Efficient bleaching process of white cement clinkers

A cement clinker and cement clinker cooling technology, applied in the field of white cement production, can solve the problems of consumption, limited improvement of whiteness, excessive heat consumption, etc., and achieve the effects of accelerating cooling rate, improving whiteness, and reducing production costs

Inactive Publication Date: 2019-01-15
江西银杉白水泥股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-efficiency bleaching process for white cement clinker, so as

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient bleaching process of white cement clinkers

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] The embodiments of the present invention will be further described below in conjunction with the drawings.

[0020] Such as figure 1 As shown, the high-efficiency bleaching process of white cement clinker in this embodiment includes the following steps:

[0021] S1: Rotary kiln 1 burns white cement clinker at high temperature, and discharges it into grate cooler 2 from the discharge end of rotary kiln 1 for cooling;

[0022] S2: After the high-temperature cement clinker enters the grate cooler 2, it falls to the first grate bed 3 for cooling. The first grate bed 3 provides mixed liquid nitrogen and air to quench the cement clinker, and the cement clinker Cool to 600℃~800℃;

[0023] S3: Then the cement clinker falls to the second grate bed 4 for cooling, and the second grate bed 4 is completely air-cooled by air, and the cement clinker is cooled to 80°C-100°C before being discharged from the grate cooler 2.

[0024] In this embodiment, the liquid nitrogen in step 2 is provided b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an efficient bleaching process of white cement clinkers. The efficient bleaching process of the white cement clinkers comprises the following steps of performing high-temperature firing on the white cement clinkers by a rotary kiln; discharging the white cement clinkers into a grate cooler from the discharging end of the rotary kiln for cooling; after the high-temperature cement clinkers enter the grate cooler, falling the high-temperature cement clinkers onto a first grate bed for cooling; performing sharp cooling on the cement clinkers in the first grate bed through providing mixed liquid nitrogen and air; cooling the cement clinkers to 600 to 800 DEG C; then, falling the cement clinkers onto a second grate bed to be cooled; performing air cooling in the second grate bed completely through the air; cooling the cement clinkers to 80 to 100 DEG C; discharging the cement clinkers out of the grate cooler. The invention aims at providing the efficient bleaching process of the white cement clinkers so as to solve the problems of whiteness improvement limitation and more heat consumption requirement during white cement clinker calcination.

Description

technical field [0001] The invention belongs to the field of white cement production, and in particular relates to a high-efficiency bleaching process of white cement clinker. Background technique [0002] After the Portland cement clinker is fired at high temperature, it needs to be cooled rapidly by air cooling to ensure that the clinker has good physical and mechanical properties, while the white Portland cement usually needs to be sprayed with water (or drenched in water or soaked in water) to increase the glass body to improve the temperature. Clinker whiteness (ie bleaching). Compared with rotary kiln calcining ordinary cement clinker, rotary kiln calcining white cement clinker is wasted due to water cooling, and the heat carried by clinker becomes water vapor. Since the rotary kiln cannot provide secondary air and tertiary air for calcination, As a result, the calcination of white cement clinker needs more heat consumption, and the output is low and the cost is high;...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/48
CPCC04B7/48
Inventor 黄少文曾嵘朱杰
Owner 江西银杉白水泥股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap