Sour taste-free polyvinyl alcohol composition, cast film and preparation method of cast film
A technology of polyvinyl alcohol flow and polyvinyl alcohol, which is applied in the field of preparation of non-acid polyvinyl alcohol casting film, can solve the problems of high equipment conditions, efficiency and production cost, and achieve superior performance, light sour taste and high tensile strength Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0037]a) 75 parts of PVA (the degree of polymerization is 1700, the degree of alcoholysis is 88%), 25 parts of glycerin and 1% zeolite are added to the twin-screw extruder at the same time, and the temperatures of the 1st to 9th sections of the extruder and the die are respectively 160°C, 170°C, 180°C, 180°C, 180°C, 180°C, 180°C, 180°C, 180°C and 170°C, and the screw speed is 250rpm. After the extruded strip is cooled, it is granulated by a pelletizer to obtain light yellow thermoplastic TPVA pellets. The resulting TPVA particle T g : 61.2°C, T c : 100.8°C, T m : 154.7°C.
[0038] b) Add the light yellow thermoplastic PVA pellets obtained from step a) into the single-screw extruder, and the temperatures of the first, second, and third sections of the extruder and the die are sequentially 190°C, 195°C, 195°C and 195°C , the screw speed is 20rpm, the PVA pellets are plasticized, melted, extruded, roller conveyed and drawn, and wound to obtain a PVA cast film. The strengths ...
Embodiment 2
[0040] a) 75 parts of PVA (the degree of polymerization is 1700, the degree of alcoholysis is 88%), 25 parts of glycerin and 2% zeolite are added to the twin-screw extruder at the same time, and the temperatures of the 1st to 9th sections of the extruder and the die are respectively 160°C, 170°C, 180°C, 180°C, 180°C, 180°C, 185°C, 183°C, 180°C and 170°C, and the screw speed is 250rpm. After the extruded strip is cooled, it is granulated by a pelletizer to obtain light yellow thermoplastic PVA pellets. The resulting TPVA particle T g : 60.8°C, T c : 97.8°C, T m : 154.1°C.
[0041] b) Add the light yellow thermoplastic PVA pellets obtained from step a) into the single-screw extruder, and the temperatures of the first, second, and third sections of the extruder and the die are sequentially 190°C, 195°C, 195°C and 195°C , the screw speed is 20rpm, the PVA pellets are plasticized, melted, extruded, roller conveyed and drawn, and wound to obtain a PVA cast film. The strengths o...
Embodiment 3
[0043] a) 75 parts of PVA (the degree of polymerization is 1700, the degree of alcoholysis is 88%), 25 parts of glycerin and 3% zeolite are added to the twin-screw extruder at the same time, and the temperatures of the 1st to 9th sections of the extruder and the die are respectively 160°C, 170°C, 180°C, 180°C, 185°C, 185°C, 186°C, 190°C, 180°C and 170°C, and the screw speed is 250rpm. After the extruded strip is cooled, it is granulated by a pelletizer to obtain light yellow thermoplastic PVA pellets. The resulting TPVA particle T g : 63.1°C, T c : 99.0°C, T m : 152.9°C.
[0044] b) Add the light yellow thermoplastic PVA pellets obtained from step a) into the single-screw extruder, and the temperatures of the first, second, and third sections of the extruder and the die are sequentially 190°C, 195°C, 195°C and 195°C , the screw speed is 20rpm, the PVA pellets are plasticized, melted, extruded, roller conveyed and drawn, and wound to obtain a PVA cast film. The elongation ...
PUM
Property | Measurement | Unit |
---|---|---|
Strength | aaaaa | aaaaa |
Strength | aaaaa | aaaaa |
Strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com