Lignin porous carbon nanosheet as well as preparation method thereof and application in supercapacitor electrode material

A technology of lignin and nanosheets, applied in hybrid capacitor electrodes, hybrid/electric double layer capacitor manufacturing, nano-carbon, etc., can solve the problems of unsuitable supercapacitor electrodes, difficult removal of silica template, weak solid particle dispersion ability, etc. problems, to achieve the effect of high value-added utilization, good application value, and environmental protection

Active Publication Date: 2019-03-19
SOUTH CHINA UNIV OF TECH
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has cumbersome steps and is not easy to remove the silica template
[0008] In summary, due to the poor water solubility of industrial lignin such as alkali lignin or enzymatic lignin, the ability to disperse solid particles is weak, resulting in serious agglomeration of lignin porous carbon prepared by direct carbonization products, and random microscopic pores. It is suitable for use as a supercapacitor electrode, but the existing chemical activation method or template method has problems such as complicated process, serious corrosion of equipment, and high production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lignin porous carbon nanosheet as well as preparation method thereof and application in supercapacitor electrode material
  • Lignin porous carbon nanosheet as well as preparation method thereof and application in supercapacitor electrode material
  • Lignin porous carbon nanosheet as well as preparation method thereof and application in supercapacitor electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] Weigh 5 parts by mass of sodium lignosulfonate and 5 parts by mass of zinc oxalate solid powder and dissolve them in 500 parts by volume of water, and stir evenly to obtain a stable dispersion A. Take 50 parts by volume of the dispersion liquid A, add 50 parts by volume of ethanol under stirring, and separate the precipitate after standing still to obtain a lignin / zinc oxalate composite. Then take 50 parts by volume of dispersion liquid A, add the lignin / zinc oxalate complex prepared above, stir for 20 minutes, add 50 parts by volume of ethanol, and separate the lignin / zinc oxalate complex after standing still. The above operation was repeated 6 times, and the precipitate was separated to obtain a layer-by-layer self-assembled composite lignin / zinc oxalate composite.

[0064] Place the layer-by-layer self-assembled lignin / zinc oxalate composite in an inert atmosphere, carbonize at 750°C for 3 hours to obtain a lignin carbon / zinc oxide composite, soak the product in 1mol...

Embodiment 2

[0066] Weigh 10 parts by mass of magnesium lignosulfonate and 5 parts by mass of magnesium oxalate solid powder and dissolve them in 500 parts by volume of water, and stir evenly to obtain a stable dispersion A. Take 50 parts by volume of the dispersion liquid A, add 50 parts by volume of ethanol under stirring, and separate the precipitate after standing still to obtain a lignin / magnesium oxalate composite. Then take 50 parts by volume of dispersion liquid A, add the lignin / magnesium oxalate complex prepared above, stir for 20 minutes, add 50 parts by volume of ethanol, and separate the lignin / magnesium oxalate complex after standing. The above operation was repeated 8 times, and the precipitate was separated to obtain a layer-by-layer self-assembled composite lignin / magnesium oxalate composite.

[0067] Place the layer-by-layer self-assembled lignin / magnesium oxalate composite in an inert atmosphere, carbonize at 550°C for 4 hours to obtain a lignin carbon / magnesium oxide co...

Embodiment 3

[0069]Weigh 5 parts by mass of calcium lignosulfonate and 7.5 parts by mass of calcium oxalate solid powder and dissolve them in 500 parts by volume of water, and stir evenly to obtain a stable dispersion A. Take 50 parts by volume of the dispersion liquid A, add 50 parts by volume of ethanol under stirring, and separate the precipitate after standing still to obtain a lignin / calcium oxalate composite. Then take 50 parts by volume of dispersion liquid A, add the lignin / calcium oxalate complex prepared above, stir for 20 minutes, add 50 parts by volume of ethanol, and separate the lignin / calcium oxalate complex after standing. The above operation was repeated 6 times, and the precipitate was separated to obtain a layer-by-layer self-assembled composite lignin / calcium oxalate composite.

[0070] Place the layer-by-layer self-assembled lignin / calcium oxalate composite in an inert atmosphere, carbonize at 650°C for 3 hours to obtain a lignin carbon / calcium oxide composite, soak th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of biomass charcoal materials, and particularly relates to a lignin porous carbon nanosheet as well as a preparation method thereof and an application in asupercapacitor electrode material. The preparation method comprises the following steps: self-assembling lignosulfonate and oxalate in a selective solvent layer by layer to obtain layer-by-layer self-assembled lignin / oxalate compound, and carbonizing and acid pickling the compound to obtain the lignin porous carbon nanosheet. The specific surface area range of the lignin porous carbon nanosheet prepared by virtue of the method provided in the invention is 200 to 1500 m2 / g, the microporous specific surface area range is 100 to 500 m2 / g, the mesoporous specific surface area range is 100 to 1000m2 / g, the aperture is 0.5 to 30 micrometers, and the pore volume is 0.5 to 1.5 cm3 / g; and the lignin porous carbon nanosheet can be applied to the supercapacitor electrode material, has higher specific capacity and excellent multiplying power performance (the specific capacity maintaining rate is 76.6 percent), and has good potential application value.

Description

technical field [0001] The invention belongs to the technical field of biomass carbon materials, and in particular relates to a lignin porous carbon nanosheet, a preparation method thereof, and an application in supercapacitor electrode materials. Background technique [0002] The massive consumption of traditional fossil energy and the increasingly severe environmental pollution have forced countries all over the world to raise the development of green and environmentally friendly new energy to a strategic height. Electrochemical energy storage devices play a very important role in the development of green and sustainable energy storage and conversion technologies. As a new type of energy storage device between traditional physical capacitors and secondary batteries, supercapacitors are widely used in portable electronic devices and electric vehicles due to their advantages such as high power density, fast charging and discharging, long cycle life and wide applicable temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/15H01G11/24H01G11/36H01G11/44
CPCH01G11/24H01G11/36H01G11/44C01B32/15Y02E60/13C01P2004/03C01P2004/04C01P2006/12C01P2006/14C01P2006/16H01G11/86H01G11/34C01P2006/40
Inventor 邱学青符方宝杨东杰王欢李致贤黄锦浩欧阳新平刘伟峰
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com