A kind of preparation method of aluminum-phosphorus alloy for hypereutectic aluminum-silicon modification

An aluminum-phosphorus alloy and hypereutectic technology, which is applied in the field of preparation of aluminum-phosphorus alloys for hypereutectic aluminum-silicon modification, can solve the problem of no preparation method, and achieve the effects of good refining effect, improved performance and simple operation.

Active Publication Date: 2021-04-09
LIAONING UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although these phosphorus-containing master alloys are easy to prepare, for hypereutectic aluminum-silicon alloys with limited Cu, Ni, Zr and other elements, these phosphorus-containing master alloys cannot be used for modification.
Therefore, seeking a high-efficiency and clean master alloy is already a future development trend and market demand. People have been looking forward to the appearance of aluminum-phosphorus alloys, but so far there is still no preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of aluminum-phosphorus alloy for hypereutectic aluminum-silicon modification
  • A kind of preparation method of aluminum-phosphorus alloy for hypereutectic aluminum-silicon modification

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Melt 198.5g of industrial pure aluminum and adjust the temperature of molten aluminum to 1400°C;

[0021] (2) Wrap 12g of aluminum phosphide particles with 1.5g of aluminum foil and press them into molten aluminum. 3.03% of mass;

[0022] (3) After the aluminum phosphide is dissolved in the molten aluminum, keep it warm for 2 minutes, and pour the aluminum-phosphorus alloy liquid into the metal tank made of steel plate.

[0023] According to the above operations, an aluminum-phosphorus alloy with a phosphorus content of 3.03% can be obtained.

Embodiment 2

[0025] (1) Melt 198g of industrial pure aluminum and adjust the temperature of the molten aluminum to 1800°C;

[0026] (2) 24g of aluminum phosphide particles are wrapped together with 2g of aluminum foil, pressed into molten aluminum with a quartz tube, and the content of phosphorus accounts for 5.73% of the total mass of the molten aluminum;

[0027] (3) After the aluminum phosphide is dissolved in the molten aluminum, keep it warm for 6 minutes, and pour the aluminum-phosphorus alloy liquid into the metal tank made of steel plate.

[0028] According to the above operations, an aluminum-phosphorus alloy with a phosphorus content of 5.73% can be obtained.

Embodiment 3

[0030] (1) Melt 200g of industrial pure aluminum and adjust the temperature of the molten aluminum to 1400°C;

[0031] (2) 4g of aluminum phosphide particles to be added are wrapped together with aluminum foil, and pressed into molten aluminum with a quartz tube, and the content of phosphorus accounts for 1.05% of the total mass of the molten aluminum;

[0032] (3) After the aluminum phosphide is dissolved in the molten aluminum, keep it warm for 2 minutes, and pour the aluminum-phosphorus alloy liquid into the metal tank made of steel plate.

[0033] According to the above operations, an aluminum-phosphorus alloy with a phosphorus content of 1.05% can be obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

A method for preparing an aluminum-phosphorus alloy for hypereutectic aluminum-silicon modification, the steps are: (1) melting industrial pure aluminum, and adjusting the temperature of the molten aluminum to 1400-2000°C; (2) pressing aluminum phosphide particles into Aluminum liquid, wherein, the content of phosphorus in the aluminum phosphide accounts for 1-10% of the total mass of the aluminum liquid; (3) after the aluminum phosphide is pressed into the aluminum liquid, it is kept warm for 2min-10min to obtain a phosphorus-containing aluminum melt; The aluminum melt of phosphorus is poured into the metal groove made of the steel plate, and the aluminum-phosphorus alloy sheet is obtained. The method has the advantages of simple process and easy operation, can be used as a primary modification agent for refinement of hypereutectic aluminum-silicon alloy, has good refinement effect of primary crystal silicon, and has no pollution to the environment.

Description

technical field [0001] The invention belongs to a preparation method of an intermediate alloy, in particular to a preparation method of an aluminum-phosphorus alloy for hypereutectic aluminum-silicon modification. Background technique [0002] Hypereutectic aluminum-silicon alloy has the characteristics of low density, high hardness, wear resistance, high temperature resistance, and low thermal expansion coefficient. It is most suitable for manufacturing high-performance automotive engine cylinders, pistons and other parts. However, the coarse primary silicon in the tissue leads to almost zero elongation, which cannot meet the requirements of the parts. For this reason, people try to change the shape of primary silicon while refining primary silicon to improve its toughness, thus developing new technologies such as metamorphic treatment. Among many modification methods, phosphorus modification treatment is the most effective and stable method for refining primary silicon. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/04C22C1/03C22C1/02C22C21/00
CPCC22C1/026C22C1/03C22C21/00C22C21/04
Inventor 李青春陈淑英岳旭东常国威
Owner LIAONING UNIVERSITY OF TECHNOLOGY