Black-body celadon body material, black-fetal celadon porcelain and manufacturing method of black-fetal celadon porcelain

A technology of black-bodied celadon base materials and black-bodied celadon porcelain, which is applied in the field of black-bodied celadon base materials, can solve problems such as large differences, and achieve the effects of suitable firing temperature, reasonable content, and stable quality

Inactive Publication Date: 2019-01-11
龙泉市建春青瓷厂
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in terms of product shape, appearance characteristics, glaze configuration, detail finishing process, firing process, etc., they are quite different from Southern Song Dynasty celadon with thin body and thick glaze and black body. imitating Ge Kiln celadon from the Song Dynasty to improve the production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Black body celadon base material, the base material contains 20 parts of Huangkou porcelain clay, 30 parts of Mudaikou purple gold clay, 10 parts of Gaojitou purple gold clay, 20 parts of Jindan porcelain clay, 12 parts of Baogeng porcelain clay, carboxymethyl 0.1 part of sodium cellulose, 0.02 part of tris(nonylphenyl) phosphite.

[0055] Wherein, the fineness of tire material is 120 mesh.

[0056] Black body celadon porcelain, containing by weight: 18 parts of Siyuan glazed soil, 18 parts of Zhoucun glazed soil, 10 parts of potassium feldspar, 11 parts of Tashi limestone, 2 parts of quartz, 2 parts of alumina, Baoxi purple gold soil 5 parts, 0.01 part of aluminum dihydrogen phosphate, 0.05 part of ammonium hypophosphite, 1 part of borax.

[0057] The production method of black-bodied celadon porcelain, including mud preparation, bisque firing, cinnabar-bodied celadon glaze preparation, glaze application, and glaze firing,

[0058] 1) The preparation steps of mud mud...

Embodiment 2

[0069] Black-bodied celadon base material, the base material contains 23 parts of Huangkou porcelain clay, 34 parts of Mudaikou purple gold clay, 13 parts of Gaojitou purple gold clay, 22 parts of Jindan porcelain clay, 15 parts of Baogeng porcelain clay, carboxymethyl 0.25 parts of cellulose sodium and 0.035 parts of tris(nonylphenyl)phosphite.

[0070] Among them, the fineness of tire material is 160 mesh.

[0071] Black body celadon porcelain, containing by weight: 22 parts of Siyuan glazed soil, 20 parts of Zhoucun glazed soil, 12 parts of potassium feldspar, 13 parts of Tashi limestone, 3.5 parts of quartz, 3 parts of alumina, Baoxi purple gold soil 7.5 parts, 0.03 parts of aluminum dihydrogen phosphate, 0.08 parts of ammonium hypophosphite, and 2 parts of borax.

[0072] The production method of black-bodied celadon porcelain, including mud preparation, bisque firing, cinnabar-bodied celadon glaze preparation, glaze application, and glaze firing,

[0073] 1) The prepar...

Embodiment 3

[0084] Black body celadon base material, the base material contains 26 parts of Huangkou porcelain clay, 38 parts of Mudaikou purple gold clay, 16 parts of Gaojitou purple gold clay, 25 parts of Jindan porcelain clay, 17 parts of Baogeng porcelain clay, carboxymethyl 0.4 part of cellulose sodium, 0.05 part of tris(nonylphenyl) phosphite.

[0085] Wherein, the fineness of tire material is 200 mesh.

[0086] Black body celadon porcelain, containing by weight: 25 parts of Siyuan glazed soil, 22 parts of Zhoucun glazed soil, 15 parts of potassium feldspar, 15 parts of Tashi limestone, 5 parts of quartz, 4 parts of alumina, Baoxi purple gold soil 10 parts, 0.05 parts of aluminum dihydrogen phosphate, 0.012 parts of ammonium hypophosphite, 3 parts of borax.

[0087] The production method of black-bodied celadon porcelain, including mud preparation, bisque firing, cinnabar-bodied celadon glaze preparation, glaze application, and glaze firing,

[0088] 1) The preparation steps of mu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a black-body celadon body material, a black-body celadon porcelain and a manufacturing method of the black-fetal celadon porcelain. The body material contains Huangkou porcelain clay, Mudaikou Zijin clay, Gaojitou Zijin clay, Jindan porcelain clay, Baogeng porcelain clay, sodium carboxymethyl cellulose and tris(nonylphenyl)phosphite; a glaze material of the porcelain contains Siyuan glaze clay, Zhoucun glaze clay, potash feldspar, agalmatolite limestone, quartz, alumina, Baoxi Zijin clay, aluminum dihydrogen phosphate, ammonium hypophosphite and borax. The preparation method includes blank mud preparation, biscuiting, vermilion-body celadon glaze material preparation, glaze application and glaze firing. The black-body celadon body has high yield and stable quality in the firing process and has pure black-body color of Longquan celadon; the glaze material for porcelain reduces the fluidity and transparency of a glaze layer in a high temperature state, has the characteristics of thin body, thick glaze of the black body and has the glaze which is thicker than the body; the firing temperature of the preparation method is appropriate, and the prepared black-bodyceladon porcelain has the advantages of stable quality, beautiful color, low defective percentage, and easy management and operation.

Description

technical field [0001] The invention relates to the technical field of celadon manufacture, in particular to black-bodied celadon body material, black-bodied celadon porcelain and a manufacturing method thereof. technical background [0002] "The Source of Three Rivers" Longquan City is located in the southwest of Zhejiang. The local ceramic mineral resources in Longquan are abundant and the water system is abundant. Most of the local kiln workers build their workshops on the foothills of rivers or streams near the clay mines. The forests on the mountains and the nearby clay mines provide raw materials and fuel for production, and the nearby streams are The workshop provides water for production, and such natural conditions become an inherent advantage for firing porcelain. In particular, the local specialty "Purple Gold Soil" is the key. There are many local porcelain clay producing areas in Longquan, mainly Baoxi, Mudai, Yuandi, Wuduba, Hangkou, Lingshang, Shangyang, Xia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C03C8/00
CPCC03C8/00C04B33/13C04B33/131C04B35/6365
Inventor 吴建春
Owner 龙泉市建春青瓷厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com