Ceramic product with self-cleaning glaze and making method thereof

A technology for a ceramic product and a manufacturing method, applied in the field of ceramics, can solve the problems of unsatisfactory glaze surface smoothness, easy contamination and cleaning, and difficult removal of the glaze surface, so as to reduce the scratch defect of the glaze surface, improve the quality of the glaze surface, Easy to clean effect

Active Publication Date: 2019-03-08
福建省德化龙辉陶瓷有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Based on the above prior art, the purpose of the present invention is to provide a ceramic product with self-cleaning glaze and its manufacturing method, to overcome the unsatisfactory smoothness of the ceramic glaze in the prior art, the glaze is easy to stain and clean It is more difficult, the glaze will turn yellow and it is not easy to remove, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic product with self-cleaning glaze and making method thereof
  • Ceramic product with self-cleaning glaze and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This embodiment provides a ceramic product with a self-cleaning glaze, including a base material and a glaze, and the base material includes the following raw materials in parts by weight: 40 parts of kaolin, 18 parts of quartz, 25 parts of potassium feldspar, 10 parts of clay, talc 1 part; the glaze includes a bottom glaze and a top glaze, and the bottom glaze includes the following raw materials in parts by weight: 24 parts of potassium feldspar, 10 parts of nano-zinc oxide, 10 parts of quicklime, 4 parts of burnt talc, 24 parts of kaolin, zirconium silicate 8 parts, 5 parts of wollastonite, 1 part of bone ash, 1 part of calcium borate, 20 parts of frit; the surface glaze includes the following raw materials in parts by weight: 26 parts of potassium feldspar, 8 parts of zinc oxide, 8 parts of calcium oxide, and 8 parts of aluminum oxide , 3 parts of magnesium oxide, 26 parts of kaolin, 5 parts of wollastonite, 1 part of zirconia, and 3 parts of calcium borate.

[0033...

Embodiment 2

[0042]This embodiment provides a ceramic product with a self-cleaning glaze, including a base material and a glaze, and the base material includes the following raw materials in parts by weight: 41 parts of kaolin, 18 parts of quartz, 26 parts of potassium feldspar, 11 parts of clay, and talc 2 parts; the glaze includes a bottom glaze and a top glaze, and the bottom glaze includes the following raw materials in parts by weight: 24 parts of potassium feldspar, 11 parts of nano-zinc oxide, 11 parts of quicklime, 4 parts of burnt talc, 25 parts of kaolin, zirconium silicate 9 parts, 6 parts of wollastonite, 1 part of bone ash, 2 parts of calcium borate, 21 parts of frit; the surface glaze includes the following raw materials in parts by weight: 27 parts of potassium feldspar, 9 parts of zinc oxide, 9 parts of calcium oxide, and 9 parts of aluminum oxide 4 parts, magnesium oxide 4 parts, kaolin 27 parts, wollastonite 6 parts, zirconia 2 parts, calcium borate 4 parts.

[0043] This...

Embodiment 3

[0052] This embodiment provides a ceramic product with a self-cleaning glaze, including a tire material and a glaze material, and the tire material includes the following raw materials in parts by weight: 43 parts of kaolin, 20 parts of quartz, 28 parts of potassium feldspar, 12 parts of clay, 3 parts of talc;

[0053] The glaze includes a bottom glaze and a surface glaze, and the bottom glaze includes the following raw materials in parts by weight: 25 parts of potassium feldspar, 12 parts of nano-zinc oxide, 12 parts of quicklime, 5 parts of burnt talc, 25 parts of kaolin, 10 parts of zirconium silicate, 7 parts of wollastonite, 2 parts of bone ash, 2 parts of calcium borate, 23 parts of frit; the surface glaze includes the following raw materials in parts by weight: 28 parts of potassium feldspar, 10 parts of zinc oxide, 10 parts of calcium oxide, 10 parts of aluminum oxide, 5 parts of magnesium, 28 parts of kaolin, 7 parts of wollastonite, 2 parts of zirconia, and 5 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a ceramic product with self-cleaning glaze. The ceramic product comprises a tire material and the glaze, wherein the tire material comprises kaolin, quartz, potassium feldspar,clay and talc; the glaze comprises ground glaze and cover glaze, wherein the ground glaze comprises the following raw materials: potassium feldspar, nano zinc oxide, calcium oxide, burning talc, zirconium silicate, wollastonite, kaolin, bone ash, calcium borate and frit; the cover glaze comprises the following raw materials: potassium feldspar, kaolin, wollastonite, zinc oxide, calcium oxide, aluminum oxide, magnesium oxide, zirconium oxide and calcium borate. A making method of the ceramic product with the self-cleaning glaze comprises the following steps: (1) respectively mixing the tire material and the glaze, adding water, wet-milling with a ball mill and sieving to obtain tire material slurry and glaze slurry; (2) making a green body with the tire material slurry for biscuit firing; (3) applying the ground glaze; (4) applying the cover glaze; (4) firing. The ceramic product made of the making method provided by the invention is fine and bright in glazed surface and can effectivelyprevent the accumulation of dirt and the formation of black spots.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a ceramic product with self-cleaning glaze and a manufacturing method thereof. Background technique [0002] The development history of ceramics is an important part of the history of Chinese civilization. As one of the four ancient civilizations, China has made outstanding contributions to the progress and development of human society. Among them, the invention and development of ceramics has unique significance. Ceramics from all dynasties and dynasties in Chinese history have different artistic styles and technical characteristics. "china" in English means both China and ceramics, which clearly shows that China is the "hometown of ceramics". As early as more than a thousand years before the Europeans mastered the porcelain manufacturing technology, the Han people had already produced very exquisite ceramics. China is one of the first countries in the world to us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C03C8/00C04B41/89
CPCC03C8/00C04B33/13C04B41/009C04B41/52C04B41/89C04B2235/3418C04B2235/3472C04B41/504C04B41/5022
Inventor 李仁鹏李婧
Owner 福建省德化龙辉陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com