel ball quenching cooling time and the liquid discharging temperature, and for such steel balls with relatively large specifications, the core cooling rate can be obviously increased, the core structure isguaranteed and the core hardness is improved.

Description

technical field [0001] The invention relates to the technical field of bearing heat treatment, in particular to water-based quenching equipment and a quenching method for φ76.2mm steel balls made of GCr15SiMn steel. Background technique [0002] After heat treatment and quenching, the surface hardness and structure of the steel ball can easily meet the technical standard requirements, while the hardness and structure of the core will show differences with the size of the steel ball. With the development of the wind power market, users have put forward higher requirements for product quality. The GCr15SiMn steel ball with a specification of Ф76.2mm is the type used by a wind power bearing user. The technical conditions require that the surface hardness is HRC60~64, and the core hardness is ≥HRC57. The surface hardness after oil quenching and alkaline water quenching can meet the technical requirements, but the core hardness is HRC52~54, which does not meet the technical requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D9/36C21D1/62C21D1/18C21D1/60
Inventor 王珂龚建勋陈卉珍张中文周鹏龙郝奥玄韩万顺王旗卫王红伟倪滨昆
Owner LUOYANG LYC BEARING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap